Porous bimetallic Mn2Co1Ox catalysts prepared by a one-step combustion method for the low temperature selective catalytic reduction of NOx with NH3

[1]  R. Pirone,et al.  Nanostructured MnOx catalysts for low-temperature NOx SCR , 2015 .

[2]  R. Pirone,et al.  MnOx-CeO2 catalysts synthesized by solution combustion synthesis for the low-temperature NH3-SCR , 2015 .

[3]  A. Jensen,et al.  Mn/TiO2 and Mn–Fe/TiO2 catalysts synthesized by deposition precipitation—promising for selective catalytic reduction of NO with NH3 at low temperatures , 2015 .

[4]  C. J. Tyne,et al.  Dispersion and valence state of MnO2/Ce(1 − x)ZrxO2–TiO2 for low temperature NH3-SCR , 2014 .

[5]  Zhongbiao Wu,et al.  Manganese–niobium mixed oxide catalyst for the selective catalytic reduction of NOx with NH3 at low temperatures , 2014 .

[6]  Liyi Shi,et al.  Rational Design of High-Performance DeNOx Catalysts Based on MnxCo3–xO4 Nanocages Derived from Metal–Organic Frameworks , 2014 .

[7]  Jianlin Shi,et al.  Ni-Mn bi-metal oxide catalysts for the low temperature SCR removal of NO with NH3 , 2014 .

[8]  Zhenhua Wang,et al.  Synthesis and electrochemical characterization of Sr 2 Fe 1.5 Mo 0.5 O 6 –Sm 0.2 Ce 0.8 O 1.9 composite cathode for intermediate-temperature solid oxide fuel cells , 2013 .

[9]  Yonghong Li,et al.  A Ce–Sn–Ox catalyst for the selective catalytic reduction of NOx with NH3 , 2013 .

[10]  Hamidreza Arandiyan,et al.  Comparison of the performance for oxidation of formaldehyde on nano-Co3O4, 2D-Co3O4, and 3D-Co3O4 catalysts , 2013 .

[11]  J. Hao,et al.  Design strategies for P-containing fuels adaptable CeO2-MoO3 catalysts for DeNO(x): significance of phosphorus resistance and N2 selectivity. , 2013, Environmental science & technology.

[12]  Jiming Hao,et al.  Nitrogen oxides emissions from thermal power plants in china: current status and future predictions. , 2013, Environmental science & technology.

[13]  Liyi Shi,et al.  Low-temperature selective catalytic reduction of NO with NH₃ over nanoflaky MnOx on carbon nanotubes in situ prepared via a chemical bath deposition route. , 2013, Nanoscale.

[14]  G. Lu,et al.  Highly Active and Stable Co3O4/ZSM-5 Catalyst for Propane Oxidation: Effect of the Preparation Method , 2013 .

[15]  Caixia Liu,et al.  Improvement of activity and SO₂ tolerance of Sn-modified MnOx-CeO₂ catalysts for NH₃-SCR at low temperatures. , 2013, Environmental science & technology.

[16]  H. Yang,et al.  Disordered Co1.28Mn1.71O4 as a visible-light-responsive photocatalyst for hydrogen evolution. , 2013, Chemistry.

[17]  Liyi Shi,et al.  In situ supported MnO(x)-CeO(x) on carbon nanotubes for the low-temperature selective catalytic reduction of NO with NH3. , 2013, Nanoscale.

[18]  Zongbin Zhao,et al.  Selective catalytic reduction of nitrogen oxides by ammonia over Co3O4 nanocrystals with different shapes , 2013 .

[19]  Bichun Huang,et al.  Manganese oxides supported on multi-walled carbon nanotubes for selective catalytic reduction of NO with NH3: Catalytic activity and characterization , 2012 .

[20]  Xinyong Li,et al.  Shape-controlled fabrication of the porous Co3O4 nanoflower clusters for efficient catalytic oxidation of gaseous toluene. , 2012, Journal of hazardous materials.

[21]  P. Smirniotis,et al.  Co-doping a metal (Cr, Fe, Co, Ni, Cu, Zn, Ce, and Zr) on Mn/TiO2 catalyst and its effect on the selective reduction of NO with NH3 at low-temperatures , 2011 .

[22]  S. Moreno,et al.  Cu–Mn and Co–Mn catalysts synthesized from hydrotalcites and their use in the oxidation of VOCs , 2011 .

[23]  Zhihang Chen,et al.  Cr–MnOx mixed-oxide catalysts for selective catalytic reduction of NOx with NH3 at low temperature , 2010 .

[24]  O. Kröcher,et al.  Characterization of Nb-Containing MnO x −CeO 2 Catalyst for Low-Temperature Selective Catalytic Reduction of NO with NH 3 , 2010 .

[25]  Yue Liu,et al.  Low-temperature selective catalytic reduction of NO with NH(3) over Mn-Ce oxides supported on TiO2 and Al2O3: a comparative study. , 2010, Chemosphere.

[26]  Yue Liu,et al.  Ceria modified MnOx/TiO2 as a superior catalyst for NO reduction with NH3 at low-temperature , 2008 .

[27]  M. S. Hegde,et al.  Low-Temperature Selective Catalytic Reduction of NO with NH3 over Ti0.9M0.1O2-δ (M = Cr, Mn, Fe, Co, Cu) , 2008 .

[28]  J. Hao,et al.  Novel promoting effect of SO2 on the selective catalytic reduction of NOx by ammonia over Co3O4 catalyst , 2007 .

[29]  R. T. Yang,et al.  MnOx-CeO2 mixed oxides prepared by co-precipitation for selective catalytic reduction of NO with NH3 at low temperatures , 2004 .

[30]  F. Larachi,et al.  Composition–activity effects of Mn–Ce–O composites on phenol catalytic wet oxidation , 2001 .