Solidus and liquidus temperatures in the UO2–PuO2 system

Abstract The melting of plutonium and uranium mixed oxide containing Pu of more than 30% was investigated using a tungsten capsule and a rhenium inner capsule. In the conventional measurements of (Pu, U)O 2.00 in the tungsten capsule, a liquid phase of tungsten and plutonium oxide appeared in the mixed oxide during melting. This liquid phase was found to have an effect on the measurement of melting point. Therefore, the rhenium inner capsule was used to avoid the effect. The solidus and liquidus temperatures in the UO 2 –PuO 2 system were decided from the (Pu, U)O 2.00 data measured using the rhenium capsule, and the effect of the Am content on the solidus temperature was evaluated. The variation of the solidus and liquidus temperatures in the UO 2 –PuO 2 –AmO 2 ternary system was represented to an accuracy of σ  = ±9 K and σ  = ±16 K, respectively, by the ideal solution model.

[1]  Theodore M. Besmann,et al.  Chemical thermodynamic representations of 〈PuO2−x〉 and 〈U1−zPuzOw〉 , 1985 .

[2]  W. E. Baily,et al.  The solid-liquid phase diagram for the UO2-PuO2 system☆ , 1967 .

[3]  R. Konings,et al.  Melting behaviour of oxide systems for heterogeneous transmutation of actinides. III. The system Am–Mg–O , 1997 .

[4]  R. E. Latta,et al.  Determination of solidus-liquidus temperatures in the uo2 + x system (−0.50 , 1970 .

[5]  Juan J. Carbajo,et al.  A review of the thermophysical properties of MOX and UO , 2001 .

[6]  Masato Kato,et al.  Preparation and characterization of (Pu, U, Np, Am, simulated FP) O2−X , 2005 .

[7]  R. Woodley.  Oxygen potentials of plutonia and urania-plutonia solid solutions , 1981 .

[8]  F. Pavese,et al.  Recommended values of temperature on the International Temperature Scale of 1990 for a selected set of secondary reference points , 1996 .

[9]  K. Yoshikawa,et al.  Melting temperature and thermal conductivity of irradiated mixed oxide fuel , 1993 .

[10]  L. F. Epstein,et al.  Ideal solution behavior and heats of fusion from the UO2-PuO2 phase diagram , 1967 .

[11]  M. G. Adamson,et al.  Experimental and thermodynamic evaluation of the melting behavior of irradiated oxide fuels , 1985 .

[12]  R. Konings,et al.  Melting behaviour of oxide systems for heterogeneous transmutation of actinides. I. The systems PuAlO and PuMgO , 1997 .

[13]  D. Geithoff,et al.  Plutonium redistribution in fast reactor mixed oxide fuel pins , 1973 .

[14]  Kenji Konashi,et al.  The melting temperature of irradiated oxide fuel , 1988 .

[15]  Tetsuya Ishii,et al.  An investigation of the Pu migration phenomena during irradiation in fast reactor , 2001 .