Morphology dependent field emission of acid-spun carbon nanotube fibers

Acid spun carbon nanotube (CNT) fibers were investigated for their field emission properties and performance was determined to be dependent on fiber morphology. The fibers were fabricated by wet-spinning of pre-made CNTs. Fiber morphology was controlled by a fabrication method and processing conditions, as well as purity, size, and type of the CNT starting material. The internal fiber structure consisted of CNT fibrils held together by van der Waals forces. Alignment and packing density of the CNTs affects the fiber's electrical and thermal conductivity. Fibers with similar diameters and differing morphology were compared, and those composed of the most densely packed and well aligned CNTs were the best field emitters as exhibited by a lower turn-on voltage and a larger field enhancement factor. Fibers with higher electrical and thermal conductivity demonstrated higher maximum current before failure and longer lifetimes. A stable emission current at 3 mA was obtained for 10 h at a field strength of <1 V μm(-1). This stable high current operation makes these CNT fibers excellent candidates for use as low voltage electron sources for vacuum electronic devices.

[1]  Michael J. Bronikowski,et al.  Gas-phase production of carbon single-walled nanotubes from carbon monoxide via the HiPco process: A parametric study , 2001 .

[2]  Myung Jong Kim,et al.  Macroscopic, Neat, Single-Walled Carbon Nanotube Fibers , 2002, Science.

[3]  G. Mcguire,et al.  Back-gated milliampere-class field emission device based on carbon nanosheets , 2006 .

[4]  R. Fowler,et al.  Electron Emission in Intense Electric Fields , 1928 .

[5]  Otto Zhou,et al.  Carbon nanotube based microfocus field emission x-ray source for microcomputed tomography , 2006 .

[6]  Guohua Cao,et al.  A carbon nanotube field emission cathode with high current density and long-term stability , 2009, Nanotechnology.

[7]  Hollis H. Jones,et al.  Performance of a carbon nanotube field emission electron gun , 2007, SPIE Defense + Commercial Sensing.

[8]  K. Jiang,et al.  A vacuum sensor using field emitters made by multiwalled carbon nanotube yarns , 2012 .

[9]  P. T. Murray,et al.  Evidence for adsorbate-enhanced field emission from carbon nanotube fibers , 2013, 1306.6459.

[10]  M. Kaiser,et al.  Characterization of the field emission properties of individual thin carbon nanotubes , 2004 .

[11]  Kenneth A. Smith,et al.  Gas-phase catalytic growth of single-walled carbon nanotubes from carbon monoxide , 1999 .

[12]  S. Turano,et al.  A thin film triode type carbon nanotube field emission cathode , 2013 .

[13]  H. Kawarada,et al.  Enhanced field emission properties of vertically aligned double-walled carbon nanotube arrays , 2008, Nanotechnology.

[14]  Philip G. Collins,et al.  UNIQUE CHARACTERISTICS OF COLD CATHODE CARBON-NANOTUBE-MATRIX FIELD EMITTERS , 1997 .

[15]  M. A. Timofeyev,et al.  Nanocrystalline graphite: Promising material for high current field emission cathodes , 2010 .

[16]  J. A. Briones-Leon,et al.  Millimeter-long carbon nanotubes: outstanding electron-emitting sources. , 2011, ACS nano.

[17]  M. Pasquali,et al.  Demonstration of an Acid-Spun Single-Walled Nanotube Fiber Cathode , 2012, IEEE Transactions on Plasma Science.

[18]  Lianxi Zheng,et al.  Structure‐Dependent Electrical Properties of Carbon Nanotube Fibers , 2007 .

[19]  Young Hee Lee,et al.  Patterned growth and field emission properties of vertically aligned carbon nanotubes , 2001 .

[20]  G. Kochanski,et al.  A micromachined vacuum triode using a carbon nanotube cold cathode , 2002 .

[21]  U. Valdré,et al.  Experimental and computational study of field emission characteristics from amorphous carbon single nanotips grown by carbon contamination. I. Experiments and computation , 2002 .

[22]  S. Raina,et al.  Field emission from nanodiamond grown with 'ridge' type geometrically enhanced features , 2008 .

[23]  R. Vaia,et al.  Transient Microstructure of Low Hard Segment Thermoplastic Polyurethane under Uniaxial Deformation , 2008 .

[24]  K. Jiang,et al.  New-type planar field emission display with superaligned carbon nanotube yarn emitter. , 2012, Nano letters.

[25]  K. R. Atkinson,et al.  Multifunctional Carbon Nanotube Yarns by Downsizing an Ancient Technology , 2004, Science.

[26]  G. Amaratunga,et al.  Aligned carbon nanotubes/fibers for applications in vacuum microwave amplifiers , 2006 .

[27]  Peter H. Siegel,et al.  Field emission testing of carbon nanotubes for THz frequency vacuum microtube sources , 2004, SPIE MOEMS-MEMS.

[28]  V. Binh,et al.  Polymer embedded C nanopearls field emission cathodes for time of flight mass spectrometers , 2007, 2007 IEEE 20th International Vacuum Nanoelectronics Conference.

[29]  S. Orlanducci,et al.  Carbon nanotube/nanodiamond structures: An innovative concept for stable and ready-to-start electron emitters , 2009 .

[30]  C. Klinke,et al.  Carbon nanotube films as electron field emitters , 2002 .

[31]  L. Lu,et al.  3ω method for specific heat and thermal conductivity measurements , 2001, quant-ph/0202038.

[32]  G. Amaratunga,et al.  Hot electron field emission via individually transistor-ballasted carbon nanotube arrays. , 2012, ACS nano.

[33]  Lianxi Zheng,et al.  Strong carbon-nanotube fibers spun from long carbon-nanotube arrays. , 2007, Small.

[34]  W. Kang,et al.  Development of a vacuum packaged nanodiamond lateral field emission device , 2007, 2007 IEEE 20th International Vacuum Nanoelectronics Conference.

[35]  Revealing the Substructure of Single-Walled Carbon Nanotube Fibers , 2005 .

[36]  T. Clapp,et al.  Ultrastrong, Stiff, and Lightweight Carbon‐Nanotube Fibers , 2007 .

[37]  C. Yeh,et al.  Field emission from carbon nanosheets on pyramidal Si(100) , 2007 .

[38]  Martin Sparkes,et al.  Hysteresis during field emission from chemical vapor deposition synthesized carbon nanotube fibers , 2014 .

[39]  V. Binh,et al.  Freestanding vertically aligned arrays of individual carbon nanotubes on metallic substrates for field emission cathodes , 2004 .

[40]  Mei Zhang,et al.  Field emission of electrons by carbon nanotube twist-yarns , 2007 .

[41]  Tsu-Wei Chou,et al.  Carbon Nanotube Fiber Based Stretchable Conductor , 2013 .

[42]  László Forró,et al.  Field emission properties of multiwalled carbon nanotubes , 1998 .

[43]  Yeonsu Jung,et al.  High-performance field emission from a carbon nanotube carpet , 2012 .

[44]  K. Jiang,et al.  Efficient fabrication of carbon nanotube micro tip arrays by tailoring cross-stacked carbon nanotube sheets. , 2012, Nano letters.

[45]  Matteo Pasquali,et al.  Macroscopic self-standing SWCNT fibres as efficient electron emitters with very high emission current for robust cold cathodes , 2013 .

[46]  Seung Hoon Nahm,et al.  Field emission properties from the tip and side of multi-walled carbon nanotube yarns , 2010 .

[47]  Gehan A. J. Amaratunga,et al.  Field electron emission from individual carbon nanotubes of a vertically aligned array , 2002 .

[48]  Jian Zhang,et al.  Design of a 3D field emission electron source with improved emission current density and cathode life , 2013, Medical Imaging.

[49]  Gaurav Mittal,et al.  Recent progress in nanostructured next-generation field emission devices , 2014 .

[50]  V. Binh,et al.  Quasi-monochromatic field-emission x-ray source. , 2012, The Review of scientific instruments.

[51]  M. Shiraishi,et al.  Work function of carbon nanotubes , 2001 .

[52]  S. Roth,et al.  Field emission characteristics of point emitters fabricated by a multiwalled carbon nanotube yarn , 2009, Nanotechnology.

[53]  László Forró,et al.  Field emission from single-wall carbon nanotube films , 1998 .

[54]  Y. Cohen,et al.  Strong, Light, Multifunctional Fibers of Carbon Nanotubes with Ultrahigh Conductivity , 2013, Science.

[55]  Gehan A. J. Amaratunga,et al.  Carbon nanotubes as field emission sources , 2004 .

[56]  Yuan Cheng,et al.  Electron field emission from carbon nanotubes , 2003, Comptes Rendus Physique.

[57]  J. Kong,et al.  Spinning and Processing Continuous Yarns from 4‐Inch Wafer Scale Super‐Aligned Carbon Nanotube Arrays , 2006 .

[58]  K. Jiang,et al.  Efficient fabrication of field electron emitters from the multiwalled carbon nanotube yarns , 2006 .