Adding fly ash microsphere to improve packing density, flowability and strength of cement paste

Abstract Fly ash microsphere (FAM) is a superfine fly ash. Being finer than cement, it can fill into the voids between cement grains. To study the effects of adding FAM, cement paste samples with FAM contents ranging from 0 to 60% and different water contents were made for packing density, flowability and strength measurements. The results showed that the addition of up to 40% FAM would significantly increase the packing density of the cementitious materials. With the voids partially filled by FAM and the same volume of water in the voids released, the addition of FAM could increase the water film thickness of the cement paste. Consequently, the addition of FAM could increase flowability at same strength, increase strength at same flowability, or increase both strength and flowability. Hence, FAM is an effective cementitious filler for improving the performance of cement paste and concrete.

[1]  Aikaterini Mccarthy,et al.  Characteristics of the ultrafine component of fly ash , 2006 .

[2]  Jay G. Sanjayan,et al.  Effects of ultra-fine materials on workability and strength of concrete containing alkali-activated slag as the binder , 1999 .

[3]  Sidney Mindess,et al.  Rheology of high-performance concrete: Effect of ultrafine particles , 1998 .

[4]  Akh Kwan,et al.  Packing density of cementitious materials: part 1—measurement using a wet packing method , 2008 .

[5]  Serdar Aydın,et al.  The effect of grinding process on mechanical properties and alkali–silica reaction resistance of fly ash incorporated cement mortars , 2010 .

[6]  F. Nai-qian,et al.  The influence of superplasticizer and superfine mineral powder on the flexibility, strength and durability of HPC , 2001 .

[7]  Hajime Okamura,et al.  Self-Compacting Concrete , 2000 .

[8]  J. Ferreira,et al.  Influence of particle size distribution on rheology and particle packing of silica-based suspensions , 2004 .

[9]  Josef Kaufmann,et al.  Effect of the addition of ultrafine cement and short fiber reinforcement on shrinkage, rheological and mechanical properties of Portland cement pastes , 2004 .

[10]  C. Artelt,et al.  Impact of Superplasticizer Concentration and of Ultra-fine Particles on the Rheological Behaviour of Dense Mortar Suspensions , 2008 .

[11]  G. Escadeillas,et al.  The nature of limestone filler and self-consolidating feasibility—Relationships between physical, chemical and mineralogical properties of fillers and the flow at different states, from powder to cement-based suspension , 2012 .

[12]  A. Kwan,et al.  Packing density of cementitious materials: part 2—packing and flow of OPC + PFA + CSF , 2008 .

[13]  M. Salleh,et al.  Assessment of the effects of rice husk ash particle size on strength, water permeability and workability of binary blended concrete , 2010 .

[14]  Michael Haist,et al.  Investigation on the influence of granular packing on the flow properties of cementitious suspensions , 2008 .

[15]  Orhan Aksogan,et al.  The effect of particle size distribution on the properties of blended cements incorporating GGBFS and natural pozzolan (NP) , 2007 .

[16]  Tongsheng Zhang,et al.  A gap-graded particle size distribution for blended cements: Analytical approach and experimental validation , 2011 .

[17]  Taehyo Park,et al.  Rheological Properties of Cementitious Materials Containing Mineral Admixtures , 2005 .

[18]  A. Chaipanich,et al.  Utilization of fly ash with silica fume and properties of Portland cement–fly ash–silica fume concrete , 2010 .

[19]  Peter A. Claisse,et al.  Workability of Cement Pastes , 2001 .

[20]  T Sedran,et al.  Optimization of ultra-high-performance concrete by the use of a packing model , 1994 .

[21]  Guangcheng Long,et al.  Very-high-performance concrete with ultrafine powders , 2002 .

[22]  Xiong Zhang,et al.  The effect of ultra-fine admixture on the rheological property of cement paste , 2000 .

[23]  Etsuo Sakai,et al.  Effect of particle size distribution of fly ash–cement system on the fluidity of cement pastes , 2003 .

[24]  Aci Committe.  State-of-the-Art Report on High Strength Concrete , 1984 .

[25]  Ann H. Kwan,et al.  Role of water film thickness in rheology of CSF mortar , 2010 .

[26]  Meirong Wang,et al.  Microstructural and mechanical characterization of fly ash cenosphere/metakaolin-based geopolymeric composites , 2011 .

[27]  H. H. C. Wong,et al.  Effects of packing density, excess water and solid surface area on flowability of cement paste , 2008 .

[28]  H. H. C. Wong,et al.  Rheology of Cement Paste: Role of Excess Water to Solid Surface Area Ratio , 2008 .

[29]  I. Celik.  The effects of particle size distribution and surface area upon cement strength development , 2009 .

[30]  H. Mörtel,et al.  Dense packing of cement pastes and resulting consequences on mortar properties , 1997 .

[31]  P. Aitcin.  High Performance Concrete , 1998 .

[32]  A. Kwan,et al.  Effects of superplasticiser on rheology and cohesiveness of CSF cement paste , 2012 .

[33]  G. C. Cordeiro,et al.  Use of ultrafine rice husk ash with high-carbon content as pozzolan in high performance concrete , 2009 .