Effect of the Pyro-Gasification Temperature of Wood on the Physical and Mechanical Properties of Biochar-Polymer Biocomposites

The physical and mechanical properties of wood (WPC) and biochar polymer composites (BPC) obtained at different pyro-gasification temperatures and different fiber proportions were investigated. Composite pellets made from wood chips or biochar and thermoplastic polymers (polypropylene or high-density polyethylene) were obtained by twin-screw extrusion, and test specimens were prepared by injection molding. Results showed that BPCs were more dimensionally stable compared to WPCs, but their mechanical properties decreased with increasing pyro-gasification temperatures due to the poor adhesion between the polymer and biochar. Indeed, FTIR investigations revealed the decrease or absence of hydroxyl groups on biochar, which prevents the coupling agent from reacting with the biochar surface. The change in the biochar chemical structure led to an improvement in the dimensional stability and hydrophobicity of the biocomposites. Despite the increased dimensional stability of BPCs compared to WPCs, BPCs still adsorb water. This was explained by the surface roughness and by the biochar agglomerations present in the composite. In conclusion, the thermochemical conversion of black spruce wood chips into biochar makes it brittle but more hydrophobic, thereby reducing the wettability of the BPCs.

[1]  Ahmed Koubaa,et al.  The conversion of wood residues, using pilot-scale technologies, into porous activated biochars for supercapacitors , 2019, Journal of Porous Materials.

[2]  Ahmed Koubaa,et al.  The influence of pilot-scale pyro-gasification and activation conditions on porosity development in activated biochars , 2018, Biomass and Bioenergy.

[3]  Ahmed Koubaa,et al.  Production, characterization, and potential of activated biochar as adsorbent for phenolic compounds from leachates in a lumber industry site , 2018, Environmental Science and Pollution Research.

[4]  Ahmed Koubaa,et al.  Activated Biochar as an Effective Sorbent for Organic and Inorganic Contaminants in Water , 2018, Water, Air, & Soil Pollution.

[5]  Weiming Yi,et al.  Mechanical Properties of Rice Husk Biochar Reinforced High Density Polyethylene Composites , 2018, Polymers.

[6]  T. Kärki,et al.  Durability of wood plastic composites manufactured from recycled plastic , 2018, Heliyon.

[7]  P. Perré,et al.  Numerical and experimental assessment of water absorption of wood-polymer composites , 2018, Measurement.

[8]  Qingfa Zhang,et al.  The Dynamic Mechanical Analysis of Highly Filled Rice Husk Biochar/High-Density Polyethylene Composites , 2017, Polymers.

[9]  C. S. Lin,et al.  Returning biochar to fields: A review , 2017 .

[10]  A. Mateus,et al.  Optimization of a Wood Plastic Composite for Architectural Applications , 2017 .

[11]  D. Bhattacharyya,et al.  Mechanical and flammability characterisations of biochar/polypropylene biocomposites , 2016 .

[12]  D. Bhattacharyya,et al.  Biocomposites from waste derived biochars: Mechanical, thermal, chemical, and morphological properties. , 2016, Waste management.

[13]  Haiping Yang,et al.  Effects of binders on the properties of bio-char pellets , 2015 .

[14]  D. Bhattacharyya,et al.  A sustainable and resilient approach through biochar addition in wood polymer composites. , 2015, The Science of the total environment.

[15]  Lei Zhang,et al.  Mini-chunk biochar supercapacitors , 2014, Journal of Applied Electrochemistry.

[16]  P. Perré,et al.  Effect of Fiber Origin, Proportion, and Chemical Composition on the Mechanical and Physical Properties of Wood-Plastic Composites , 2014 .

[17]  S. C. Peterson.  Utilization of low-ash biochar to partially replace carbon black in styrene–butadiene rubber composites , 2013 .

[18]  G. Ahmetli,et al.  Epoxy composites based on inexpensive char filler obtained from plastic waste and natural resources , 2013 .

[19]  M. Schwanninger,et al.  Characterization of slow pyrolysis biochars: effects of feedstocks and pyrolysis temperature on biochar properties. , 2012, Journal of environmental quality.

[20]  S. C. Peterson.  Evaluating corn starch and corn stover biochar as renewable filler in carboxylated styrene–butadiene rubber composites , 2012 .

[21]  L. Beesley,et al.  A review of biochars' potential role in the remediation, revegetation and restoration of contaminated soils. , 2011, Environmental pollution.

[22]  N. Ayrilmis,et al.  Surface characteristics and overlaying properties of flat-pressed wood plastic composites , 2011, European Journal of Wood and Wood Products.

[23]  Naoko Ellis,et al.  Biochar based solid acid catalyst for biodiesel production , 2010 .

[24]  E. Hassan,et al.  Characterization of Fast Pyrolysis Bio-oils Produced from Pretreated Pine Wood , 2009, Applied biochemistry and biotechnology.

[25]  P. Perré,et al.  Analysis of Among-Species Variability in Wood Fiber Surface Using DRIFTS and XPS: Effects on Esterification Efficiency , 2008 .

[26]  E. Ōsawa,et al.  Carbon blacks as the source materials for carbon nanotechnology , 2006 .

[27]  H. Militz,et al.  Chemical changes in hydrothermal treated wood: FTIR analysis of combined hydrothermal and dry heat-treated wood , 2005, Holz als Roh- und Werkstoff.

[28]  Ann Wennerberg,et al.  Oral implant surfaces: Part 1--review focusing on topographic and chemical properties of different surfaces and in vivo responses to them. , 2004, The International journal of prosthodontics.

[29]  G. Michler,et al.  Modified polypropylene wood flour composites. II. Fracture, deformation, and mechanical properties , 2004 .

[30]  Jean L. Leblanc,et al.  Rubber–filler interactions and rheological properties in filled compounds , 2002 .

[31]  J. T. Fredrich,et al.  3D imaging of porous media using laser scanning confocal microscopy with application to microscale transport processes , 1999 .