Stress–strain behaviour and abrupt loss of stiffness of geopolymer at elevated temperatures

This paper reports stress versus strain curves of geopolymer tested while the specimens were kept at elevated temperatures, with the aim to study the fire resistance of geopolymer. Tests were performed at temperatures from 23 to 680 °C and after cooling. Hot strengths of geopolymer increased when the temperature increased from 290 to 520 °C, reaching the highest strength at 520 °C, which is almost double that of its initial strength at room temperature. However, glass transition behaviour was observed to occur between 520 and 575 °C, which was characterised by abrupt loss of stiffness and significant viscoelastic behaviour. The glass transition temperature is determined to be 560 °C. Further, the strength reductions occurred during cooling to room temperature. This is attributed to the damage due to brittle nature of the material making it difficult to accommodate thermal strain differentials during cooling phase.

[1]  Gabriel A. Khoury,et al.  Transient thermal strain of concrete: literature review, conditions within specimen and behaviour of individual constituents , 1985 .

[2]  T. Hansen,et al.  Cracks in Concrete Core Due to Fire or Thermal Heating Shock , 1994 .

[3]  R. Hill,et al.  Book Review: Mechanical properties of non-metallic brittle materials. Edited by W.H. WALTON. Butterworths, London; Inter-Science, New York, 1958. 492 pp., 90s , 1960 .

[4]  B. Rangan,et al.  Heat-cured, low-calcium, fly ash-based geopolymer concrete , 2006 .

[5]  M. Weil,et al.  The influence of calcium content on the structure and thermal performance of fly ash based geopolymers , 2007 .

[6]  B. Vijaya Rangan,et al.  ON THE DEVELOPMENT OF FLY ASH-BASED GEOPOLYMER CONCRETE , 2004 .

[7]  Jay G. Sanjayan,et al.  An investigation of the mechanisms for strength gain or loss of geopolymer mortar after exposure to elevated temperature , 2009 .

[8]  Jay G. Sanjayan,et al.  Damage behavior of geopolymer composites exposed to elevated temperatures , 2008 .

[9]  B. V. Rangan,et al.  Fly ash-based geopolymer concrete: study of slender reinforced columns , 2007 .

[10]  S. Küçükbayrak,et al.  Characterization of sintered coal fly ashes , 2008 .

[11]  J. Sanjayan,et al.  Microcracking and strength development of alkali activated slag concrete , 2001 .

[12]  J. Wastiels,et al.  Low-temperature synthesized aluminosilicate glasses , 1996 .

[13]  G. A. Khoury,et al.  Mechanical Properties of Hardened Cement Paste Exposed to Temperatures up to 700 C (1292 F) , 1990 .

[14]  U. Schneider.  Recommendation of RILEM TC 200-HTC: Mechanical concrete properties at high temperatures—modelling and application , 2007 .

[15]  J. Deventer,et al.  Thermal evolution of metakaolin geopolymers: Part 1 – Physical evolution , 2006 .

[16]  Kwesi Sagoe-Crentsil,et al.  Comparative performance of geopolymers made with metakaolin and fly ash after exposure to elevated temperatures , 2007 .

[17]  Kenneth J. D. MacKenzie,et al.  Thermal behaviour of inorganic geopolymers and composites derived from sodium polysialate , 2003 .

[18]  M. Pigeon,et al.  Effects of Water Absorption on Performance of Concretes Subjected to Accelerated Freezing-and-Thawing Tests , 2003 .

[19]  J. Davidovits.  Geopolymers : inorganic polymeric new materials , 1991 .

[20]  V. Li,et al.  Influence of microcracking on water absorption and sorptivity of ECC , 2009 .

[21]  K. Chawla,et al.  Mechanical Behavior of Materials , 1998 .

[22]  Kwesi Sagoe-Crentsil,et al.  Factors affecting the performance of metakaolin geopolymers exposed to elevated temperatures , 2008 .

[23]  J. Deventer,et al.  Understanding the relationship between geopolymer composition, microstructure and mechanical properties , 2005 .

[24]  V. Kodur,et al.  Stress-strain curves for high strength concrete at elevated temperatures , 2004 .