Broadband Dielectric Spectroscopy: A Viable Technique for Aging Assessment of Low-Voltage Cable Insulation Used in Nuclear Power Plants

This paper deals with the study of a non-destructive technique to detect the aging state of cable insulation used in a nuclear environment subjected to radiation and temperature aging. Cable samples were aged under dose rates ranging from 0.42 and 1.06 kGy/h at 55 and 85 °C. The imaginary part of the permittivity at 100 kHz is found to correlate well with mechanical properties, such as elongation at break, which is typically used to diagnose cable insulation, but it is a destructive property and cannot be used on field. It has been demonstrated also that a post-irradiation effect occurs even years after aging is stopped, increasing the imaginary permittivity and worsening mechanical properties due to the slow conversion of radicals into oxidized species. The main consequence is that when cable insulation is subjected to a nuclear accident, releasing a huge amount of radiation, the health of cable insulation must be followed also for a long time after the accident occurred, since aging due to oxidation progresses even when the radiation source is switched off.

[1]  N. Bowler,et al.  Aging Mechanisms and Monitoring of Cable Polymers , 2020 .

[2]  D. Fabiani,et al.  In situ defect recognition analysis on long cables through nondestructive reflectometry and dielectric spectroscopy methods: a comparison , 2020, 2020 IEEE Electrical Insulation Conference (EIC).

[3]  Davide Fabiani,et al.  Ageing Assessment of XLPE LV Cables for Nuclear Applications Through Physico-Chemical and Electrical Measurements , 2020, IEEE Access.

[4]  D. Fabiani,et al.  Post-irradiation effect analysis on XLPE-insulated LV cables used in nuclear power plants , 2019, 2019 2nd International Conference on Electrical Materials and Power Equipment (ICEMPE).

[5]  S. Banerjee LOW FREQUENCY DIELECTRIC SPECTROSCOPY AS A CONDITION MONITORING TECHNIQUE FOR LOW VOLTAGE CABLE IN NUCLEAR PLANTS , 2019 .

[6]  I. Furó,et al.  Effect of gamma radiation on carbon-black-filled EPDM seals in water and air , 2017 .

[7]  N. Bowler,et al.  Towards aging mechanisms of cross-linked polyethylene (XLPE) cable insulation materials in nuclear power plants , 2016, 2016 IEEE Conference on Electrical Insulation and Dielectric Phenomena (CEIDP).

[8]  Leonard S. Fifield,et al.  State of the Art Assessment of NDE Techniques for Aging Cable Management in Nuclear Power Plants FY2015 , 2015 .

[9]  D. Fabiani,et al.  Non-destructive condition monitoring of aged ethylene-propylene copolymer cable insulation samples using dielectric spectroscopy and NMR spectroscopy , 2015 .

[10]  D. Fabiani,et al.  Dielectric spectroscopy as a condition monitoring technique for cable insulation based on crosslinked polyethylene , 2015 .

[11]  T. Okamoto,et al.  Remaining issues of the degradation models of polymeric insulation used in nuclear power plant safety cables , 2014, IEEE Transactions on Dielectrics and Electrical Insulation.

[12]  Luca Verardi,et al.  Aging of nuclear power plant cables: in search of non-destructive diagnostic quantities , 2014 .

[13]  E. Suljovrujic,et al.  Post-irradiation effects in polyethylenes irradiated under various atmospheres , 2013 .

[14]  G. Montanari,et al.  Aging investigation of low-voltage cable insulation used in nuclear power plants , 2012, 2012 Annual Report Conference on Electrical Insulation and Dielectric Phenomena.

[15]  D. Fabiani,et al.  Effect of aspect ratio and water contamination on the electric properties of nanostructured insulating materials , 2010, IEEE Transactions on Dielectrics and Electrical Insulation.

[16]  Jong-Il Weon,et al.  Effects of thermal ageing on mechanical and thermal behaviors of linear low density polyethylene pipe , 2010 .

[17]  Xavier Colin,et al.  Lifetime prediction of polyethylene in nuclear plants , 2007 .

[18]  J. Schultz Dielectric Spectroscopy in Analysis of Polymers , 2006 .

[19]  K. Gillen,et al.  Accelerated aging and lifetime prediction: Review of non-Arrhenius behaviour due to two competing processes , 2005 .

[20]  L. Audouin,et al.  A Theoretical Model for the Diffusion-Limited Thermal Oxidation of Elastomers at Medium Temperatures , 2003 .

[21]  R. Clavreul Ageing of polymers in electrical equipment used in nuclear power plants , 1999 .

[22]  J. Mijovic,et al.  Dielectric spectroscopy of reactive polymers , 1998 .

[23]  G. Spadaro Effect of irradiation temperature and dose rate on the mechanical tensile behaviour of low density polyethylene , 1993 .

[24]  K. Gillen,et al.  Rigorous experimental confirmation of a theoretical model for diffusion-limited oxidation , 1992 .