Interfacial and electrokinetic characterization of IPA solutions related to semiconductor wafer drying and cleaning

In this study, the interfacial and electrokinetic phenomena of mixtures of isopropyl alcohol (IPA) and deionized (DI) water in relation to semiconductor wafer drying is investigated. The dielectric constant of an IPA solution linearly decreased from 78 to 18 with the addition of IPA to DI water. The viscosity of IPA solutions increased as the volume percentage of IPA in DI water increased. The zeta potentials of silica particles and silicon wafers were also measured in IPA solutions. The zeta potential approached neutral values as the volume ratio of IPA in DI water increased. A surface tension decrease from 72 to 23 dynes/cm was measured when the IPA concentration increased to 30 vol %. The surface excess of IPA at the air-liquid interface reached a maximum at around 20 vol % IPA. The adhesion forces of silica particles on silicon wafers were measured using atomic force microscopy in IPA solutions. The adhesion force increased as the volume percent of IPA in water increased. Lower particulate contamination was observed when the wafers were immersed and withdrawn from solutions containing less than 25 vol % IPA.

[1]  Ahmed Busnaina,et al.  The Effect of Additives in Post-Cu CMP Cleaning on Particle Adhesion and Removal , 2004 .

[2]  Jin-Goo Park,et al.  Interaction Forces Between Silica Particles and Wafer Surfaces during Chemical Mechanical Planarization of Copper , 2003 .

[3]  C. Lucy,et al.  Capillary electrophoresis in aqueous-organic media. Ionic strength effects and limitations of the Hubbard-Onsager dielectric friction model. , 2002, Journal of chromatography. A.

[4]  S. Ross,et al.  Colloidal Dispersions: Suspensions, Emulsions, and Foams , 2002 .

[5]  J. Britten.  A moving-zone Marangoni drying process for critical cleaning and wet processing , 1997 .

[6]  Susan L. Burkett,et al.  The effect of cleaning procedures on surface charging of various substrates , 1995 .

[7]  T. Ohmi,et al.  Static charge removal with IPA solution , 1994 .

[8]  J. Marra,et al.  Physical principles of Marangoni drying , 1991 .

[9]  J. A. M. Huethorst,et al.  Marangoni drying: A new extremely clean drying process , 1990 .

[10]  T. Ohmi,et al.  Particle-free wafer cleaning and drying technology , 1989 .

[11]  P. C. Hiemenz,et al.  Principles of colloid and surface chemistry , 1977 .

[12]  J. Visser.  On Hamaker constants: A comparison between Hamaker constants and Lifshitz-van der Waals constants , 1972 .

[13]  D. Shaw,et al.  Introduction to colloid and surface chemistry , 1970 .

[14]  A. Adamson.  Physical chemistry of surfaces , 1960 .

[15]  Ludwig Wilhelmy.  Ueber die Abhängigkeit der Capillaritäts‐Constanten des Alkohols von Substanz und Gestalt des benetzten festen Körpers , 1863 .