Cure shrinkage characterization and modeling of a polyester resin containing low profile additives

Resin Transfer Moulding (RTM) has great potential as an efficient and economical process for fabricating large and complicated composite structural components. The low capital investment cost required and process versatility in component integration and assembly make RTM very attractive for high volume automotive applications. One of the challenges facing the automotive field is the resulting surface finish of manufactured components. The shrinkage associated with the curing of thermoset resins contributes to the poor surface quality. Low profile additives (LPA) are added to the resin to compensate for the cure shrinkage; however their effects on the thermal, rheological and morphological properties of polyester resins are not well understood. In this paper, the effect of LPA on cure kinetics, cure shrinkage and viscosity of a polyester resin is studied through differential scanning calorimetry (DSC) and special rheological techniques. Models are developed to predict cure shrinkage, LPA expansion, cure kinetics and viscosity variations of the resin as a function of processing temperature. Finally, morphological changes in the resin with and without LPA, during isothermal cure, are studied with hot stage optical microscopy. The results show that the LPA content in the range tested had no significant effect on the cure kinetics. However, higher LPA content reduced cure rate and cure shrinkage. A minimum of 10% LPA was required to compensate for cure shrinkage. Shrinkage behavior of all formulations was similar until a degree-of-cure of 0.5. However, resin formulations with higher LPA content showed expansion at later stages during curing.

[1]  M. Vayer,et al.  Modeling PVTX diagrams: Application to various blends based on unsaturated polyester-influence of thermoplastic additive, fillers, and reinforcements , 2004 .

[2]  Jose M. Castro,et al.  KINETICS AND RHEOLOGY OF TYPICAL POLYURETHANE REACTION INJECTION MOLDING SYSTEMS. , 1980 .

[3]  G. George,et al.  Calorimetric and Rheological Characterization of a High-Performance Epoxy Curable at Low Temperatures , 2003 .

[4]  Roberto J. J. Williams,et al.  Cure of unsaturated polyester resins: 2. Influence of low-profile additives and fillers on the polymerization reaction, mechanical properties and surface rugosities , 1993 .

[5]  C. R. Nair,et al.  Rheological cure characterization of phosphazene–triazine polymers , 2003 .

[6]  Willis T. Schwartz,et al.  Mechanism of low‐profile behavior in single‐phase unsaturated polyester systems , 1975 .

[7]  C. Su,et al.  Effects of poly(vinyl acetate) and poly(methyl methacrylate) low-profile additives on the curing of unsaturated polyester resins. II. Morphological changes during cure , 1995 .

[8]  R. R. Hill,et al.  Analysis of volumetric changes of unsaturated polyester resins during curing , 1995 .

[9]  L. J. Lee,et al.  Shrinkage behaviour of low-profile unsaturated polyester resins , 1994 .

[10]  L. J. Lee,et al.  Dilatometric study of low profile unsaturated polyester resins , 1995 .

[11]  L. J. Lee,et al.  Effect of nanoclay on shrinkage control of low profile unsaturated polyester (UP) resin cured at room temperature , 2004 .

[12]  Musa R. Kamal,et al.  Kinetics and thermal characterization of thermoset cure , 1973 .

[13]  John W. Gillespie,et al.  Process-Induced Stress and Deformation in Thick-Section Thermoset Composite Laminates , 1992 .

[14]  M. Chan-Park,et al.  Tough low profile additives in sheet molding compound , 1996 .

[15]  L. J. Lee,et al.  Shrinkage control of low-profile unsaturated polyester resins cured at low temperature , 1998 .

[16]  L. J. Lee,et al.  Control of shrinkage and residual styrene of unsaturated polyester resins cured at low temperatures: I. Effect of curing agents , 2003 .

[17]  C. A. Hieber,et al.  Characterization of the rheological properties of a fast-curing epoxy-molding compound , 1997 .

[18]  L. J. Lee,et al.  Low temperature cure of unsaturated polyester resins with thermoplastic additives. II. Structure formation and shrinkage control mechanism , 2000 .

[19]  Yan‐Jyi Huang,et al.  Effects of poly(methyl methacrylate)-based low-profile additives on the properties of cured unsaturated polyester resins. II. Volume shrinkage characteristics and internal pigmentability , 2004 .

[20]  L. J. Lee,et al.  Effect of co‐promoter and secondary monomer on shrinkage control of unsaturated polyester (UP)/styrene (St)/low‐profile additive (LPA) systems cured at low temperatures , 2001 .

[21]  Michael R Wisnom,et al.  In-situ measurement of chemical shrinkage of MY750 epoxy resin by a novel gravimetric method , 2004 .

[22]  L. J. Lee,et al.  Low temperature cure of unsaturated polyester resins with thermoplastic additives: I. Dilatometry and morphology study , 2000 .

[23]  Zhiyi Zhang,et al.  Microvoids in unsaturated polyester resins containing poly(vinyl acetate) and composites with calcium carbonate and glass fibers , 2000 .

[24]  M. S. Kiasat,et al.  The effect of the addition of a low profile additive on the curing shrinkage of an unsaturated polyester resin , 1999 .

[25]  K. Schoch,et al.  Real-time measurement of resin shrinkage during cure , 2004 .

[26]  Yan‐Jyi Huang,et al.  Effects of poly(vinyl acetate) and poly(vinyl chloride‐ co‐vinyl acetate) low‐profile additives on properties of cured unsaturated polyester resins. I. Volume shrinkage characteristics and internal pigmentability , 2003 .

[27]  Yan-Jyi Huang,et al.  Volume shrinkage characteristics in the cure of low-shrink unsaturated polyester resins , 1996 .

[28]  L. J. Lee,et al.  Effects of thermoplastic additives on the cure of unsaturated polyester resins , 1991 .

[29]  Henry Lee,et al.  Handbook of Epoxy Resins , 1967 .