Silica-silica polyimide buffered optical fibre irradiation and strength experiment at cryogenic temperatures for 355 nm pulsed lasers

Abstract A controlled UV-light delivery system is envisioned to be built in order to study the stability properties of superconducting strands. The application requires a wave guide from room temperature to cryogenic temperatures. Hydrogen loaded and unloaded polyimide buffered silica–silica 100 μm core fibres were tested at cryogenic temperatures. A thermal stress test was done at 1.9 K and at 4.2 K which shows that the minimal mechanical bending radius for the fibre can be 10 mm for testing (transmission was not measured). The cryogenic transmission loss was measured for one fibre to assess the magnitude of the transmission decrease due to microbending that takes place during cooldown. UV-irradiation degradation measurements were done for bent fibres at 4.2 K with a deuterium lamp and 355 nm pulsed lasers. The irradiation tests show that the fibres have transmission degradation only for wavelengths smaller than 330 nm due to the two photon absorption. The test demonstrates that the fibres are suitable for the cryogenic UV applications with 355 nm and 70 μJ pulsed lasers.

[1]  Karl-Friedrich Klein,et al.  High-OH fibers with higher stability in the UV-region , 2006, SPIE BiOS.

[2]  L. Rossi,et al.  Self Field Instability in High- ${\rm J}_{\rm c}$ ${\rm Nb}_{3}{\rm Sn}$ Strands With High Copper Residual Resistivity Ratio , 2009, IEEE Transactions on Applied Superconductivity.

[3]  P. Tixador,et al.  A novel technique for minimum quench energy measurements in superconductors using a single-mode diode laser , 2005 .

[4]  David L. Griscom,et al.  Defect structure of glasses: Some outstanding questions in regard to vitreous silica , 1985 .

[5]  M. A. Biondi,et al.  Infrared Absorption of Aluminum, Copper, Lead, and Nickel at 4.2°K , 1968 .

[6]  D. Lynch,et al.  Optical properties of metals. , 1981, Applied optics.

[7]  K. Chen,et al.  Modelling and Analysis of UV Laser Micromachining of Copper , 2001 .

[8]  Martin N. Wilson,et al.  Superconducting Magnets , 1984 .

[9]  Karl-Friedrich Klein,et al.  UV fibers for applications below 200 nm , 2001, SPIE BiOS.

[10]  Anatolii Viacheslavovich Sokolov,et al.  Optical Properties of Metals , 1967 .

[11]  Kenneth T. V. Grattan,et al.  UV-stabilized silica-based fibre for applications around 200 nm wavelength , 1997 .

[12]  David L. Griscom,et al.  Thermal bleaching of x-ray-induced defect centers in high purity fused silica by diffusion of radiolytic molecular hydrogen , 1984 .

[13]  John Crisp,et al.  Introduction to Fiber Optics , 1996 .

[14]  Peter Karlitschek,et al.  Influence of hydrogen on the colour center formation in optical fibers induced by pulsed UV-laser radiation. , 1998 .

[15]  S. Mihailov,et al.  Dependence of the damage and transmission properties of fused silica fibers on the excimer laser wavelength. , 1988, Applied optics.