Bulky amorphous alloys were found to form in Zr-Al-M (M=Co, Ni, Cu) systems by arc melting on a copper hearth. The largest thickness for glass formation is 6. 1 mm for Zr 60 Al 10 Co 3 Ni 9 Cu 18 , 6.8 mm for Zr 60 Al 15 Co 5 Ni 15 Cu 5 and 6.2 mm for Zr 55 Al 20 Co 17.5 Ni 2.5 Cu 5 . The optimum composition for glass-forming ability shifts from the Cu-rich side to the Co-rich side through the Ni-rich side with increasing Al content from 10 to 20%. The use of a metallic mold casting process enabled the formation of amorphous cylinders with the largest diameter of 7 mm for the three alloys. The compositional effect for the large glass-forming ability has also been discussed by taking the present data into consideration. The cast amorphous Zr 60 Al 10 Co 3 Ni 9 Cu 18 alloy subjected to tensile testing exhibits distinct serrated flow before final fracture. The generation of the serrated flow is noticed because the alloy has a ductile nature which enables the momentary stop of the shear sliding. The Young's modulus, tensile fracture strength and fracture elongation are 97 GPa, 1510 MPa and 2.0%, respectively. The fracture occurs along the maximum shear plane and the fracture surface consists of a well-developed vein pattern. The size of their veins is about 10 times as large as that for the melt-spun ribbon and hence the shear deformation region occurs in a much wider region for the cast alloy, indicating the necessity of a larger amount of energy up to final fracture. The finding of the amorphous alloys with the large glass-forming ability and the extremely ductile nature is important for the subsequent development of metallic glassy materials.
[1]
Hung Chen.
REVIEW ARTICLE: Glassy metals
,
1980
.
[2]
M. Yamane,et al.
Effect of Heat-Treatment for Nucleation on the Crystallization of MgO-Al2O3-SiO2 Glass Containing TiO2
,
1988
.
[3]
A. Inoue,et al.
Extremely wide supercooled liquid region and large glass-forming ability in Zr65 − xAl7.5Cu17.5Ni10Bex amorphous alloys
,
1994
.
[4]
A. Inoue,et al.
New Amorphous Mg-Ce-Ni Alloys with High Strength and Good Ductility
,
1988
.
[5]
Tao Zhang,et al.
Glass-forming ability of alloys
,
1993
.
[6]
K. Amiya,et al.
Ti-based amorphous alloys with a wide supercooled liquid region
,
1994
.