Modification of hydrogen-passivated silicon by a scanning tunneling microscope operating in air

The chemical modification of hydrogen‐passivated n‐Si (111) surfaces by a scanning tunneling microscope (STM) operating in air is reported. The modified surface regions have been characterized by STM spectroscopy, scanning electron microscopy (SEM), time‐of‐flight secondary‐ion mass spectrometry (TOF SIMS), and chemical etch/Nomarski microscopy. Comparison of STM images with SEM, TOF SIMS, and optical information indicates that the STM contrast mechanism of these features arises entirely from electronic structure effects rather than from topographical differences between the modified and unmodified substrate. No surface modification was observed in a nitrogen ambient. Direct writing of features with 100 nm resolution was demonstrated. The permanence of these features was verified by SEM imaging after three months storage in air. The results suggest that field‐enhanced oxidation/diffusion occurs at the tip‐substrate interface in the presence of oxygen.

[1]  Christie R. K. Marrian,et al.  Low‐voltage electron beam lithography with a scanning tunneling microscope , 1990 .

[2]  J. Dieleman,et al.  Direct writing in Si with a scanning tunneling microscope , 1989 .

[3]  R. A. Bowling,et al.  Electrical characteristics of reoxidized-nitrided chemical vapor deposited oxides , 1989 .

[4]  Tadahiro Ohmi,et al.  Control Factor of Native Oxide Growth on Silicon in Air or in Ultrapure Water , 1989 .

[5]  M. Grundner,et al.  Reaction of water with hydrofluoric acid treated silicon(111) and (100) surfaces , 1989 .

[6]  Weimer,et al.  Band bending and the apparent barrier height in scanning tunneling microscopy. , 1989, Physical review. B, Condensed matter.

[7]  T. Takahagi,et al.  The formation of hydrogen passivated silicon single‐crystal surfaces using ultraviolet cleaning and HF etching , 1988 .

[8]  Y. Chabal,et al.  Infrared spectroscopy of Si(111) surfaces after HF treatment: Hydrogen termination and surface morphology , 1988 .

[9]  E. Kratschmer,et al.  Nanostructure technology , 1988 .

[10]  W. Kaiser,et al.  Scanning tunneling microscopy characterization of the geometric and electronic structure of hydrogen-terminated silicon surfaces , 1988 .

[11]  R. Silver,et al.  Direct writing of submicron metallic features with a scanning tunneling microscope , 1987 .

[12]  F. J. Grunthaner,et al.  Chemical and electronic structure of the SiO2/Si interface , 1987 .

[13]  Chang,et al.  Unusually low surface-recombination velocity on silicon and germanium surfaces. , 1986, Physical review letters.

[14]  Roger Fabian W. Pease,et al.  Lithography with the scanning tunneling microscope , 1986 .

[15]  H. Grubin.  The physics of semiconductor devices , 1979, IEEE Journal of Quantum Electronics.

[16]  R. Kirby,et al.  Electron beam induced effects on gas adsorption utilizing auger electron spectroscopy: Co and O2 on Si: I. Adsorption studies , 1974 .

[17]  B. Joyce,et al.  Electron beam-adsorbate interactions on silicon surfaces , 1973 .

[18]  J. Coad,et al.  Electron-beam assisted adsorption on the Si(111) surface , 1970 .