Enhanced visible photoluminescence from ultrathin ZnO films grown on Si-nanowires by atomic layer deposition

Bright room temperature visible emission is obtained in heterostructures consisting of approximately 3.5 nm thick ZnO ultrathin films grown on Si-nanowires produced by means of self-masking dry etching in hydrogen-containing plasma. The ZnO films were deposited on Si-nanowires by using atomic layer deposition (ALD) under an ambient temperature of 25 degrees C. The orders of magnitude enhancement in the intensity of the room temperature photoluminescence peaked around 560 nm in the present ZnO/Si-nanowire heterostructures is presumably due to the high aspect (surface/volume) ratio inherent to the Si-nanowires, which has, in turn, allowed considerably more ZnO material to be grown on the template and led to markedly more efficient visible emission. Moreover, the ordered nanowire structure also features an extremely low reflectance (approximately 0.15%) at 325 nm, which may further enhance the efficiency of emission by effectively trapping the excitation light.

[1]  J. Shieh,et al.  Well-Aligned Silicon Nanograss Fabricated by Hydrogen Plasma Dry Etching , 2005 .

[2]  Chun-Wei Chen,et al.  Anomalous blueshift in emission spectra of ZnO nanorods with sizes beyond quantum confinement regime , 2006 .

[3]  D. Shen,et al.  The structural and optical properties of ZnO nanorod arrays , 2005 .

[4]  Peidong Yang,et al.  Nanowire ultraviolet photodetectors and optical switches , 2002 .

[5]  Changhong Liu,et al.  High‐Density, Ordered Ultraviolet Light‐Emitting ZnO Nanowire Arrays , 2003 .

[6]  C. Ku,et al.  Fabrication of epitaxial ZnO films by atomic-layer deposition with interrupted flow , 2009 .

[7]  Henryk Temkin,et al.  Size-dependent surface luminescence in ZnO nanowires , 2004 .

[8]  Zhong Lin Wang,et al.  Piezoelectric field effect transistor and nanoforce sensor based on a single ZnO nanowire. , 2006, Nano letters.

[9]  Peidong Yang,et al.  Low-temperature wafer-scale production of ZnO nanowire arrays. , 2003, Angewandte Chemie.

[10]  R. K. Thareja,et al.  Photoluminescence and ultraviolet laser emission from nanocrystalline ZnO thin films , 2001 .

[11]  Mato Knez,et al.  Synthesis and Surface Engineering of Complex Nanostructures by Atomic Layer Deposition , 2007 .

[12]  O. Urakawa,et al.  Small - , 2007 .

[13]  Larry E. Halliburton,et al.  Role of copper in the green luminescence from ZnO crystals , 2002 .

[14]  Yu Hang Leung,et al.  Optical properties of ZnO nanostructures. , 2006, Small.

[15]  Yiying Wu,et al.  Room-Temperature Ultraviolet Nanowire Nanolasers , 2001, Science.

[16]  W. Oldham,et al.  Plasma etch effects on low‐temperature selective epitaxial growth of silicon , 1992 .

[17]  Jiann Shieh,et al.  Plasma nanofabrications and antireflection applications , 2007 .

[18]  Jiann Shieh,et al.  Robust Airlike Superhydrophobic Surfaces , 2010, Advanced materials.

[19]  Younan Xia,et al.  One‐Dimensional Nanostructures: Synthesis, Characterization, and Applications , 2003 .

[20]  Robert P. H. Chang,et al.  Fabrication of inverted opal ZnO photonic crystals by atomic layer deposition , 2005 .

[21]  Andries Meijerink,et al.  Identification of the transition responsible for the visible emission in ZnO using quantum size effects , 2000 .

[22]  U. Chung,et al.  Fabrication and device characterization of omega-shaped-gate ZnO nanowire field-effect transistors. , 2006, Nano letters.

[23]  F. Boey,et al.  Correlation between the characteristic green emissions and specific defects of ZnO. , 2010, Physical chemistry chemical physics : PCCP.

[24]  Song-Yeu Tsai,et al.  Visible Photoluminescence of Ultrathin ZnO Nanowire at Room Temperature , 2006 .

[25]  M. Ferenets,et al.  Thin Solid Films , 2010 .