Heat Transfer in Polypropylene‐Based Foams Produced Using Different Foaming Processes

This paper presents the characterization of the cellular structure and thermal conduction behaviour of polypropylene foams produced using different foaming processes, with the aim of selecting the best possible PP foam thermal insulator. Thermal conductivity results have shown that the global heat transfer behaviour is controlled by the relative density. For relative densities higher than 0.2, thermal conductivity differences were insignificant, the data being predicted by the mixture's rule and Russell's model. In the low density range, all of the proposed models underestimated the overall conductivity, the effect of the processing method being more significant, slight differences being observed between foams produced by extrusion and those produced by gas dissolution with higher cell sizes and anisotropies. Foams with finer cellular structures showed to be better insulating materials.

[1]  J. Saja,et al.  An experimental study on the thermal conductivity of aluminium foams by using the transient plane source method , 2008 .

[2]  C. Körner,et al.  Thermal conductivity of AZ91 magnesium integral foams measured by the Transient Plane Source method , 2008 .

[3]  J. Saja,et al.  Foams based on low density polyethylene/hectorite nanocomposites: Thermal stability and thermo‐mechanical properties , 2007 .

[4]  J. Saja,et al.  Foaming behaviour and cellular structure of LDPE/hectorite nanocomposites , 2007 .

[5]  J. Saja,et al.  Density gradients in aluminium foams: characterisation by computed tomography and measurements of the effective thermal conductivity , 2007 .

[6]  M. Rodríguez-Pérez.  Crosslinked Polyolefin Foams: Production, Structure, Properties, and Applications , 2005 .

[7]  J. Saja,et al.  Measurement of the thermal diffusivity and specific heat capacity of polyethylene foams using the transient plane source technique , 2004 .

[8]  J. A. de Saja,et al.  Applicability of the transient plane source method to measure the thermal conductivity of low‐density polyethylene foams , 2004 .

[9]  Chul B. Park,et al.  Effect of Talc Content on the Volume Expansion Ratio of Extruded PP Foams , 2003 .

[10]  J. Saja,et al.  The microestructure of polyethylene foams produced by a nitrogen solution process , 2001 .

[11]  J. Saja,et al.  The Thermal Conductivity of a Polyethylene Foam Block Produced by a Compression Molding Process , 2001 .

[12]  J. Saja,et al.  The effect of blending on the physical properties of crosslinked closed cell polyethylene foams , 1999 .

[13]  Chul B. Park,et al.  The effect of talc on cell nucleation in extrusion foam processing of polypropylene with CO2 and isopentane , 1998 .

[14]  S. Gustafsson,et al.  THERMAL CONDUCTIVITY, THERMAL DIFFUSIVITY, AND SPECIFIC HEAT OF THIN SAMPLES FROM TRANSIENT MEASUREMENTS WITH HOT DISK SENSORS , 1994 .

[15]  N. C. Hilyard,et al.  Low density cellular plastics , 1994 .

[16]  A G Leach,et al.  The thermal conductivity of foams. I. Models for heat conduction , 1993 .

[17]  S. Gustafsson.  Transient plane source techniques for thermal conductivity and thermal diffusivity measurements of solid materials , 1991 .

[18]  K. T. Collington,et al.  The production of cellular crosslinked polyolefins. II: The injection moulding and press moulding techniques , 1988 .