Effects of Normalizing Annealing on the Recrystallization Texture of 4.2wt.%Si Non-Oriented Electrical Steel Thin Sheets

The 4.2wt.%Si non-oriented electrical steel thin sheets with the thickness of 0.30mm were produced by the conventional procedure including hot rolling, cold rolling and annealing. The recrystallization texture was analyzed with emphasis on the effect of normalizing annealing. The results show that the  fiber with peak at {111} is weaker and η fiber is stronger in the sheets with normalizing annealing than those without normalizing annealing, either under the cold rolled reduction of 77% or 86%. Effects of normalizing annealing on the recrystallization texture can be explained in terms of the characteristic of the shear bands formed during cold rolling process.