Production of belite calcium sulfoaluminate cement using sulfur as a fuel and as a source of clinker sulfur trioxide: pilot kiln trial

A pilot-scale trial was undertaken in a 7·4 m kiln to demonstrate the production of belite calcium sulfoaluminate cement clinker using sulfur as a raw feed. The sulfur was introduced in its elemental form as fuel to the burner, thus partially offsetting fuel costs while providing sulfur trioxide which is incorporated in the clinker. The study demonstrates that sulfur trioxide is readily sequestered into cement clinker in a standard rotary kiln; however, some scrubbing of the exit gas may still be required. As the products of scrubbing (anhydrite or gypsum) are usually required to optimise the cement formulation, the recovered sulfur product can find an immediate use in the final cement product. This trial demonstrates the successful production of targeted belite calcium sulfoaluminate clinkers at scale using sulfur as both a fuel and sulfur trioxide source.

[1]  Kurt E. Peray.  The Rotary Cement Kiln , 1986 .

[2]  E. Tillmanns,et al.  Ternesite, Ca5(SiO4)2SO4, a new mineral from the Ettringer Bellerberg/Eifel, Germany , 1997 .

[3]  Ali Hasanbeigi,et al.  Emerging energy-efficiency and CO2 emission-reduction technologies for cement and concrete production: A technical review , 2012 .

[4]  K. Scrivener,et al.  Phase compositions and equilibria in the CaO–Al2O3–Fe2O3–SO3 system, for assemblages containing ye'elimite and ferrite Ca2(Al,Fe)O5 , 2013 .

[5]  G. Will,et al.  Charge density in anhydrite, CaSO4, from X-ray and neutron diffraction measurements , 1980 .

[6]  Theodore Hanein,et al.  Thermodynamic data of ye’elemite (C4A3S̅ ) for cement clinker equilibrium calculations , 2015 .

[7]  R. J. Hill,et al.  Rietveld crystal structure refinements, crystal chemistry and calculated powder diffraction data for the polymorphs of dicalcium silicate and related phases , 1995 .

[8]  J. Greneche,et al.  Characterisation of iron inclusion during the formation of calcium sulfoaluminate phase , 2010 .

[9]  M. García-Maté,et al.  Rietveld quantitative phase analysis of Yeelimite-containing cements , 2012 .

[10]  A. Ayuela,et al.  Structure, Atomistic Simulations, and Phase Transition of Stoichiometric Yeelimite , 2013 .

[11]  Á. G. Torre,et al.  Pseudocubic Crystal Structure and Phase Transition in Doped Ye’elimite , 2014 .

[12]  S. J. Louisnathan.  Refinement of the crystal structure of a natural gehlenite, Ca 2 Al(Al,Si) 2 O 7 , 1971 .

[13]  S. Geller,et al.  The crystal structure of brownmillerite, Ca2FeAlO5 , 1971 .

[14]  A. Jephcoat,et al.  A correction for powder diffraction peak asymmetry due to axial divergence , 1994 .

[15]  W. A. Dollase,et al.  Correction of intensities for preferred orientation in powder diffractometry: application of the March model , 1986 .

[16]  J. Ideker,et al.  Advances in alternative cementitious binders , 2011 .

[17]  E. Gartner.  Industrially interesting approaches to “low-CO2” cements ☆ , 2004 .

[18]  Jerome B. Hastings,et al.  Rietveld refinement of Debye–Scherrer synchrotron X‐ray data from Al2O3 , 1987 .

[19]  J. Bass,et al.  Orthorhombic perovskite CaTiO3 and CdTiO3: structure and space group , 1987 .

[20]  Mohammed S. Imbabi,et al.  Lowering the carbon footprint and energy consumption of cement production: A novel Calcium SulfoAluminate cement production process , 2016 .

[21]  M. Juenger,et al.  Synthesis and hydration of calcium sulfoaluminate-belite cements with varied phase compositions , 2011 .