Formation of highly adherent nano-porous alumina on Ti-based substrates: a novel bone implant coating

Thin, nano-porous, highly adherent layers of anodised aluminium formed on the surface of titanium alloys are being developed as coatings for metallic surgical implants. The layers are formed by anodisation of a 1–5 μm thick layer of aluminium which has been deposited on substrate material by electron beam evaporation. The surface ceramic layer so produced is alumina with 6–8 wt % phosphate ions and contains ∼5×108 cm−2 pores with a ∼160 nm average diameter, running perpendicular to the surface. Mechanical testing showed the coatings' shear and tensile strength to be at least 20 and 10 MPa, respectively. Initial cell/material studies show promising cellular response to the nano-porous alumina. A normal osteoblastic growth pattern with cell number increasing from day 1 to 21 was shown, with slightly higher proliferative activity on the nano-porous alumina compared to the Thermanox control. Scanning electron microscopy (SEM) examination of the cells on the porous alumina membrane showed normal osteoblast morphology. Flattened cells with filopodia attaching to the pores and good coverage were also observed. In addition, the pore structure produced in these ceramic coatings is expected to be suitable for loading with bioactive material to enhance further their biological properties.

[1]  G. Thompson,et al.  Nucleation and growth of porous anodic films on aluminium , 1978, Nature.

[2]  Larry L. Hench,et al.  Clinical performance of skeletal prostheses , 1995 .

[3]  Larry L. Hench,et al.  Bioceramics: From Concept to Clinic , 1991 .

[4]  G. Thompson,et al.  Porous anodic alumina: fabrication, characterization and applications , 1997 .

[5]  W. Augustyniak,et al.  Low energy cosmic ray erosion of ice grains in interplanetary and interstellar media , 1978, Nature.

[6]  R. C. Furneaux,et al.  The formation of controlled-porosity membranes from anodically oxidized aluminium , 1989, Nature.

[7]  Frank Müller,et al.  Self-Organized Formation of Hexagonal Pore Structures in Anodic Alumina , 1998 .

[8]  M V Swain,et al.  Interfacial bond strength of electrophoretically deposited hydroxyapatite coatings on metals , 1999, Journal of materials science. Materials in medicine.

[9]  G R Nakayama,et al.  Assessment of the Alamar Blue assay for cellular growth and viability in vitro. , 1997, Journal of immunological methods.

[10]  K. Rie,et al.  Plasma Deposition, Plasma Coating, and Ion Implantation to Improve Metallic Implants and Prostheses , 2000 .

[11]  V. Fornasier,et al.  Hydroxyapatite coating on carbon composite hip implants in dogs. , 1992, The Journal of bone and joint surgery. British volume.

[12]  M. Cabrini,et al.  Increasing of the corrosion resistance of the Ti6Al4V alloy by high thickness anodic oxidation , 1992 .

[13]  Larry L. Hench,et al.  Medical Materials for the Next Millennium , 1999 .

[14]  S D Cook,et al.  The effect of surface macrotexture and hydroxylapatite coating on the mechanical strengths and histologic profiles of titanium implant materials. , 1987, Journal of biomedical materials research.

[15]  Enrica Verne,et al.  Coatings on Al2O3 by bioactive glass-ceramics , 2000 .