Wear rates and wear mechanisms of alumina-based tools cutting steel at a low cutting speed

Abstract Three ceramic insert materials, zirconia-toughened alumina (Al 2 O 3 –7vol%ZrO 2 ), mixed-based alumina (Al 2 O 3 –TiN–TiC–ZrO 2 ) and alumina reinforced with SiC whiskers (Al 2 O 3 –SiC w ), were used to cut AISI 1040 steel at 3.9 m s −1 . In addition, a traditional grade P10 insert (WC–TiC–Co) was tested. The lifetimes, according to KT/KM and VB B criteria, were determined using a profilometer and by image processing. The worn zones were observed with scanning electron microscopy techniques. Adhesion and plastic deformation were dominant wear mechanisms in zirconia-toughened alumina, mixed-based alumina and sintered carbide P10, both in the craters and in the cutting edges. As well as adhesion in alumina reinforced with SiC whiskers, a chipping wear mechanism was observed.