Structure and properties of amorphous and nanocrystalline NiTi prepared by severe plastic deformation and annealing

The formation of homogeneous nanocrystalline structure by nanocrystallization of amorphous NiTi subjected to high pressure torsion is demonstrated. Structural evolution during annealing was investigated and homogeneous nanocrystalline structures with different grain sizes have been obtained by controlled annealing. Nanocrystallization results in the record value of room temperature strength for this material equal to 2650 MPa with an elongation to failure of about 5%. At elevated temperatures of (0.4…0.5)Tm nanocrystalline nitinol showed a high ultimate strength with sufficient elongation (up to 200%). The observation that the shape and the size of grains after deformation remain close to that of the initial state suggests that in nanocrystalline NiTi such mechanism as grain boundary sliding and grain rotation are active and the generation and motion of dislocations play the role of accommodation of stress concentration.

[1]  P. Sanders,et al.  The strength of nanocrystalline metals with and without flaws , 1997 .

[2]  R. Valiev,et al.  Tensile superplasticity in a nanocrystalline nickel aluminide , 1998 .

[3]  P. Moine,et al.  Wear behaviour of N+ implanted NiTi alloys , 1986 .

[4]  C. Saw,et al.  The synthesis of amorphous NiTi alloy powders by mechanical alloying , 1985 .

[5]  R. Valiev,et al.  Bulk nanostructured materials from severe plastic deformation , 2000 .

[6]  H. V. Swygenhoven,et al.  Microscopic description of plasticity in computer generated metallic nanophase samples: a comparison between Cu and Ni , 1999 .

[7]  D. Parkin,et al.  Crystal-to-amorphous transformation of NiTi induced by cold rolling , 1990 .

[8]  C. Koch,et al.  The influence of mill energy and temperature on the structure of the TiNi intermetallic after mechanical attrition , 1993 .

[9]  C. Pande,et al.  Yield stress of fine grained materials , 1998 .

[10]  D. G. Morris.  Mechanical Behaviour of Nanostructured Materials , 1998 .

[11]  K. Tsuchiya,et al.  Crystal refinement and amorphisation by cold rolling in tini shape memory alloys , 2001 .

[12]  A. A. Nazarov,et al.  Microstructures and hardness of ultrafine-grained Ni3Al , 1993 .

[13]  W. Johnson,et al.  Structural difference rule for amorphous alloy formation by ion mixing , 1983 .

[14]  R. Valiev,et al.  Thermal evolution of high-purity and boron-doped sub-microcrystalline Ni3Al produced by severe plastic deformation , 1999 .

[15]  R. Valiev,et al.  Investigations and applications of severe plastic deformation , 2000 .

[16]  Sarah Green,et al.  The surface performance of shot peened and ion implanted NiTi shape memory alloy , 1995 .

[17]  Diego Mantovani,et al.  Shape memory alloys: Properties and biomedical applications , 2000 .