论文信息 - The effect of hot isostatic pressing on crack healing, microstructure, mechanical properties of Rene88DT superalloy prepared by laser solid forming

The effect of hot isostatic pressing on crack healing, microstructure, mechanical properties of Rene88DT superalloy prepared by laser solid forming

Crack characterization in Rene88DT superalloy prepared by laser solid forming (LSF) was investigated; the effect of hot isostatic pressing (HIP) on crack healing, microstructure and mechanical properties was also analyzed. It was found that cracks in LSFed Rene88DT mainly nucleate and propagate in the overlap zone of laser-deposited passes, and can be attributed to the liquation cracks. The size and amount of the cracks in LSFed Rene88DT are significantly affected by the overlap of as-deposited passes. Through HIP processing, crack healing occurred, which leads to a substantial improvement of the mechanical properties of LSFed Rene88DT superalloy. However, the insufficient overlap will result in very large cracks in the deposit, which makes the diffusion bonding during HIP not completely eliminate the local segregation of Ti and Nb in the crack healing region.

[1] J. A. Romero,et al. Using the laser engineered net shaping (LENS) process to produce complex components from a CAD solid model , 1997, Photonics West.

[2] O. Ojo,et al. Liquid film migration of constitutionally liquated γ′ in weld heat affected zone (HAZ) of Inconel 738LC superalloy , 2004 .

[3] J. B. Won,et al. Effect of HIP process on the micro-structural evolution of a nickel-based superalloy , 2006 .

[4] H. Bor,et al. Influence of hot isostatic pressing on the fracture transitions in the fine grain MAR-M247 superalloys , 2004 .

[5] Xiaofeng Zhu,et al. Boundary liquation and interface cracking characterization in laser deposition of Inconel 738 on directionally solidified Ni-based superalloy , 2005 .