论文信息 - Failure Mechanisms in Bolted CFRP

Failure Mechanisms in Bolted CFRP

An experimental investigation on the damage mechanisms of mechanically fastened joints in composite laminates is presented. This information concerning damage mechanisms is required before developing damage progression models. For doublelap joints with fingertight washers, specimens that fail in the bearing, tension and shearout modes are investigated. For fully failed specimens and for specimens loaded to several percentages of failure load, the damage mechanisms are investigated using Xradiography and sectioning. It is concluded that failure occurs by a process of damage accumulation, where the failure mechanisms present are fiber fracture, delamination at the laminate loaded hole, matrix cracks and related fiber microbuckling, and internal delamination. Modelling this interaction between failure mechanisms requires further analytical efforts. Due to the importance of the through-thickness stresses present at the hole boundary, delamination has a significant effect on the joint strength, so the use of a threedimensional failure criterion is suggested.

F. L. Matthews | P. Camanho | P. P. Camanho | S. Bowron | S. Bowron

[1] Wen-Hsiang Chen,et al. Failure Process and Pin-Bearing Strength of Laminated Composites at Elevated Temperature , 1992 .

[2] Fu-Kuo Chang,et al. Post-Failure Analysis of Bolted Composite Joints in Tension or Shear-Out Mode Failure , 1987 .

[3] Wen-Hwa Chen,et al. Numerical and Experimental Failure Analysis of Composite Laminates with Bolted Joints under Bending Loads , 1995 .

[4] Fu-Kuo Chang,et al. Strength Envelope of Bolted Composite Joints under Bypass Loads , 1996 .

[5] Walter J. Horn,et al. Influence of Clamp-Up Force on the Strength of Bolted Composite Joints , 1994 .

[6] Fu-Kuo Chang,et al. Bearing Failure of Bolted Composite Joints. Part I: Experimental Characterization , 1996 .

[7] Ran Y. Kim,et al. Experimental and Analytical Studies On the Onset of Delamination in Laminated Composites , 1984 .

[8] Larry Lessard,et al. Two-Dimensional Modeling of Composite Pinned-Joint Failure , 1995 .

[9] Charles E. Harris,et al. Internal State Variable Approach for Predicting Stiffness Reductions in Fibrous Laminated Composites with Matrix Cracks , 1989 .

[10] Lin Ye,et al. Role of matrix resin in delamination onset and growth in composite laminates , 1988 .

[11] Fu-Kuo Chang,et al. An Accumulative Damage Model for Tensile and Shear Failures of Laminated Composite Plates , 1995 .