Casting defects in low-pressure die-cast aluminum alloy wheels

Defects in automotive aluminum alloy casting continue to challenge metallurgists and production engineers as greater emphasis is placed on product quality and production cost. A range of casting-related defects found in low-pressure die-cast aluminum wheels were examined metallographically in samples taken from several industrial wheel-casting facilities. The defects examined include macro- and micro- porosity, entrained oxide films, and exogenous oxide inclusions. Particular emphasis is placed on the impact of these defects with respect to the three main casting-related criteria by which automotive wheel quality are judged: wheel cosmetics, air-tightness, and wheel mechanical performance.

[1]  David L. McDowell,et al.  Microstructure-based fatigue modeling of cast A356-T6 alloy , 2003 .

[2]  M. Rappaz,et al.  Modeling of microporosity, macroporosity, and pipe-shrinkage formation during the solidification of alloys using a mushy-zone refinement method: Applications to aluminum alloys , 2002 .

[3]  Michel Rappaz,et al.  Modeling of casting, welding and advanced solidification processes-V : proceedings of the fifth International Conference on Modeling of Casting and Welding Processes, held in Davos Switzerland, September 16-21, 1990 , 1991 .

[4]  J. R. Griffiths,et al.  CASTING DEFECTS AND THE FATIGUE BEHAVIOUR OF AN ALUMINIUM CASTING ALLOY , 1990 .

[5]  K. Nogita,et al.  Eutectic solidification and its role in casting porosity formation , 2004 .

[6]  David L. McDowell,et al.  Computational micromechanics analysis of cyclic crack-tip behavior for microstructurally small cracks in dual-phase Al–Si alloys , 2001 .

[7]  A. S. Machin,et al.  The effect of solution heat-treatment time on the fatigue properties of an Al-Si-Mg casting alloy , 2002 .

[8]  Diran Apelian,et al.  Fatigue behavior of A356/357 aluminum cast alloys. Part II – Effect of microstructural constituents , 2001 .

[9]  Julie Huang,et al.  Simulation of microporosity formation in modified and unmodified A356 alloy castings , 1998 .

[10]  J. Campbell,et al.  Liquid metal quality , 2002 .

[11]  S. Cockcroft,et al.  Simulation of microporosity in A356 aluminium alloy castings , 2005 .

[12]  J. Gruzleski,et al.  Structure and properties of hypoeutectic Al-Si-Mg alloys modified with pure strontium , 1982 .

[13]  R. D. Pehlke,et al.  Mathematical modeling of porosity formation in solidification , 1985 .

[14]  A. L. Maples,et al.  A thermodynamic prediction for microporosity formation in aluminum-rich Al-Cu alloys , 1987 .

[15]  G. Sigworth,et al.  Mechanisms of porosity formation during solidification: A theoretical analysis , 1993 .

[16]  S. Felicelli,et al.  A model for prediction of pressure and redistribution of gas-forming elements in multicomponent casting alloys , 2000 .

[17]  David R Poirier,et al.  Microstructural effects on high-cycle fatigue-crack initiation in A356.2 casting alloy , 1999 .

[18]  G. Byczynski,et al.  The effects of strontium and grain refiner additions on the fatigue and tensile properties of industrial Al-Si-Cu-Mg alloy castings produced using the Ford Motor Company—Cosworth precision sand process , 2002 .

[19]  D. Apelian,et al.  Fatigue behavior of A356-T6 aluminum cast alloys. Part I. Effect of casting defects , 2001 .

[20]  D. See,et al.  Modeling microporosity in aluminum–silicon alloys: a review , 2001 .