Plastic shrinkage of mortars with shrinkage reducing admixture and lightweight aggregates studied by neutron tomography

Water transport in fresh, highly permeable concrete and rapid water evaporation from the concrete surface during the first few hours after placement are the key parameters influencing plastic shrinkage cracking. In this work, neutron tomography was used to determine both the water loss from the concrete surface due to evaporation and the redistribution of fluid that occurs in fresh mortars exposed to external drying. In addition to the reference mortar with a water to cement ratio (w/c) of 0.30, a mortar with the addition of pre-wetted lightweight aggregates (LWA) and a mortar with a shrinkage reducing admixture (SRA) were tested. The addition of SRA reduced the evaporation rate from the mortar at the initial stages of drying and reduced the total water loss. The pre-wetted LWA released a large part of the absorbed water as a consequence of capillary pressure developing in the fresh mortar due to evaporation.

[1]  Manabu Kanematsu,et al.  QUANTIFICATION OF WATER PENETRATION INTO CONCRETE THROUGH CRACKS BY NEUTRON RADIOGRAPHY , 2009 .

[2]  Pietro Lura,et al.  Impact of admixtures on the plastic shrinkage cracking of self-compacting concrete , 2014 .

[3]  C. Brinker,et al.  Sol-Gel Science: The Physics and Chemistry of Sol-Gel Processing , 1990 .

[4]  Avinash C. Kak,et al.  Principles of computerized tomographic imaging , 2001, Classics in applied mathematics.

[5]  Franz Pfeiffer,et al.  Dark-field X-ray imaging of unsaturated water transport in porous materials , 2014 .

[6]  Anders Kaestner,et al.  Release of internal curing water from lightweight aggregates in cement paste investigated by neutron and X-ray tomography , 2011 .

[7]  Anders Kaestner,et al.  Spatiotemporal computed tomography of dynamic processes , 2011 .

[8]  E. Lehmann,et al.  Methods of scattering corrections for quantitative neutron radiography , 2005 .

[9]  D. Bentz.  Influence of Shrinkage-Reducing Admixtures on Early-Age Properties of Cement Pastes , 2006 .

[10]  B. Weber,et al.  Real-time measurements of temperature, pressure and moisture profiles in High-Performance Concrete exposed to high temperatures during neutron radiography imaging , 2015 .

[11]  R. Hassanein.  Correction methods for the quantitative evaluation of thermal neutron tomography , 2006 .

[12]  D. Gawin,et al.  Modeling of Water Migration during Internal Curing with Superabsorbent Polymers , 2012 .

[13]  Tommy Nantung,et al.  Water absorption in internally cured mortar made with water-filled lightweight aggregate , 2009 .

[14]  Tommy Nantung,et al.  Plastic Shrinkage Cracking in Internally Cured Mixtures , 2010 .

[15]  P. Vontobel,et al.  PROPERTIES OF THE RADIOGRAPHY FACILITY NEUTRA AT SINQ AND ITS POTENTIAL FOR USE AS EUROPEAN REFERENCE FACILITY , 2001 .

[16]  Jan Olek,et al.  Mechanism of plastic shrinkage cracking in portland cement and portland cement-silica fume paste and mortar , 1990 .

[17]  D. Bentz,et al.  Shrinkage-reducing admixtures and early-age desiccation in cement pastes and mortars , 2001 .

[18]  J. Olek,et al.  Characterization of plastic shrinkage cracking in fiber reinforced concrete using image analysis and a modified Weibull function , 2003 .

[19]  B Münch,et al.  Focussed ion beam nanotomography reveals the 3D morphology of different solid phases in hardened cement pastes , 2011, Journal of microscopy.

[20]  H. Justnes,et al.  Discussion: Neutron radiography: an excellent method of measuring water penetration and moisture distribution in cementitious materials , 1994 .

[21]  N. Kardjilov,et al.  Scattering correction algorithm for neutron radiography and tomography tested at facilities with different beam characteristics , 2006 .

[22]  Pietro Lura,et al.  Evaporation, settlement, temperature evolution, and development of plastic shrinkage cracks in mortars with shrinkage-reducing admixtures , 2006 .

[23]  L. Pel,et al.  Fire spalling of concrete as studied by NMR, model validation , 2012 .

[24]  Gaurav Sant,et al.  Interactions between shrinkage reducing admixtures (SRA) and cement paste's pore solution , 2008 .

[25]  F. H. Wittmann,et al.  On the action of capillary pressure in fresh concrete , 1976 .

[26]  Pietro Lura,et al.  Internal curing with lightweight aggregate produced from biomass-derived waste , 2014 .

[27]  F. Wittmann,et al.  Determination of moisture distributions in porous building materials by neutron transmission analysis , 1998 .

[28]  A. Grader,et al.  Four-Dimensional X-Ray Microtomography Study of Water Movement During Internal Curing | NIST , 2006 .

[29]  Tommy Nantung,et al.  Volume change and cracking in internally cured mixtures made with saturated lightweight aggregate under sealed and unsealed conditions , 2009 .

[30]  N. Kardjilov,et al.  Hydrogen distribution measurements by neutrons. , 2004, Applied radiation and isotopes : including data, instrumentation and methods for use in agriculture, industry and medicine.

[31]  D.M. Mount,et al.  An Efficient k-Means Clustering Algorithm: Analysis and Implementation , 2002, IEEE Trans. Pattern Anal. Mach. Intell..

[32]  T. Noguchi,et al.  Evaluation of water transfer from saturated lightweight aggregate to cement paste matrix by neutron radiography , 2009 .

[33]  Pietro Lura,et al.  Influence of Shrinkage-Reducing Admixtures on Development of Plastic Shrinkage Cracks , 2007 .

[34]  S. Ross,et al.  Power laws for image quality measures in PET penalized-likelihood image reconstruction , 2013, 2013 IEEE Nuclear Science Symposium and Medical Imaging Conference (2013 NSS/MIC).

[35]  Nemkumar Banthia,et al.  Influence of Polypropylene Fiber Geometry on Plastic Shrinkage Cracking in Concrete , 2006 .

[36]  Mohammad Shekarchi,et al.  An investigation on the use of zeolite aggregates for internal curing of concrete , 2013 .

[37]  J. Carmeliet,et al.  Visualization and quantification of liquid water transport in softwood by means of neutron radiography , 2012 .

[38]  Pietro Lura,et al.  Performance of Shrinkage-Reducing Admixtures at Different Humidities and at Early Ages , 2008 .

[39]  H. Henriksson,et al.  Nuclear data activities at the NEA Data Bank , 2007 .

[40]  Rachid Deriche,et al.  Vector-valued image regularization with PDEs: a common framework for different applications , 2005, IEEE Transactions on Pattern Analysis and Machine Intelligence.

[41]  Michael Golias,et al.  Absorption and desorption properties of fine lightweight aggregate for application to internally cured concrete mixtures , 2011 .