The effect of the glass transition temperature on the toughness of photopolymerizable (meth)acrylate networks under physiological conditions.

The purpose of this study is to evaluate how the toughness of photopolymerizable (meth)acrylate networks is influenced by physiological conditions. By utilizing two ternary (meth)acrylate networks, MA-co-MMA-co-PEGDMA and 2HEMA-co-BMA-co-PEGDMA, relationships between glass transition temperature (T(g)), water content and state, and toughness were studied by varying the weight ratio of the linear monomers (MA to MMA or 2HEMA to BMA). Differential scanning calorimetry and thermogravimetric analysis were performed to evaluate the thermal behavior and water content as a function of either MA or 2HEMA concentration while tensile strain-to-failure tests were performed at 37°C to determine network toughness. Both networks exhibited a maximum in toughness in PBS in the composition corresponding to a T(g) close to the testing temperature. This toughness maximum was achieved by adjusting the glass transition temperature and/or hydrophilicity through changes in chemistry. These relationships may be utilized to design tough photopolymerizable networks for use in mechanically rigorous biomedical applications.

[1]  Jeffrey A. Hubbell,et al.  Photopolymerized hydrogel materials for drug delivery applications , 1995 .

[2]  T. Hatakeyama,et al.  Effect of Bound Water on Tensile Properties of Native Cellulose , 1983 .

[3]  T. L. Smith.  Deformation and failure of plastics and elastomers , 1965 .

[4]  H. Kusanagi,et al.  Fourier transform infra-red spectroscopic studies of water molecules sorbed in solid polymers , 1994 .

[5]  Robin Shandas,et al.  Unconstrained recovery characterization of shape-memory polymer networks for cardiovascular applications. , 2007, Biomaterials.

[6]  D. Mooney,et al.  Independent Control of Rigidity and Toughness of Polymeric Hydrogels , 2003 .

[7]  E. Franses,et al.  FTIR ATR analysis for microstructure and water uptake in poly(methyl methacrylate) spin cast and Langmuir-Blodgett thin films , 1994 .

[8]  M. M. Pradas,et al.  Thermal transitions of poly(N-isopropylmethacrylamide) in aqueous solutions , 2004 .

[9]  N. Peppas,et al.  Dynamic mechanical properties of polymer-fluid systems : characterization of poly(2-hydroxyethyl methacrylate) and poly(2-hydroxyethyl methacrylate-co-methyl methacrylate) hydrogels , 1991 .

[10]  Miguel F. Refojo,et al.  Hydrogels from 2‐hydroxyethyl methacrylate and propylene glycol monoacrylate , 1965 .

[11]  T. Hatakeyama,et al.  Relationship between hydrogen bonding and bound water in polyhydroxystyrene derivatives , 1983 .

[12]  Yingjun Wang,et al.  INFLUENCE OF WATER STATES IN HYDROGELS ON THE TRANSMISSIBILITY AND PERMEABILITY OF OXYGEN IN CONTACT LENS MATERIALS , 2008 .

[13]  J. G. Ribelles,et al.  Interaction between water and polymer chains in poly(hydroxyethyl acrylate) hydrogels , 2001 .

[14]  Wei Min Huang,et al.  On the effects of moisture in a polyurethane shape memory polymer , 2004 .

[15]  Won-Gun Koh,et al.  Biomimetic strain hardening in interpenetrating polymer network hydrogels , 2007 .

[16]  P. McCarron,et al.  Investigation of swelling and network parameters of poly(ethylene glycol)-crosslinked poly(methyl vinyl ether-co-maleic acid) hydrogels , 2009 .

[17]  R. Kusy,et al.  Mechanical properties and interrelationships of poly(methyl methacrylate) following hydration over saturated salts , 2001 .

[18]  James S. Taylor,et al.  Ideal copolymers and the second‐order transitions of synthetic rubbers. i. non‐crystalline copolymers , 2007 .

[19]  H. Hatakeyama,et al.  Determination of bound water content in polymers by DTA, DSC and TG , 1988 .

[20]  Chłopek Jan,et al.  The study of lifetime of polymer and composite bone joint screws under cyclical loads and in vitro conditions , 2005, Journal of materials science. Materials in medicine.

[21]  Yiping Liu,et al.  Thermomechanics of the shape memory effect in polymers for biomedical applications. , 2005, Journal of biomedical materials research. Part A.

[22]  J. Drummond,et al.  Degradation, Fatigue, and Failure of Resin Dental Composite Materials , 2008, Journal of dental research.

[23]  B. Tighe,et al.  Synthetic hydrogels: 3. Hydroxyalkyl acrylate and methacrylate copolymers: surface and mechanical properties , 1988 .

[24]  A.M.S. Hamouda,et al.  The influence of humidity on the deformation and fracture behaviour of PMMA , 2002 .

[25]  G. P. Johari,et al.  Glass-liquid transition of water and ethylene glycol solution in poly(2-hydroxyethyl methacrylate) hydrogel , 1990 .

[26]  F. E. Karasz,et al.  A Classical Thermodynamic Discussion of the Effect of Composition on Glass-Transition Temperatures , 1978 .

[27]  Wei Min Huang,et al.  Effects of moisture on the thermomechanical properties of a polyurethane shape memory polymer , 2006 .

[28]  Ken Gall,et al.  Effect of chemical structure and crosslinking density on the thermo-mechanical properties and toughness of (meth)acrylate shape-memory polymer networks , 2008 .

[29]  K. Gall,et al.  On the toughness of photopolymerizable (meth)acrylate networks for biomedical applications , 2009 .

[30]  Yoshimi Tanaka,et al.  Novel hydrogels with excellent mechanical performance , 2005 .

[31]  D. G. Smith,et al.  33. Solvent-modified polymer networks. Part I. The preparation and characterisation of expanded-network and macroporous styrene–divinylbenzene copolymers and their sulphonates , 1963 .

[32]  W McIntosh,et al.  Transdermal photopolymerization for minimally invasive implantation. , 1999, Proceedings of the National Academy of Sciences of the United States of America.

[33]  J. Rault,et al.  Thermal Transitions in Hydrogels of Poly(ethyl acrylate)/Poly(hydroxyethyl acrylate) Interpenetrating Networks , 1997 .

[34]  Jianliang Xiao,et al.  Hydrogel–hydrogel composites: The interfacial structure and interaction between water and polymer chains , 2008 .

[35]  M. M. Pradas,et al.  Influence of the Hydrophobic Phase on the Thermal Transitions of Water Sorbed in a Polymer Hydrogel Based on Interpenetration of a Hydrophilic and a Hydrophobic Network , 2003 .

[36]  Rodolfo Pinal,et al.  Entropy of Mixing and the Glass Transition of Amorphous Mixtures , 2008, Entropy.

[37]  W. Hayes,et al.  The Effects of Donor Age and Strain Rate on the Biomechanical Properties of Bone-Patellar Tendon-Bone Allografts , 1994, The American journal of sports medicine.

[38]  F. Selmin,et al.  Plasticizing effect of water on poly(lactide-co-glycolide). , 2005, Journal of controlled release : official journal of the Controlled Release Society.

[39]  B. Tighe,et al.  Synthetic hydrogels: 1. Hydroxyalkyl acrylate and methacrylate copolymers - water binding studies , 1987 .

[40]  Alicia M. Ortega,et al.  Strong, Tailored, Biocompatible Shape‐Memory Polymer Networks , 2008, Advanced functional materials.

[41]  M. Rahman,et al.  Measurement of glass transition temperature by mechanical (DMTA), thermal (DSC and MDSC), water diffusion and density methods: A comparison study , 2007 .