Thermo-responsive copolymers with ionic group as novel draw solutes for forward osmosis processes

Thermo-responsive copolymers containing ionic groups (P(MTxEOy), where x and y are the feed molar percent of [2-(methacryloyloxy)ethyl]trimethylammonium chloride (MTAC) and 2-(2-methoxyethoxy)ethyl methacrylate (MEO), respectively) were synthesized via free radical polymerization using MTAC and MEO as monomers, in order to use the copolymers as a draw solute in a forward osmosis (FO) system. The osmotic pressure and lower critical solution temperature (LCST) could be controlled by changing the composition of the copolymers. For example, P(MT25EO75) shows a relatively high osmotic pressure of 0.909 Osmol/kg at 0.2 g/mL, and P(MT5EO95) shows a LCST close to room temperature at 32 °C. When P(MT20EO80) was used as a draw solute in the FO system, a reasonable water permeation flux value of 5.45 Lm−2h−1 at 0.1 g/mL was observed and the draw solute (P(MT20EO80)) could be recovered with a very large draw solute recovery value of 99.80% from the draw solutions by heating to 70 °C, above the LCST, followed by a microfiltration process. Therefore, it is expected that such copolymer system could be a prospective candidate as a draw solute in the FO system.

[1]  Tzahi Y. Cath,et al.  Selection of inorganic-based draw solutions for forward osmosis applications , 2010 .

[2]  Sidney Loeb,et al.  One hundred and thirty benign and renewable megawatts from Great Salt lake? The possibilities of hydroelectric power by pressure-retarded osmosis , 2001 .

[3]  Sherub Phuntsho,et al.  A novel low energy fertilizer driven forward osmosis desalination for direct fertigation: Evaluating , 2011 .

[4]  Mark L. Stone,et al.  SWITCHABLE POLARITY SOLVENTS AS DRAW SOLUTES FOR FORWARD OSMOSIS , 2013 .

[5]  Jong‐Chan Lee,et al.  Dual effective organic/inorganic hybrid star-shaped polymer coatings on ultrafiltration membrane for bio- and oil-fouling resistance. , 2012, ACS applied materials & interfaces.

[6]  Raphael Semiat,et al.  Energy issues in desalination processes. , 2008, Environmental science & technology.

[7]  Yufeng Cai,et al.  CO2 switchable dual responsive polymers as draw solutes for forward osmosis desalination. , 2013, Chemical communications.

[8]  Menachem Elimelech,et al.  Energy requirements of ammonia-carbon dioxide forward osmosis desalination , 2007 .

[9]  Tongwen Xu,et al.  Thermo-sensitive polyelectrolytes as draw solutions in forward osmosis process , 2013 .

[10]  Laura Chekli,et al.  A review of draw solutes in forward osmosis process and their use in modern applications , 2012 .

[11]  H. Lazarides,et al.  Osmotic concentration of liquid foods , 2001 .

[12]  Jong‐Chan Lee,et al.  Photo-cross-linkable star-shaped polymers with poly(ethylene glycol) and renewable cardanol side groups: synthesis, characterization, and application to antifouling coatings for filtration membranes , 2013 .

[13]  Joon Ha Kim,et al.  Mathematical model of flat sheet membrane modules for FO process: Plate-and-frame module and spiral- , 2011 .

[14]  Tzahi Y Cath,et al.  Removal of natural steroid hormones from wastewater using membrane contactor processes. , 2006, Environmental science & technology.

[15]  Mark L. Stone,et al.  An initial study of hexavalent phosphazene salts as draw solutes in forward osmosis , 2013 .

[16]  E. Drioli,et al.  Recent advances on membrane processes for the concentration of fruit juices: a review , 2004 .

[17]  Richard E. Kravath,et al.  Desalination of sea water by direct osmosis , 1975 .

[18]  G. Odian,et al.  Principles of polymerization , 1981 .

[19]  C. Cabassud,et al.  Fouling control by air sparging inside hollow fibre membranes—effects on energy consumption , 1998 .

[20]  Ronan K. McGovern,et al.  Quantifying the potential of ultra-permeable membranes for water desalination , 2014 .

[21]  M. Coote,et al.  The mechanism of the propagation step in free-radical copolymerisation , 1999 .

[22]  Qingchun Ge,et al.  Hydroacid complexes: a new class of draw solutes to promote forward osmosis (FO) processes. , 2013, Chemical communications.

[23]  Menachem Elimelech,et al.  A novel ammonia-carbon dioxide forward (direct) osmosis desalination process , 2005 .

[24]  Xue Li,et al.  Emerging forward osmosis (FO) technologies and challenges ahead for clean water and clean energy applications , 2012 .

[25]  Robert L McGinnis,et al.  Desalination by ammonia–carbon dioxide forward osmosis: Influence of draw and feed solution concentrations on process performance , 2006 .

[26]  Xiuyun Sun,et al.  Biological denitrification of high-nitrate wastewater in a modified anoxic/oxic-membrane bioreactor (A/O-MBR). , 2009, Journal of hazardous materials.

[27]  Jong‐Chan Lee,et al.  Poly(1-oxotrimethylene) fibers prepared by different draw ratios for the tire cord application , 2012, Macromolecular Research.

[28]  Y C Kim,et al.  A feasibility study of magnetic separation of magnetic nanoparticle for forward osmosis. , 2011, Water science and technology : a journal of the International Association on Water Pollution Research.

[29]  Allan F. M. Barton,et al.  CRC Handbook of solubility parameters and other cohesion parameters , 1983 .

[30]  Z. Gan,et al.  Thermosensitive block copolymers PEG-b-PBEMAGG containing functional pendant amino groups , 2012, Macromolecular Research.

[31]  Chuyang Y. Tang,et al.  Effect of draw solution concentration and operating conditions on forward osmosis and pressure retarded osmosis performance in a spiral wound module , 2010 .

[32]  D. Brooks,et al.  A Novel Functional Polymer with Tunable LCST , 2008 .

[33]  Ji-Hun Seo,et al.  Novel lower critical solution temperature phase transition materials effectively control osmosis by mild temperature changes. , 2012, Chemical communications.

[34]  Kai Yu Wang,et al.  Study of draw solutes using 2-methylimidazole-based compounds in forward osmosis , 2010 .

[35]  How Yong Ng,et al.  A novel hybrid forward osmosis - nanofiltration (FO-NF) process for seawater desalination: Draw solution selection and system configuration , 2010 .

[36]  How Yong Ng,et al.  Concentration of brine by forward osmosis: Performance and influence of membrane structure , 2008 .

[37]  Ning Zhao,et al.  Multi-membrane hydrogel fabricated by facile dynamic self-assembly , 2009 .

[38]  Sheng Dai,et al.  Thermo- and photo-responsive polymeric systems , 2009 .

[39]  Shiping Zhu,et al.  Chain conformation of a new class of PEG-based thermoresponsive polymer brushes grafted on silicon as determined by neutron reflectometry. , 2009, Langmuir : the ACS journal of surfaces and colloids.

[40]  C. D. Moody,et al.  Forward osmosis extractors , 1976 .

[41]  P. Flory,et al.  Statistical Thermodynamics of Chain Molecule Liquids. II. Liquid Mixtures of Normal Paraffin Hydrocarbons , 1964 .

[42]  Rosemary Norman,et al.  Low grade thermal energy sources and uses from the process industry in the UK , 2012 .

[43]  Jincai Su,et al.  Exploration of polyelectrolytes as draw solutes in forward osmosis processes. , 2012, Water research.

[44]  Amy E. Childress,et al.  Forward osmosis: Principles, applications, and recent developments , 2006 .

[45]  Andrea Achilli,et al.  Organic ionic salt draw solutions for osmotic membrane bioreactors. , 2012, Bioresource technology.

[46]  Dan Li,et al.  Forward osmosis desalination using polymer hydrogels as a draw agent: influence of draw agent, feed solution and membrane on process performance. , 2013, Water research.

[47]  B. Freeman,et al.  Gas and Liquid Separations Using Membranes: An Overview , 2004 .

[48]  Dan Li,et al.  Composite polymer hydrogels as draw agents in forward osmosis and solar dewatering , 2011 .

[49]  R. Lord.  Osmosis, osmometry, and osmoregulation , 1999, Postgraduate medical journal.

[50]  Ming Ming Ling,et al.  Desalination process using super hydrophilic nanoparticles via forward osmosis integrated with ultrafiltration regeneration , 2011 .

[51]  T. Kojima,et al.  Homopolymer and copolymers of 4-nitro-3-methylphenyl methacrylate with glycidyl methacrylate : Synthesis, characterization, monomer reactivity ratios and thermal properties , 2007 .

[52]  Jong‐Chan Lee,et al.  The increase of antifouling properties of ultrafiltration membrane coated by star-shaped polymers , 2012 .

[53]  Yu Chen,et al.  Synthesis of thermoresponsive hyperbranched polyamidoamine and the molecular weight, pH, and anion sensitive thermoresponsive properties thereof , 2012, Macromolecular Research.

[54]  Ming Ming Ling,et al.  Facile synthesis of thermosensitive magnetic nanoparticles as "smart" draw solutes in forward osmosis. , 2011, Chemical communications.

[55]  Tai‐Shung Chung,et al.  Draw solutions for forward osmosis processes: Developments, challenges, and prospects for the future , 2013 .

[56]  J. Sokoloff,et al.  Comparison of the kinetic friction of planar neutral and polyelectrolyte polymer brushes using molecular dynamics simulations. , 2011, Physical review. E, Statistical, nonlinear, and soft matter physics.

[57]  Kai Yu Wang,et al.  Highly Water-Soluble Magnetic Nanoparticles as Novel Draw Solutes in Forward Osmosis for Water Reuse , 2010 .

[58]  N. Rastogi,et al.  Influence of concentration polarization on flux behavior in forward osmosis during desalination using ammonium bicarbonate , 2013 .

[59]  Ruixue Liu,et al.  Thermoresponsive copolymers: from fundamental studies to applications , 2009 .

[60]  Ken Rainwater,et al.  Energy analysis and efficiency assessment of reverse osmosis desalination process , 2011 .

[61]  U. Schubert,et al.  Temperature responsive bio-compatible polymers based on poly(ethylene oxide) and poly(2-oxazoline)s , 2012 .

[62]  J. Georgiadis,et al.  Science and technology for water purification in the coming decades , 2008, Nature.

[63]  Dan Li,et al.  Stimuli-responsive polymer hydrogels as a new class of draw agent for forward osmosis desalination. , 2011, Chemical communications.