An Investigation on Adding Polypropylene Fibers to Reinforce Lightweight Cement Composites (LWC)

The influence of polypropylene fibers has been studied in different proportioning and fiber length to improve the performance characteristics of the lightweight cement composites. Fibers used in two different lengths (6mm and 12mm) and fiber proportions (0.15% and 0.35%) by cement weight in the mixture design. Hardened concrete properties such as: 7- and 28-day compressive strength, splitting tensile strength, flexural strength, water absorption, and shrinkage were evaluated. Fiber addition was seen to enhance the physical and mechanical properties of lightweight concrete. Compared to unreinforced LWC, polypropylene (PP) reinforced LWC with fiber proportioning 0.35% and 12 mm fiber length, caused 30.1% increase in the flexural strength and 27% increase in the splitting tensile strength. Increased fiber availability in the LWC matrix, in addition to the ability of longer PP fibers to bridge on the micro cracks, are suggested as the reasons for the enhancement in mechanical properties.

[1]  B. Sheu,et al.  Strength properties of nylon- and polypropylene-fiber-reinforced concretes , 2005 .

[2]  M. Latifi,et al.  Performance of fibers embedded in a cementitious matrix , 2009 .

[3]  Vesa Penttala,et al.  Drying of lightweight concrete produced from crushed expanded clay aggregates , 1996 .

[4]  Surendra P. Shah,et al.  Fiber reinforced concrete : developments and innovations , 1994 .

[5]  Jack Zeng,et al.  PROPERTIES OF POLYPROPYLENE FIBER REINFORCED CONCRETE , 1993 .

[6]  S. Martínez-Ramírez,et al.  Microstructure studies on Portland cement pastes obtained in highly alkaline environments , 2001 .

[7]  A. Leung,et al.  Influence of steel fibres on strength and ductility of normal and lightweight high strength concrete , 2002 .

[8]  B. P. Hughes,et al.  Improving the toughness of high strength cement paste with fibre reinforcement , 1976 .

[9]  Parviz Soroushian,et al.  Mechanical properties of hybrid fiber reinforced lightweight aggregate concrete made with natural pumice , 2011 .

[10]  Harun Tanyildizi.  Statistical analysis for mechanical properties of polypropylene fiber reinforced lightweight concrete containing silica fume exposed to high temperature , 2009 .

[11]  Erika Holt,et al.  Cracking risks associated with early age shrinkage , 2004 .

[12]  P. Balaguru,et al.  Test Methods for Durability of Polymeric Fibers in Concrete and UV Light Exposure , 1995, SP-155: Testing of Fiber Reinforced Concrete.

[13]  Weiguo Shen,et al.  Influences of polypropylene fiber and SBR polymer latex on abrasion resistance of cement mortar , 2010 .

[14]  Wei Sun,et al.  Mechanical properties of steel fiber-reinforced, high-strength, lightweight concrete , 1997 .

[15]  Parviz Soroushian,et al.  Mechanical properties of polypropylene fiber reinforced concrete and the effects of pozzolanic materials , 1996 .

[16]  A. Bentur,et al.  Effect of lightweight fly ash aggregate microstructure on the strength of concretes , 1997 .

[17]  N. Berke,et al.  Effect of Low Addition Rates of Polypropylene Fibers on Plastic Shrinkage Cracking and Mechanical Properties of Concrete , 1994, SP-142: Fiber Reinforced Concrete Developments and Innovations.

[18]  M. E. Karaguler,et al.  Comparison of Shrinkage Cracking Performance of Different Types of Fibers and Wiremesh , 1994 .

[19]  Obada Kayali,et al.  Some characteristics of high strength fiber reinforced lightweight aggregate concrete , 2003 .

[20]  Wei Chen,et al.  Alkali binding in hydrated Portland cement paste , 2010 .

[21]  B. Mobasher,et al.  Mechanical properties of fiber reinforced lightweight concrete composites , 1994 .

[22]  S. Mindess,et al.  Properties of concrete reinforced with fibrillated polypropylene fibres under impact loading , 1988 .

[23]  R. F. Zollo.  Fiber-reinforced concrete: An overview after 30 years of development , 1997 .

[24]  Bing Chen,et al.  Contribution Of Hybrid Fibers On The Properties Of The High-Strength Lightweight Concrete Having Good Workability , 2005 .

[25]  P. Soroushian,et al.  Optimization of the Use of Lightweight Aggregates in Carbon Fiber Reinforced Cement , 1992 .

[26]  Michel Pigeon,et al.  Restrained Shrinkage Tests on Fiber Reinforced Cementitious Composites , 1995 .

[27]  A. Richardson.  Compressive strength of concrete with polypropylene fibre additions , 2006 .

[28]  Antoine E. Naaman,et al.  Comparative flexural behavior of four fiber reinforced cementitious composites , 2008 .

[29]  M. Latifi,et al.  Utilizing polypropylene fibers to improve physical and mechanical properties of concrete , 2012 .