Indentation Crack‐Shape Evolution during Subcritical Crack Growth

Indentation crack-shape evolution during subcritical crack growth was examined in soda-lime glass. Crack-arrest markings were generated on the fracture surfaces by temporary unloading during subcritical crack growth. Crack shapes were determined from these crack-arrest markings by optical microscopy. The shapes were found to be semi-elliptical, but the ellipticity changed significantly with crack extension under an applied bending stress. Crack-shape evolution was predicted by using the stress intensity factor equation for a semi-elliptical crack for the applied stress distribution and the subcritical crack growth parameters for the material/environment system. Experimental results were found to be in excellent agreement with the predictions. The influence of the initial crack size and shape, the loading configuration, and the subcritical crack growth exponent it on crack-shape evolution was also investigated in the simulations. It was found that, for the particular loading configuration and material, there is an equilibrium shape associated with the subcritically growing crack. The variation in crack shape with its extension during subcritical crack growth was found to be an important factor in lifetime prediction.

[1]  Hiroyuki Abe,et al.  Effect of Humidity on Small‐Crack Growth in Silica Optical Fibers , 1993 .

[2]  D. J. Green,et al.  Determination of Subcritical Crack Growth Parameters by In Situ Observation of Indentation Cracks , 1995 .

[3]  R. Scattergood,et al.  Crack-shape effects for indentation fracture toughness measurements , 1992 .

[4]  R. Matsumoto.  Evaluation of Fracture Toughness Determination Methods as Applied to Ceria‐Stabilized Tetragonal Zirconia Polycrystal , 1987 .

[5]  Sheldon M. Wiederhorn,et al.  Subcritical Crack Growth in Ceramics , 1974 .

[6]  Michael V. Swain,et al.  Microfracture beneath point indentations in brittle solids , 1975 .

[7]  J. Lankford.  Threshold microfracture during elastic-plastic indentation of ceramics , 1980 .

[8]  J. Sullivan,et al.  Shape profiles of cracks formed under a Vickers pyramid indenter , 1986 .

[9]  A. Rosenfield,et al.  Indenter flaw geometry and fracture toughness estimates for a glass-ceramic , 1985 .

[10]  Subcritical Growth of Indentation Median Cracks in Soda‐Lime‐Silica Glass , 1995 .

[11]  J. Nadeau.  Influence of Hydrogen and Alkali Impurities on the High‐Temperature Indentation Hardness of Natural Quartz Crystals , 1970 .

[12]  M. Yoda.  Subcritical crack growth of glass , 1987 .

[13]  J. Petrovic,et al.  Slow Crack Growth from Controlled Surface Flaws in Hot-Pressed Si3N4 , 1978 .

[14]  H. Matzke,et al.  Hertzian crack growth in ThO2 observed by serial sectioning , 1982 .

[15]  T. Yoko,et al.  Mixed Alkali Effect in Noncoventional Alkali Gallotitanate Glasses , 1993 .

[16]  Brian R. Lawn,et al.  Residual stress effects in sharp contact cracking , 1979 .

[17]  James C. Newman,et al.  An empirical stress-intensity factor equation for the surface crack , 1981 .

[18]  V. Fréchette,et al.  Effects of Electric Fields on Slow Crack Growth in Glass , 1990 .

[19]  Brian R. Lawn,et al.  Relation between multiregion crack growth and dynamic fatigue of glass using indentation flaws , 1983 .

[20]  Crack evolution in Vickers indentation for soda-lime-silica glass , 1982 .

[21]  V. Fréchette,et al.  Experimental Observation of Crack Velocity and Crack Front Shape Effects in Double-Torsion Fracture Mechanics Tests , 1981 .