A micromechanics-based finite element model for compressive failure of notched uniply composite

A micromechanics based failure initiation predictive capability for analyzing notched composite laminates loaded remotely in multiaxial compression is reported. The model relies on the results from a previous experimental study that investigated compression failure mechanisms in special uniply composite laminates. The finite element method (FEM) was used in the solution process. The experimental results showed that the dominant mode of failure initiation was kink banding near the hole edge. The kink band was confined in extent to a distance within one half of the hole radius. The fibers within the kind band were rotated both in plane and out of the plane of the laminate. The position of the kink band with respect to the center of the notch depended on the remote biaxial load ratio. In the FEM, the region in which kink banding takes place is contained within a finite size rectangular area, and is meshed as an alternatingly stacked region of fiber and matrix layers. The values of boundary loads on this rectangular area which correspond to kink banding is related to the remotely applied loads via an available form analysis for orthotropic laminates. Good agreement is found between experiment and analysis for a wide range ofmore » notch sizes.« less

[1]  A. M. Waas,et al.  An experimental study of compression failure of fibrous laminated composites in the presence of stress gradients , 1990 .

[2]  R. Gibson.  Principles of Composite Material Mechanics , 1994 .

[3]  Paul A. Lagace,et al.  Notch sensitivity of graphite/epoxy fabric laminates , 1986 .

[4]  Constantinos Soutis,et al.  Influence of shear properties and fibre imperfections on the compressive behaviour of GFRP laminates , 1996 .

[5]  J. Whitney,et al.  Stress Fracture Criteria for Laminated Composites Containing Stress Concentrations , 1974 .

[6]  Anthony M. Waas,et al.  Compressive failure of composites, part II: Experimental studies , 1996 .

[7]  Anthony M. Waas,et al.  Failure Mechanisms of Uni-Ply Composite Plates With a Circular Hole Under Static Compressive Loading , 1992 .

[8]  C. Sun,et al.  Effect of Ply Thickness on Fracture of Notched Composite Laminates , 1998 .

[9]  Fu-Kuo Chang,et al.  Damage Tolerance of Laminated Composites Containing an Open Hole and Subjected to Compressive Loadings: Part I—Analysis , 1991 .

[10]  E. Riks.  The Application of Newton's Method to the Problem of Elastic Stability , 1972 .

[11]  A. Waas,et al.  Failure Mechanisms of Composite Plates With a Circular Hole Under Remote Biaxial Planar Compressive Loads , 1997 .

[12]  Norman A. Fleck,et al.  Compressive failure of notched carbon fibre composites , 1993, Proceedings of the Royal Society of London. Series A: Mathematical and Physical Sciences.

[13]  Norman A. Fleck,et al.  Compressive failure of fibre composites , 1993 .

[14]  Stelios Kyriakides,et al.  On the compressive failure of fiber reinforced composites , 1995 .

[15]  Som R. Soni,et al.  Failure Analysis of Composite Laminates with a Fastener Hole. , 1981 .

[16]  Constantinos Soutis,et al.  A Property Degradation Model for Fibre Microbuckling Failure in Composite Laminates , 1995 .

[17]  James H. Starnes,et al.  Effect of Impact Damage and Holes on the Compressive Strength of a Graphite/Epoxy Laminate , 1979 .

[18]  Constantinos Soutis,et al.  Strength prediction of CFRP plates with a hole under biaxial compression-tension , 1998 .

[19]  N. Takeda,et al.  Notched Strength and Fracture Criterion in Fabric Composite Plates Containing a Circular Hole , 1995 .

[20]  Norman A. Fleck,et al.  Static Compression Failure of Carbon Fibre T800/924C Composite Plate with a Single Hole , 1990 .

[21]  E. V. Iarve,et al.  Three-dimensional stress analysis in laminated composites with fasteners based on the B-spline approximation , 1997 .

[22]  Norman A. Fleck,et al.  Failure Prediction Technique for Compression Loaded Carbon Fibre-Epoxy Laminate with Open Holes , 1991 .