Shellac Films as a Natural Dielectric Layer for Enhanced Electron Transport in Polymer Field-Effect Transistors.

Shellac, a natural polymer resin obtained from the secretions of lac bugs, was evaluated as a dielectric layer in organic field-effect transistors (OFETs) on the basis of donor (D)-acceptor (A)-type conjugated semiconducting copolymers. The measured dielectric constant and breakdown field of the shellac layer were ∼3.4 and 3.0 MV/cm, respectively, comparable with those of a poly(4-vinylphenol) (PVP) film, a commonly used dielectric material. Bottom-gate/top-contact OFETs were fabricated with shellac or PVP as the dielectric layer and one of three different D-A-type semiconducting copolymers as the active layer: poly(cyclopentadithiophene- alt-benzothiadiazole) with p-type characteristics, poly(naphthalene-bis(dicarboximide)- alt-bithiophene) [P(NDI2OD-T2)] with n-type characteristics, and poly(dithienyl-diketopyrrolopyrrole- alt-thienothiophene) [P(DPP2T-TT)] with ambipolar characteristics. The electrical characteristics of the fabricated OFETs were then measured. For all active layers, OFETs with a shellac film as the dielectric layer exhibited a better mobility than those with PVP. For example, the mobility of the OFET with a shellac dielectric and n-type P(NDI2OD-T2) active layer was approximately 2 orders of magnitude greater than that of the corresponding OFET with a PVP insulating layer. When P(DPP2T-TT) served as the active layer, the OFET with shellac as the dielectric exhibited ambipolar characteristics, whereas the corresponding OFET with the PVP dielectric operated only in hole-accumulation mode. The total density of states was analyzed using technology computer-aided design simulations. The results revealed that compared with the OFETs with PVP as the dielectric, the OFETs with shellac as the dielectric had a lower trap-site density at the polymer semiconductor/dielectric interface and much fewer acceptor-like trap sites acting as electron traps. These results demonstrate that shellac is a suitable dielectric material for D-A-type semiconducting copolymer-based OFETs, and the use of shellac as a dielectric layer facilitates electron transport at the interface with D-A-type copolymer channels.

[1]  Tobin J Marks,et al.  Gate dielectric chemical structure-organic field-effect transistor performance correlations for electron, hole, and ambipolar organic semiconductors. , 2006, Journal of the American Chemical Society.

[2]  H. Sirringhaus.  25th Anniversary Article: Organic Field-Effect Transistors: The Path Beyond Amorphous Silicon , 2014, Advanced materials.

[3]  C. Lee,et al.  Thermally curable organic/inorganic hybrid polymers as gate dielectrics for organic thin‐film transistors , 2014 .

[4]  S. K. Sharma,et al.  Shellac-Structure, Characteristics & Modification , 1983 .

[5]  Mihai Irimia-Vladu,et al.  Green and biodegradable electronics , 2012 .

[6]  Jaehyeong Kim,et al.  Extraction of the sub-bandgap density-of-states in polymer thin-film transistors with the multi-frequency capacitance-voltage spectroscopy , 2012 .

[7]  R. Street.  Thin‐Film Transistors , 2009 .

[8]  Juhwan Kim,et al.  Simple Bar‐Coating Process for Large‐Area, High‐Performance Organic Field‐Effect Transistors and Ambipolar Complementary Integrated Circuits , 2013, Advanced materials.

[9]  Jihoon Park,et al.  Flexible semitransparent pentacene thin-film transistors with polymer dielectric layers and NiOx electrodes , 2005 .

[10]  Yong-Young Noh,et al.  Toward Printed Integrated Circuits based on Unipolar or Ambipolar Polymer Semiconductors , 2013, Advanced materials.

[11]  Jae Eun Jang,et al.  Reliable and Uniform Thin‐Film Transistor Arrays Based on Inkjet‐Printed Polymer Semiconductors for Full Color Reflective Displays , 2013, Advanced materials.

[12]  Tobin J. Marks,et al.  Gate Dielectrics for Organic Field‐Effect Transistors: New Opportunities for Organic Electronics , 2005 .

[13]  D. K. Owens,et al.  Estimation of the surface free energy of polymers , 1969 .

[14]  Noam Rappaport,et al.  Charge Transport in Disordered Organic Materials and Its Relevance to Thin‐Film Devices: A Tutorial Review , 2009 .

[15]  Ute Zschieschang,et al.  Polymer Gate Dielectrics and Conducting-Polymer Contactsfor High-Performance Organic Thin-Film Transistors , 2002 .

[16]  Peter Stallinga,et al.  Electrical Characterization of Organic Electronic Materials and Devices , 2009 .

[17]  S. Bauer,et al.  Environmentally sustainable organic field effect transistors , 2010 .

[18]  Janos Veres,et al.  Low‐k Insulators as the Choice of Dielectrics in Organic Field‐Effect Transistors , 2003 .

[19]  Gilles Horowitz,et al.  High‐Performance Ambipolar Pentacene Organic Field‐Effect Transistors on Poly(vinyl alcohol) Organic Gate Dielectric , 2005 .

[20]  N. S. Sariciftci,et al.  Organic inverter circuits employing ambipolar pentacene field-effect transistors , 2006 .

[21]  Jiyoul Lee,et al.  Effect of Donor Building Blocks on the Charge-Transfer Characteristics of Diketopyrrolopyrrole-Based Donor-Acceptor-Type Semiconducting Copolymers. , 2017, ACS applied materials & interfaces.

[22]  T. Wen,et al.  The polymer gate dielectrics and source-drain electrodes on n-type pentacene-based organic field-effect transistors , 2010 .

[23]  Henning Sirringhaus,et al.  Device Physics of Solution‐Processed Organic Field‐Effect Transistors , 2005 .

[24]  Richard H. Friend,et al.  General observation of n-type field-effect behaviour in organic semiconductors , 2005, Nature.

[25]  Jong Won Chung,et al.  Influence of Dielectric Layers on Charge Transport through Diketopyrrolopyrrole-Containing Polymer Films: Dielectric Polarizability vs Capacitance. , 2016, ACS applied materials & interfaces.

[26]  J. Hwang,et al.  Flexible Organic Thin‐Film Transistors with Silk Fibroin as the Gate Dielectric , 2011, Advanced materials.

[27]  Takao Someya,et al.  The rise of plastic bioelectronics , 2016, Nature.

[28]  George G. Malliaras,et al.  The Rise of Organic Bioelectronics , 2014 .

[29]  A. Facchetti,et al.  A high-mobility electron-transporting polymer for printed transistors , 2009, Nature.

[30]  Gui Yu,et al.  A stable solution-processed polymer semiconductor with record high-mobility for printed transistors , 2012, Scientific Reports.

[31]  Mihai Irimia-Vladu,et al.  Natural resin shellac as a substrate and a dielectric layer for organic field-effect transistors , 2013 .

[32]  T. Hua,et al.  Flexible Organic Electronics in Biology: Materials and Devices , 2015, Advanced materials.

[33]  Tzung-Fang Guo,et al.  Chicken Albumen Dielectrics in Organic Field‐Effect Transistors , 2011, Advanced materials.

[34]  Eugenio Cantatore,et al.  Applications of Organic and Printed Electronics , 2013 .

[35]  Gregory L. Whiting,et al.  From Printed Transistors to Printed Smart Systems , 2015, Proceedings of the IEEE.

[36]  K. Müllen,et al.  Field-effect transistors based on a benzothiadiazole-cyclopentadithiophene copolymer. , 2007, Journal of the American Chemical Society.