论文信息 - Fused Line Study of 17-4PH Stainless Steel Deposited with Co-Based Alloy

Fused Line Study of 17-4PH Stainless Steel Deposited with Co-Based Alloy

To improve the surface performance, precipitation hardening martensitic stainless steel 17-4PH is deposited with Co-based alloy stellite12 by plasma-transferred arc welding (PTAW). The microstructure and microhardness of the fused line between base metal and coating were characterized by optical microscope (OM), scanning electron microscope (SEM), transmission electron microscope (TEM) and hardness tester. The results show that the interface between weld coating and base metal is favorable without pore and crack. The microstructure of the fused line is composed of martensite and austenite, without precipitates. [doi:10.2320/matertrans.M2013243]

D. Deng | Rui-Bin Chen | Xiaona Li | Houyong Xia

[1] A. Davoodi,et al. Galvanic corrosion of gas tungsten arc repair welds in 17-4PH stainless steel in 3·5% NaCl solution , 2011 .

[2] M. Shamanian,et al. Microstructure and wear behavior of stellite 6 cladding on 17-4 PH stainless steel , 2011 .

[3] M. Shamanian,et al. Enhancement of wear resistance of ductile iron surface alloyed by stellite 6 , 2011 .

[4] H. Abreu,et al. Microstructure and intergranular corrosion resistance of UNS S17400 (17-4PH) stainless steel , 2010 .

[5] H. Deng,et al. Influence of coating thickness and temperature on mechanical properties of steel deposited with Co-based alloy hardfacing coating , 2010 .

[6] A. Najafizadeh,et al. Aging kinetics of 17-4 PH stainless steel , 2009 .

[7] Qunli Zhang,et al. Surface laser alloying of 17-4PH stainless steel steam turbine blades , 2008 .

[8] Laura M. Cosgriff,et al. Mechanical Properties of 17-4PH Stainless Steel Foam Panels , 2007 .

[9] Jun Wang,et al. The effect of microstructural evolution on hardening behavior of type 17-4PH stainless steel in long-term aging at 350 °C , 2006 .

[10] D. Kalish,et al. The strength, fracture toughness, and low cycle fatigue behavior of 17-4 PH stainless steel , 1974, Metallurgical and Materials Transactions B.