The size dependence of structural stability in nano-sized ZrO2 particles

Abstract The stable or metastable phase was found to be dependent on the size of ZrO 2 nano particles. Amorphous hydrated ZrO 2 powders prepared by precipitation were annealed at 1300 °C and maintained for different length of time followed by being quenched in ambient. The average particle size and phases were determined by X-ray diffraction cross-checked by transmission electron microscopy. The powders were found composed of monoclinic (m) phase when the particle size ( d ) is larger than 31 nm, whereas tetragonal (t) phase remains stable at room temperature when particle size is less than 14 nm. The mixture of the t and m phases is observed when average particle size locates between 14 and 31 nm. Thermodynamic calculation indicates that the surface free energy difference between tetragonal and monoclinic phases surpasses the volume chemical free energy difference between two phases at room temperature when the particle size of zirconia decreases below 13 nm. The lower surface energy of tetragonal phase results in the stability of tetragonal structure at room temperature, while tetragonal phase is normally stable at high temperature for coarse ceramics. The experimental results are in good agreement with theoretical prediction.

[1]  Michiyoshi Tanaka,et al.  Size effect on the crystal phase of cobalt fine particles , 1997 .

[2]  Y. Rong,et al.  Nucleation barrier for phase transformations in nanosized crystals. , 2002 .

[3]  Joshua R. Smith,et al.  Temperature effects on the universal equation of state of solids. , 1987, Physical review. B, Condensed matter.

[4]  H. Fecht Thermodynamic properties and stability of grain boundaries in metals based on the universal equation of state at negative pressure , 1990 .

[5]  Zhu,et al.  X-ray diffraction studies of the structure of nanometer-sized crystalline materials. , 1987, Physical review. B, Condensed matter.

[6]  L. Schultz,et al.  Phase formation and martensitic transformation in mechanically alloyed nanocrystalline Fe—Ni , 1993 .

[7]  S. M. Lang Axial Thermal Expansion of TetragonaI ZrO, Between 1150° and 1700°C , 1964 .

[8]  Y. Mo,et al.  Negative phototropism of rice root and its influencing factors , 2002, Science in China Series C: Life Sciences.

[9]  Fecht Intrinsic instability and entropy stabilization of grain boundaries. , 1990, Physical review letters.

[10]  Wagner Structure and thermodynamic properties of nanocrystalline metals. , 1992, Physical review. B, Condensed matter.

[11]  R. Garvie THE OCCURRENCE OF METASTABLE TETRAGONAL ZIRCONIA AS A CRYSTALLITE SIZE EFFECT , 1965 .

[12]  Bikramjit Basu,et al.  Toughening of yttria-stabilised tetragonal zirconia ceramics , 2005 .

[13]  R. J. Hill,et al.  Structures of ZrO2 polymorphs at room temperature by high-resolution neutron powder diffraction , 1988 .

[14]  Zhou,et al.  Low-temperature stable nanometer-size fcc-Fe particles with no magnetic ordering. , 1992, Physical review. B, Condensed matter.

[15]  I. Chen,et al.  Martensitic nucleation in ZrO2 , 1983 .

[16]  K. Tsuzaki,et al.  Statistics of martensitic nucleation , 1985 .

[17]  M. Smirnov,et al.  Lattice-dynamical study of the cubic-tetragonal-monoclinic transformations of zirconia , 1997 .

[18]  J. S. Smith,et al.  PREPARATION OF ULTRA-HIGH-PURITY SUBMICRON REFRACTORY OXIDES , 1965 .

[19]  N. Zhou,et al.  Size effect on the Fe nanocrystalline phase transformation , 2002 .

[20]  Georg Kresse,et al.  First-principles calculations to describe zirconia pseudopolymorphs , 1999 .

[21]  O. Ruff,et al.  Beiträge zur Keramik hochfeuerfester Stoffe. l. Die Formen des Zirkondioxyds , 1929 .

[22]  H. Baker,et al.  Alloy phase diagrams , 1992 .

[23]  S. Seal,et al.  Mechanisms of room temperature metastable tetragonal phase stabilisation in zirconia , 2005 .

[24]  M. Grimsditch,et al.  The elastic properties of monoclinic ZrO2 , 1988 .