Substrate heating method for coating metal surfaces with high-silica zeolites: ZSM-5 coatings on stainless steel plates

Syntheses of ZSM-5 coatings on stainless steel plates were carried out via the substrate heating method. The reaction mixture was kept at temperatures below 100 °C, while the metal plates were heated to temperatures above 100 °C. It was demonstrated that continuous ZSM-5 coatings of different textures with different crystal morphologies and void fractions could be formed. ZSM-5 coatings were characterized by X-ray diffraction and scanning electron microscopy. The thickness of the ZSM-5 coatings could be varied depending on the synthesis conditions. Besides providing the opportunity of manipulating coating properties, the method is also beneficial in respect to the synthesis duration as compared to the conventional procedures.

[1]  J. Hedlund,et al.  Single gas permeance ratios in MFI membranes: Effects of material properties and experimental conditions , 2005 .

[2]  A. S. Chiang,et al.  Supported zeolite membrane by vapor‐phase regrowth , 2000 .

[3]  T. Ban,et al.  Crystallization and crystal morphology of silicalite-1 prepared from silica gel using different amines as a base , 2005 .

[4]  Jungkyu Choi,et al.  Uniformly a-oriented MFI zeolite films by secondary growth. , 2006, Angewandte Chemie.

[5]  J. C. Jansen,et al.  Preparation of Coatings of Molecular Sieve Crystals for Catalysis and Separation , 1994 .

[6]  M. Ürgen,et al.  Preparation of zeolite coatings by direct heating of the substrates , 1999 .

[7]  FRACTAL GROWTH OF ZEOLITE COATINGS PREPARED BY THE SUBSTRATE HEATING METHOD , 2003 .

[8]  S. Mintova,et al.  Nanosized zeolite films for vapor-sensing applications , 2001 .

[9]  G. G. Stokes.  "J." , 1890, The New Yale Book of Quotations.

[10]  J. C. Jansen,et al.  Zeolites grown on wire gauze: A new structured catalyst packing for dustproof, low pressure drop denox processes , 1995 .

[11]  Z. Lai,et al.  Preparation of b-Oriented MFI Films on Porous Stainless Steel Substrates , 2005 .

[12]  Andrew G. Glen,et al.  APPL , 2001 .

[13]  J. Santamaría,et al.  Synthesis and characterization of ZSM-5 coatings onto cordierite honeycomb supports , 2003 .

[14]  L. Kiwi-Minsker,et al.  Zeolite/sintered metal fibers composites as effective structured catalysts , 2005 .

[15]  O. Terasaki,et al.  Microstructural Optimization of a Zeolite Membrane for Organic Vapor Separation , 2003, Science.

[16]  S. Mintova,et al.  Thin molecular sieve films on noble metal substrates , 1997 .

[17]  Mark E. Davis,et al.  Preparation of Zeolite ZSM-5 Membranes by In-Situ Crystallization on Porous α-Al_2O_3 , 1995 .

[18]  M. Fuji,et al.  Effect of Mesoporous Silica Buffer Layer on the Orientation of MFI Zeolite Membranes , 2005 .

[19]  A. Erdem-Senatalar,et al.  Searching for clear solution compositions by using the substrate heating method , 2004 .

[20]  M. D. Croon,et al.  The preparation of highly ordered single layer ZSM-5 coating on prefabricated stainless steel microchannels , 2001 .

[21]  Melkon Tatlier,et al.  A novel approach to enhance heat and mass transfer in adsorption heat pumps using the zeolite–water pair , 1999 .