论文信息 - Fracture of austenitic steel subject to a wide range of stress triaxiality ratios and crack deformation modes

Fracture of austenitic steel subject to a wide range of stress triaxiality ratios and crack deformation modes

Abstract The stress triaxiality ratio (hydrostatic pressure divided by von Mises equivalent stress) strongly affects the fracture behaviour of materials. Various fracture criteria take this effect into consideration in their effort to predict failure. The dependency of the fracture locus on the stress triaxiality ratio has to be investigated in order to evaluate these criteria and improve the understanding of ductile fracture. This was done by comparing the experimental results of austenitic steel specimens with a strong variation in their stress triaxiality ratios. The specimens had cracks with varying depths and crack tip deformation modes; tension, in-plane shear, and out-of-plane shear. The crack growth in fracture mechanics specimens was compared with the failure of standard testing specimens for tension, upsetting and torsion. By associating the experimental results with finite element simulations it was possible to compare the critical plastic equivalent strain and stress triaxiality ratio values at fracture. In the investigated triaxiality regime an exponential dependency of the fracture locus on the stress triaxiality ratio was found.

[1] A Fracture Mechanics Investigation on Crack Growth in Massive Forming , 2004 .

[2] H. Stüwe,et al. Equivalent Strains in Severe Plastic Deformation , 2003 .

[3] Y. Ling,et al. Uniaxial True Stress-Strain after Necking , 2004 .

[4] Y. Mai,et al. The effect of shallow cracks on crack tip opening displacement , 1986 .

[5] D. Koss,et al. Damage accumulation and failure of HY-100 steel , 2001 .

[6] T. Wierzbicki,et al. On fracture locus in the equivalent strain and stress triaxiality space , 2004 .

[7] R. Pippan,et al. Influence of processing temperature on microstructural and mechanical properties of high-alloyed single-phase steels subjected to severe plastic deformation , 2005 .

[8] D. Chae,et al. Damage accumulation and failure of HSLA-100 steel , 2004 .

[9] R. Pippan,et al. On the homogeneity of deformation by high pressure torsion , 2004 .

[10] Moriya Oyane,et al. Criteria of Ductile Fracture Strain , 1972 .

[11] F. A. McClintock,et al. A Criterion for Ductile Fracture by the Growth of Holes , 1968 .

[12] R. Pippan,et al. Crack Growth in Massive Forming: A Fracture Mechanics Approach , 2004 .

[13] D. M. Tracey,et al. On the ductile enlargement of voids in triaxial stress fields , 1969 .

[14] A. H. Shabaik,et al. A New Workability Criterion for Ductile Metals , 1986 .

[15] C. C. Chen,et al. Ductile Fracture in Axisymmetric Extrusion and Drawing—Part 2: Workability in Extrusion and Drawing , 1979 .