A study in flip-chip UBM/bump reliability with effects of SnPb solder composition

Abstract This paper aims to investigate the electromigration phenomenon of under-bump-metallization (UBM) and solder bumps of a flip-chip package under high temperature operation life test (HTOL). UBM is a thin film Al/Ni(V)/Cu metal stack of 1.5 μm; while bump material consists of Sn/37Pb, Sn/90Pb, and Sn/95Pb solder. Current densities of 2500 and 5000 A/cm 2 and ambient temperatures of 150–160 °C are applied to study their impact on electromigration. It is observed that bump temperature has more significant influence than current density does to bump failures. Owing to its higher melting point characteristics and less content of Sn phase, Sn/95Pb solder bumps are observed to have 13-fold improvement in Mean-Time-To-Failure (MTTF) than that of eutectic Sn/37Pb. Individual bump resistance history is calculated to evaluate UBM/bump degradation. The measured resistance increase is from bumps with electrical current flowing upward into UBM/bump interface (cathode), while bumps having opposite current polarity cause only minor resistance change. The identified failure sites and modes from aforementioned high resistance bumps reveal structural damages at the region of UBM and UBM/bump interface in forms of solder cracking or delamination. Effects of current polarity and crowding are key factors to observed electromigration behavior of flip-chip packages.

[1]  C. T. Chiu,et al.  Electromigration failures of UBM/bump systems of flip-chip packages , 2002, 52nd Electronic Components and Technology Conference 2002. (Cat. No.02CH37345).

[2]  King-Ning Tu,et al.  Electromigration of flip chip solder bump on Cu/Ni(V)/Al thin film under bump metallization , 2002, 52nd Electronic Components and Technology Conference 2002. (Cat. No.02CH37345).

[3]  Chao-Kun Hu,et al.  Copper interconnections and reliability , 1998 .

[4]  P. Gargini,et al.  The International Technology Roadmap for Semiconductors (ITRS): "Past, present and future" , 2000, GaAs IC Symposium. IEEE Gallium Arsenide Integrated Circuits Symposium. 22nd Annual Technical Digest 2000. (Cat. No.00CH37084).

[5]  D. R. Frear,et al.  Electromigration of eutectic SnPb solder interconnects for flip chip technology , 2001 .

[6]  I. Blech.  Electromigration in thin aluminum films on titanium nitride , 1976 .

[7]  James R. Lloyd,et al.  Electromigration in Thin Film Conductors , 1997 .

[8]  D. R. Frear,et al.  Electromigration of eutectic SnPb and SnAg3.8Cu0.7 flip chip solder bumps and under-bump metallization , 2001 .

[9]  K. Paik,et al.  UbBM (under bump metallization) study for Pb-free electroplating bumping : interface reaction and electromigration , 2002, 52nd Electronic Components and Technology Conference 2002. (Cat. No.02CH37345).