Damage mechanisms at the cement-implant interface of polished cemented femoral stems.

The occurrence of damage on polished femoral stems has been widely reported in the literature, and bone cement has been implicated in a tribocorrosive failure process. However, the mechanisms of cement-mediated damage and the impact of cement formulation on this process are not well understood. In this study, 13 Zimmer CPT polished femoral stems, and the corresponding cement specimens were retrieved at revision surgery and analyzed using high-resolution imaging techniques. Surface damage attributed to tribocorrosion was observed on all stems. Corrosion product, in the form of black flaky surface debris, was observed on the surface of cement specimens; both energy-dispersive X-ray spectroscopy and inductively coupled plasma mass spectrometry(ICP-MS) confirmed the presence of cobalt and chromium, with the ICP-MS showing much higher levels of Cr compared to Co when compared to the original stem material. Agglomerates of ZrO2 radiopacifier were also identified on the cement surface and, in some cases, showed evidence of abrasive wear; the size of these particles correlated well with elliptical pitting evident on the surfaces of the corresponding stems. This evidence supports the hypothesis that agglomerates of hard radiopacifier particles within the cement may induce a wear-dominated tribocorrosive interaction at the stem-cement interface that damages the surface of polished CoCr femoral stems. © 2016 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 105B: 2027-2033, 2017.

[1]  D. Williams,et al.  The effects of proteins on metallic corrosion. , 1982, Journal of biomedical materials research.

[2]  H. Willert,et al.  Crevice corrosion of cemented titanium alloy stems in total hip replacements. , 1996, Clinical orthopaedics and related research.

[3]  D W Murray,et al.  Cement migration after THR. A comparison of charnley elite and exeter femoral stems using RSA. , 1999, The Journal of bone and joint surgery. British volume.

[4]  David W. Murray,et al.  Cement migration after THR , 1999 .

[5]  B. Espehaug,et al.  The type of cement and failure of total hip replacements. , 2002, The Journal of bone and joint surgery. British volume.

[6]  W. Taylor,et al.  THA loading arising from increased femoral anteversion and offset may lead to critical cement stresses , 2003, Journal of orthopaedic research : official publication of the Orthopaedic Research Society.

[7]  L A Blunt,et al.  In vivo surface wear mechanisms of femoral components of cemented total hip arthroplasties: the influence of wear mechanism on clinical outcome. , 2004, The Journal of arthroplasty.

[8]  S. Thomas,et al.  Corrosion of cemented titanium femoral stems. , 2004, The Journal of bone and joint surgery. British volume.

[9]  P. Pellicci,et al.  High failure rate of a modern, proximally roughened, cemented stem for total hip arthroplasty , 2006, International Orthopaedics.

[10]  C. Case,et al.  Effect of synovial fluid, phosphate-buffered saline solution, and water on the dissolution and corrosion properties of CoCrMo alloys as used in orthopedic implants. , 2005, Journal of biomedical materials research. Part A.

[11]  E. Salvati,et al.  Metallic Shedding, Surface Finish Changes, and Extensive Femoral Osteolysis in the Loose Spectron EF Stem , 2006, Clinical orthopaedics and related research.

[12]  L. Blunt,et al.  Generation of fretting wear debris at the stem-cement interface in total hip replacement , 2007 .

[13]  L. Blunt,et al.  Investigation of relative micromotion at the stem—cement interface in total hip replacement , 2009, Proceedings of the Institution of Mechanical Engineers. Part H, Journal of engineering in medicine.

[14]  Hongyu Zhang,et al.  Evaluation of fretting wear on the femoral stem surface , 2009 .

[15]  Hongyu Zhang,et al.  Understanding initiation and propagation of fretting wear on the femoral stem in total hip replacement , 2009 .

[16]  C. Case,et al.  Early Failure of the Ultima Metal-on-metal Total Hip Replacement in the Presence of Normal Plain Radiographs Their Production May Provoke a Hypersensitivity Reaction, Resulting in an Immune Response , 2022 .

[17]  N. Arden,et al.  High failure rates with a large-diameter hybrid metal-on-metal total hip replacement: clinical, radiological and retrieval analysis. , 2011, The Journal of bone and joint surgery. British volume.

[18]  Hongyu Zhang,et al.  The contribution of the micropores in bone cement surface to generation of femoral stem wear in total hip replacement , 2011 .

[19]  L. Havelin,et al.  Coordinating Retrieval and Register Studies Improves Postmarket Surveillance , 2012, Clinical Orthopaedics and Related Research.

[20]  Liam Blunt,et al.  The influence of bone cement type on production of fretting wear on the femoral stem surface: a preliminary study. , 2012, Clinical biomechanics.

[21]  B. Beake,et al.  Comparison of nano-f`retting and nano-scratch tests on biomedical materials , 2013 .

[22]  A. Neville,et al.  Crevice corrosion of biomedical alloys: a novel method of assessing the effects of bone cement and its chemistry. , 2013, Journal of biomedical materials research. Part B, Applied biomaterials.

[23]  A. Neville,et al.  Fretting corrosion characteristics of polished collarless tapered stems in a simulated biological environment , 2013 .

[24]  A. Neville,et al.  Failure analysis of cemented metal-on-metal total hip replacements from a single centre cohort , 2013 .

[25]  A. Neville,et al.  Fretting corrosion of fully cemented polished collarless tapered stems: The influence of PMMA bone cement , 2013 .

[26]  A. Neville,et al.  Characterisation of the surface topography, tomography and chemistry of fretting corrosion product found on retrieved polished femoral stems. , 2014, Journal of the mechanical behavior of biomedical materials.