Preparation of Aluminum Nitride Ceramics by Aqueous Tape Casting

High compacted aluminum nitride (AlN) substrates were prepared by aqueous tape casting. Aluminium dihydrogen phosphate was used to modify AlN particle surface from hydrolysis during casting process. The absolute value of zeta potential for the AlN particle treated by Al(H2PO4)2 was 60mv at pH = 9. The slurry suitable for tape casting was prepared which possessed shear-thinning behavior and appropriate viscosity. The results showed that the green tapes own excellent properties including high bulk density, uniform pore distribution and low porosity. The samples were fired at 1700°C (lower than melting point of Pt) with pressureless sintering process which can be used to fabricate complex device.

[1]  A. Rincón,et al.  Al2O3-3YTZP-Graphene multilayers produced by tape casting and spark plasma sintering , 2014 .

[2]  A. Rincón,et al.  Tape casting of alumina/zirconia suspensions containing graphene oxide , 2014 .

[3]  Wenbin Liu,et al.  Comparison of aqueous- and non-aqueous-based tape casting for preparing YAG transparent ceramics , 2013 .

[4]  Z. Fu,et al.  Transient liquid-phase sintering of AlN ceramics with CaF2 additive , 2013 .

[5]  S. Atre,et al.  The effects of nanoparticle addition on the sintering and properties of bimodal AlN , 2012 .

[6]  Feng Yongbao,et al.  Process dependant setting behavior of aqueous gelcast AlN slurries , 2012 .

[7]  U. S. Hareesh,et al.  Hydrolysis control of alumina and AlN mixture for aqueous colloidal processing of aluminum oxynitride , 2011 .

[8]  S. Atre,et al.  Review of Net Shape Fabrication of Thermally Conducting Ceramics , 2011 .

[9]  A. Kocjan,et al.  The course of the hydrolysis and the reaction kinetics of AlN powder in diluted aqueous suspensions , 2011 .

[10]  Yi-Cheng Lin,et al.  Effects of reduction atmosphere and nano carbon powder addition on the deoxidization of injection molded aluminum nitride parts , 2008 .

[11]  S. Ghosh,et al.  Tape Cast Multilayer Composite of Nano Zirconia with High Toughness , 2006 .

[12]  Jun Li,et al.  High Thermal Conductivity Aluminum Nitride Substrates Prepared by Aqueous Tape Casting , 2006 .

[13]  Juan-Yu Yang,et al.  Aqueous tape casting processing of low dielectric constant cordierite-based glass-ceramics—selection of binder , 2006 .

[14]  J. Ferreira,et al.  Rheological characterisation of water-based AlN slurries for the tape casting process , 2005 .

[15]  T. Chartier,et al.  Drying mechanisms and stress development in aqueous alumina tape casting , 2005 .

[16]  Rong Huang,et al.  High toughness in laminated SiC ceramics from aqueous tape casting , 2005 .

[17]  A. Roosen,et al.  Constrained sintering of dielectric and ferrite LTCC tape composites , 2005 .

[18]  Heping Zhou,et al.  Thermal conductivity of AlN ceramics sintered with CaF2 and YF3 , 2003 .

[19]  J. Heinrich,et al.  Aqueous tape casting of silicon nitride , 2002 .

[20]  T. Kosmač,et al.  Protection of AlN powder against hydrolysis using aluminum dihydrogen phosphate , 2001 .

[21]  Yuping Zeng,et al.  Fabrication and Properties of Tape-Cast Laminated and Functionally Gradient Alumina–Titanium Carbide Materials , 2000 .

[22]  F. Ueno,et al.  Thermal conductivity improvement of YAG added A1N ceramics in the grain boundary elimination process , 1995 .