Electrodeposition and Characterization of Thin-Film Platinum-Iridium Alloys for Biological Interfaces

An efficient platinum-iridium thin film alloy electrodeposition method has been evaluated to modify the surface of platinum or gold microelectrodes that are being developed for neural recording and stimulation applications. A large number of electrodeposition process variables have been investigated in terms of how they affected the properties of the electrodeposited films. Three sets of Pt-Ir films of a certain composition were electroplated on gold substrates using a potential cycling technique and characterized using microscopy, elemental analysis, nanoindentation, and electrochemical techniques to evaluate the repeatability of the electrodeposition process. Deposition rates were estimated by determining film mass and thickness as a function of deposition time. The surface morphology of the Pt-Ir films was characterized using scanning electron microscopy (SEM) and the chemical composition was determined using wavelength dispersive spectroscopy (WDS). Nanoindentation measurements showed that the hardness of the electroplated Pt-Ir thin films was nearly 100% higher than that of a Pt foil. The electrochemical properties of the films were evaluated using cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS) and compared with those of pure Pt, pure Ir and 80-20% Pt-Ir foils. The final electroplating process resulted in 60-40% Pt-Ir alloys. The film thickness increased with electrodeposition time at a rate of 16.5 nm/min and stable films with up to 500 nm thickness were obtained. Characterization by SEM and EIS revealed that the real surface area of the Pt-Ir films was much larger than that of pure Pt and increased significantly with increasing deposition time.

[1]  D. Pletcher,et al.  Studies of platinum electroplating baths: Part V: Solutions derived from Pt(NO2)42− in aqueous acid , 1998 .

[2]  M. Hefny,et al.  Electro-oxidation at a coated iridium electrode , 1996 .

[3]  Alireza Zolfaghari,et al.  Capacitance of the double-layer at polycrystalline Pt electrodes bearing a surface-oxide film , 2002 .

[4]  F. Solzbacher,et al.  In vitro comparison of sputtered iridium oxide and platinum-coated neural implantable microelectrode arrays , 2010, Biomedical materials.

[5]  V. Birss,et al.  Early stages of growth of hydrous platinum oxide films , 1991 .

[6]  Feng Wu,et al.  Electrodeposition of Pt-Ir alloys on nickel-base single crystal superalloy TMS-75 , 2004 .

[7]  James D. Weiland,et al.  Electrochemical Characterization of Charge Injection at Electrodeposited Platinum Electrodes in Phosphate Buffered Saline , 2006 .

[8]  D. Pletcher,et al.  Studies of platinum electroplating baths: Part II. Deposition of platinum from a solution of Pt(H2O)42+ in aqueous acid , 1993 .

[9]  U. Schnakenberg,et al.  Sputtered Iridium Oxide Films as Charge Injection Material for Functional Electrostimulation , 2004 .

[10]  Andreas Hierlemann,et al.  Impedance characterization and modeling of electrodes for biomedical applications , 2005, IEEE Transactions on Biomedical Engineering.

[11]  J. Langford,et al.  Scherrer after sixty years: a survey and some new results in the determination of crystallite size , 1978 .

[12]  Uwe Erb,et al.  Electrodeposited nanocrystals: Synthesis, properties and industrial applications , 1995 .

[13]  S. Glarum,et al.  The A‐C Response of Iridium Oxide Films , 1980 .

[14]  James D. Weiland,et al.  Electrochemical Deposition of Platinum from Aqueous Ammonium Hexachloroplatinate Solution , 2005 .

[15]  Sang In Lee,et al.  Preparation and Characterization of Iridium Oxide Thin Films Grown by DC Reactive Sputtering , 1997 .

[16]  G. Sheela,et al.  A bromide electrolyte for the electrodeposition of platinum and platinum–iridium alloy , 2005 .

[17]  David C. Martin,et al.  Polymerization of the conducting polymer poly(3,4-ethylenedioxythiophene) (PEDOT) around living neural cells. , 2007, Biomaterials.

[18]  C. Chien,et al.  Potential Modulated Multilayer Deposition of Multisegment Cu/Ni Nanowires with Tunable Magnetic Properties , 2006 .

[19]  P. Bartlett,et al.  PLATINUM MICROELECTRODES WITH UNIQUE HIGH SURFACE AREAS , 1999 .

[20]  Aicheng Chen,et al.  Electrocatalytic Activity of Nanoporous Pt – Ir Materials toward Methanol Oxidation and Oxygen Reduction , 2008 .

[21]  B. Piersma,et al.  Coupling Reactions at the Metal‐Tissue Interface in Electrical Stimulation with Cardiac Pacemaker Electrodes , 1987 .

[22]  Daniel R. Merrill,et al.  Electrical stimulation of excitable tissue: design of efficacious and safe protocols , 2005, Journal of Neuroscience Methods.

[23]  M. C. Diez,et al.  Electro-oxidation of chlorophenols at a gold electrode , 2001 .

[24]  S.F. Cogan,et al.  Electrodeposited iridium oxide for neural stimulation and recording electrodes , 2001, IEEE Transactions on Neural Systems and Rehabilitation Engineering.

[25]  X. Beebe,et al.  Charge injection limits of activated iridium oxide electrodes with 0.2 ms pulses in bicarbonate buffered saline (neurological stimulation application) , 1988, IEEE Transactions on Biomedical Engineering.