Prediction of weld strength and seam width for laser transmission welding of thermoplastic using response surface methodology

In the present work, a study is made to investigate the effects of process parameters, namely, laser power, welding speed, size of the laser beam and clamp pressure, on the lap-shear strength and weld-seam width for laser transmission welding of acrylic (polymethyl methacrylate), using a diode laser system. Response surface methodology (RSM) is employed to develop mathematical relationships between the welding process parameters and the output variables of the weld joint to determine the welding input parameters that lead to the desired weld quality. In addition, using response surface plots, the interaction effects of process parameters on the responses are analyzed and discussed. The statistical software Design-Expert v7 is used to establish the design matrix and to obtain the regression equations. The developed mathematical models are tested by analysis-of-variance (ANOVA) method to check their adequacy. Finally, a comparison is made between measured and calculated results, which are in good agreement. This indicates that the developed models can predict the responses adequately within the limits of welding parameters being used.

[1]  Dan Watt,et al.  Welding thermoplastic elastomers to polypropylene with a diode laser , 2002 .

[2]  Val A. Kagan,et al.  Forward to Better Understanding of Optical Characterization and Development of Colored Polyamides for the Infra-Red/Laser Welding: Part I - Efficiency of Polyamides for Infra-Red Welding , 2003 .

[3]  Antti Salminen,et al.  The effect of parameters on laser transmission welding of polymers , 2003 .

[4]  V. Kagan,et al.  Laser Transmission Welding of Semicrystalline Thermoplastics - Part II: Analysis of Mechanical Performance of Welded Nylon , 2004 .

[5]  D. Mark Douglass,et al.  Laser welding of polyolefin elastomers to thermoplastic polyolefin , 2003 .

[6]  V. Gunaraj,et al.  Application of response surface methodology for predicting weld bead quality in submerged arc welding of pipes , 1999 .

[7]  M. Abreu,et al.  High-speed laser welding of plastic films , 2000 .

[8]  V. Kagan,et al.  Laser Transmission Welding of Semi-Crystalline Thermoplastics—Part I: Optical Characterization of Nylon Based Plastics , 2002 .

[9]  Friedrich G. Bachmann,et al.  Laser welding of polymers using high-power diode lasers , 2002, SPIE LASE.

[10]  A. Erdman,et al.  Laser transmission welding of thermoplastics-Part I Temperature and pressure modeling , 2007 .

[11]  Val A. Kagan,et al.  Relationship between Optical Properties and Optimized Processing Parameters for through-Transmission Laser Welding of Thermoplastics , 2004 .

[12]  N. Murugan,et al.  Prediction and comparison of the area of the heat-affected zone for the bead-on-plate and bead-on-joint in submerged arc welding of pipes , 1999 .

[13]  Marianna Kontopoulou,et al.  Contour Laser – Laser-Transmission Welding of Glass Reinforced Nylon 6 , 2006 .

[14]  M. Hashmi,et al.  Effect of laser welding parameters on the heat input and weld-bead profile , 2005 .