Long-Wavelength Optical Phonons of AgBrxCl1-x Mixed Crystals

Infrared reflectivity and second-order Raman scattering in the mixed crystal system AgBrxCl1−x, were studied at 77 K. The TO(Γ) and LO(Γ) phonon frequencies obtained by means of a Kramers-Kronig analysis shift continuously between their energetic positions in the pure components indicating one-mode behaviour of the system. This result is discussed in view of a recent model that describes the optical modes of a mixed crystal. The LO(Γ) phonon frequencies taken from the Raman spectra are found to be slightly lower. A resonant enhancement of the 2L0 scattering process that occurs for z = 0.42 with shorter-wavelength excitation is used to determine the longitudinal optical phonon frequency. Infrarot-Reflexionsvermogen und Ramanstreuung zweiter Ordnung werden im Mischkristallsystem AgBrxCl1−x bei 77 K untersucht. Die Frequenzen des TO(Γ)- und LO(Γ)-Phonons, die durch Kramers-Kronig-Analyse gewonnen werden, verschieben sich kontinuierlich zwischen reinem AgBr und reinem AgCl und zeigen Ein-Modenverhalten. Dieses Ergebnis wird im Hinblick auf ein Modell zur Beschreibung der optischen Moden in Mischkristallen diskutiert. Die den Ramanspektren entnommenen LO(Γ)-Phononenfrequenzen liegen geringfugig niedriger. Die fur z = 0,42 beobachtete resonante Erhohung des 2LO-Streuprozesses bei kurzwelligerer Anregung des Ramanspektrums gestattet die Bestimmung der longitudinal-optischen Phononenfrequenz.