Structure of Calcium Silicate Hydrate (C‐S‐H): Near‐, Mid‐, and Far‐Infrared Spectroscopy

The mid-, near-, and far-infrared (IR) spectra of synthetic, single-phase calcium silicate hydrates (C-S-H) with Ca/Si ratios (C/S) of 0.41–1.85, 1.4 nm tobermorite, 1.1 nm tobermorite, and jennite confirm the similarity of the structure of these phases and provide important new insight into their H2O and OH environments. The main mid-IR bands occur at 950–1100, 810–830, 660–670, and 440–450 cm−1, consistent with single silicate chain structures. For the C-S-H samples, the mid-IR bands change systematically with increasing C/S ratio, consistent with decreasing silicate polymerization and with an increasing content of jennite-like structural environments of C/S ratios >1.2. The 950–1100 cm−1 group of bands due to Si-O stretching shifts first to lower wave number due to decreasing polymerization and then to higher wave numbers, possibly reflecting an increase in jennite-like structural environments. Because IR spectroscopy is a local structural probe, the spatial distribution of the jennite-like domains cannot be determined from these data. A shoulder at ∼1200 cm−1 due to Si-O stretching vibrations in Q3 sites occurs only at C/S lessthan equal to 0.7. The 660–670 cm−1 band due to Si-O-Si bending broadens and decreases in intensity for samples with C/S > 0.88, consistent with depolymerization and decreased structural order. In the near-IR region, the combination band at 4567 cm−1 due to Si-OH stretching plus O-H stretching decreases in intensity and is absent at C/S greater than ∼1.2, indicating the absence of Si-OH linkages at C/S ratios greater than this. The primary Si-OH band at 3740 cm-1 decreases in a similar way. In the far-IR region, C-S-H samples with C/S ratio greater than ∼1.3 have increased absorption intensity at ∼300 cm−1, indicating the presence of CaOH environments, even though portlandite cannot be detected by X-ray diffraction for C/S ratios <1.5. These results, in combination with our previous NMR and Raman spectroscopic studies of the same samples, provide the basis for a more complete structural model for this type of C-S-H, which is described.

[1]  M. L. Hair,et al.  Hydroxyl groups on silica surface , 1975 .

[2]  C. Dobson,et al.  The carbonation of OPC and OPC/silica fume hardened cement pastes in air under conditions of fixed humidity , 1993 .

[3]  H. Taylor.  Chemistry of Cements , 1938, Nature.

[4]  X. Cong,et al.  17O and 29Si MAS NMR study of β–C2S hydration and the structure of calcium-silicate hydrates , 1993 .

[5]  F. Gimblett,et al.  Factors influencing the porosity and surface characteristics of anomalous synthetic tobermorites: II. Thermal treatment , 1988 .

[6]  A reexamination of jennite , 1977 .

[7]  P. McMillan.  Chapter 4. WATER SOLUBILITY AND SPECIATION MODELS , 1994 .

[8]  Y. I. Ryskin.  The Vibrations of Protons in Minerals: hydroxyl, water and ammonium , 1974 .

[9]  H. Taylor.  726. Hydrated calcium silicates. Part I. Compound formation at ordinary temperatures , 1950 .

[10]  Kenji Fueki,et al.  Selective O–H Bond Cleavage in the Radiolysis of Quartz , 1986 .

[11]  H. Taylor,et al.  Calcium silicate hydrate (II) (“C-S-H(II)”) , 1976 .

[12]  T. Mitsuda,et al.  29Si NMR Spectroscopy of Silicate Anions in Hydrothermally Formed C‐S‐H , 1994 .

[13]  Paul F. McMillan,et al.  Hydroxyl sites in SiO2 glass: a note on infrared and Raman spectra , 1986 .

[14]  X. Cong,et al.  Ca X-ray absorption spectroscopy of C—S—H and some model compounds , 1997 .

[15]  X. Cong,et al.  Raman spectroscopy of C-S-H, tobermorite, and jennite , 1997 .

[16]  D. Macphee,et al.  Polymerization effects in C-S-H: implications for Portland cement hydration , 1988 .

[17]  H. Megaw,et al.  Crystal Structure of Tobermorite , 1956, Nature.

[18]  S. Ghosh,et al.  Infrared and Raman spectral studies in cement and concrete (review) , 1980 .

[19]  A. B. Carpenter,et al.  Jennite, a new mineral , 1966 .

[20]  H. Taylor.  Nanostructure of C?S?H: Current status , 1993 .

[21]  J. E. Bailey,et al.  The compositional and molecular character of the calcium silicate hydrates formed in the paste hydration of 3CaO·SiO2 , 1993 .

[22]  F. Shebl,et al.  Tobermorite as the final product of β-C2S hydration , 1985 .

[23]  X. Cong,et al.  17O MAS NMR Investigation of the Structure of Calcium Silicate Hydrate Gel , 1996 .

[24]  Zhengkui Xu,et al.  Mesostructure of calcium silicate hydrate (C-S-H) gels in Portland cement paste : Short-range ordering, nanocrystallinity, and local compositional order , 1997 .

[25]  James H. Adair,et al.  Morphological forms of tobermorite in hydrothermally treated calcium silicate hydrate gels , 1996 .

[26]  A new approach on the hydration mechanism of tricalcium silicate , 1985 .

[27]  H. Taylor.  Proposed Structure for Calcium Silicate Hydrate Gel , 1986 .

[28]  DUDLEY WILLIAMS,et al.  Frequency Assignments in Infra-red Spectrum of Water , 1966, Nature.

[29]  T. Uchino,et al.  Interpretation of Hydrated States of Sodium Silicate Glasses by Infrared and Raman Analysis , 1991 .

[30]  A. Benesi,et al.  Silicon‐29 Magic Angle Spinning Nuclear Magnetic Resonance Study of Calcium Silicate Hydrates , 1989 .

[31]  X. Cong,et al.  29Si and 17O NMR investigation of the structure of some crystalline calcium silicate hydrates , 1996 .

[32]  M. Handke,et al.  Vibrational Spectra, Force Constants, and Si-O Bond Character in Calcium Silicate Crystal Structure , 1986 .

[33]  H. Boyer,et al.  Some possibilities of Raman microprobe in cement chemistry , 1980 .

[34]  H. Taylor.  Tobermorite, jennite, and cement gel , 1992 .

[35]  R. Doremus,et al.  The infrared transmission spectra of four silicate glasses before and after exposure to water , 1990 .

[36]  J. Kubicki,et al.  A model for H2O solubility mechanisms in albite melts from infrared spectroscopy and molecular orbital calculations , 1993 .

[37]  V. Marinkovič,et al.  Hydrothermal metastability and structural disorder of 0.301 nm phase , 1986 .

[38]  K. Nakamoto,et al.  Stretching Frequencies as a Function of Distances in Hydrogen Bonds , 1955 .

[39]  S. A. Hamid.  The crystal structure of the 11Å natural tobermorite Ca2.25[Si3O7.5(OH)1.5] · 1H2O , 1981 .

[40]  Edward M. Stolper,et al.  Water in silicate glasses: An infrared spectroscopic study , 1982 .

[41]  C. Frondel.  Structural hydroxyl in chalcedony (type B quartz) , 1982 .

[42]  C. Dobson,et al.  Application of Selective 29Si Isotopic Enrichment to Studies of the Structure of Calcium Silicate Hydrate (C‐S‐H) Gels , 1994 .

[43]  P. L. Pratt,et al.  Morphological Development of Hydrating Tricalcium Silicate as Examined by Electron Microscopy Techniques , 1981 .

[44]  X. Cong,et al.  29Si MAS NMR study of the structure of calcium silicate hydrate , 1996 .