Modeling of scatter and size effect in ductile fracture: application to thermal embrittlement of duplex stainless steels

Abstract The aim of this work was to investigate the effect of specimen size and geometry on ductile fracture of cast duplex stainless steels after thermal embrittlement. Different specimen geometries, including smooth and notched bars, Charpy and compact tension (CT) specimens, were tested using three different materials. These specimens were used to investigate both crack initiation and propagation. In all cases, a significant scatter was observed. Size effects were also evidenced using homothetic samples having the same geometry. Microstructural investigations have also shown that damage is highly heterogeneous. In order to predict rupture, finite element models were used. The material was described using the Gurson model. In order to model size effects and scatter, it was necessary to account for the distribution of damage nucleation rates which were experimentally measured by quantitative metallography. Comparison of experiments with simulations showed that the model can be applied to describe both crack initiation and propagation. In particular it can predict mean value and scatter observed on strain to failure (tensile bars) and on initiation and propagation energies (Charpy and CT specimens).

[1]  Jean-Baptiste Leblond,et al.  Approximate models for ductile metals containing non-spherical voids—Case of axisymmetric prolate ellipsoidal cavities , 1993 .

[2]  Alberto Carpinteri,et al.  Crack-resistance behavior as a consequence of self-similar fracture topologies , 1996 .

[3]  D. M. Tracey,et al.  On the ductile enlargement of voids in triaxial stress fields , 1969 .

[4]  Jonas Faleskog,et al.  Micromechanics of coalescence—I. Synergistic effects of elasticity, plastic yielding and multi-size-scale voids , 1997 .

[5]  A. Needleman,et al.  Analysis of the cup-cone fracture in a round tensile bar , 1984 .

[6]  F. M. Beremin.  Cavity formation from inclusions in ductile fracture of A508 steel , 1981 .

[7]  C. Shih,et al.  Family of crack-tip fields characterized by a triaxiality parameter—II. Fracture applications , 1992 .

[8]  Jacques Besson,et al.  Object-Oriented Programming Applied to the Finite Element Method Part II. Application to Material Behaviors , 1998 .

[9]  Frank A. McClintock,et al.  PLASTICITY ASPECTS OF FRACTURE , 1971 .

[10]  R. Billardon,et al.  Investigation of localization due to damage in elasto-plastic materials , 1995 .

[11]  Y. Liu,et al.  Mesh-dependence and stress singularity in finite element analysis of creep crack growth by continuum damage mechanics , 1994 .

[12]  C. Shih,et al.  Family of crack-tip fields characterized by a triaxiality parameter—I. Structure of fields , 1991 .

[13]  S. Carassou,et al.  Effet d’échelle sur la rupture ductile d’un acier type A48. , 1994 .

[14]  Susumu Shima,et al.  Plasticity theory for porous metals , 1976 .

[15]  Z. Bažant,et al.  Nonlocal Continuum Damage, Localization Instability and Convergence , 1988 .

[16]  V. Tvergaard.  Material Failure by Void Growth to Coalescence , 1989 .

[17]  Jacques Besson,et al.  Size and geometry effects on ductile rupture of notched bars in a C-Mn steel: experiments and modelling , 1997 .

[18]  J. Hancock,et al.  Two-Parameter Characterization of Elastic-Plastic Crack-Tip Fields , 1991 .

[19]  J. Im,et al.  Cavity formation from inclusions in ductile fracture , 1975 .

[20]  Jacques Besson,et al.  Notch fracture toughness of a cast duplex stainless steel: modelling of experimental scatter and size effect , 1997 .

[21]  Viggo Tvergaard,et al.  VOID GROWTH AND FAILURE IN NOTCHED BARS , 1988 .

[22]  Jacques Besson,et al.  Polymorphic constitutive equations in finite element codes , 1997 .

[23]  P. Joly.  Etude de la rupture d'aciers inoxydables austéno-ferritiques moulés, fragilisés par vieillissement à 400°C , 1992 .

[24]  A. Gurson.  Continuum Theory of Ductile Rupture by Void Nucleation and Growth: Part I—Yield Criteria and Flow Rules for Porous Ductile Media , 1977 .

[25]  Jean-Baptiste Leblond,et al.  Approximate Models for Ductile Metals Containing Nonspherical Voids—Case of Axisymmetric Oblate Ellipsoidal Cavities , 1994 .

[26]  John W. Hutchinson,et al.  A computational approach to ductile crack growth under large scale yielding conditions , 1995 .

[27]  Lydia Devillers-Guerville.  Rupture d'aciers inoxydables austéno-ferritiques moules, fragilises par vieillissement à 350-400c : aspects microstructuraux - simulation numérique de la dispersion et des effets d’échelle , 1998 .

[28]  J. Brooks,et al.  Microstructural development and solidification cracking susceptibility of austenitic stainless steel welds , 1991 .

[29]  C. Bathias,et al.  On the creep crack growth prediction by a local approach , 1986 .

[30]  J. Knott,et al.  Fundamentals of Fracture Mechanics , 2008 .