Comparison of GaN and 6H-SiC p-i-n photodetectors with excellent ultraviolet sensitivity and selectivity

We fabricated GaN and 6H-SiC p-i-n photodetectors and compared their electrical and optical characteristics. The GaN diodes suffered from significant leakage current of 37 /spl mu/A/mm/sup 2/ at -5 V, while the SiC diode leakage current was below the noise level at 10 pA/mm/sup 2/ at -20 V. The built-in potentials and the unintentional "i-layer" doping densities were obtained from capacitance-voltage (C-V) measurements. The SiC detectors exhibited a broad spectral response in contrast to the abrupt cutoff observed in the GaN detectors. The peak responsivities of the GaN and SiC photodetectors corresponded to internal quantum efficiencies of 57% at 3.42 eV and 82% at 4.49 eV, respectively. Furthermore, both detectors exhibited excellent visible rejection ratios which is needed for solar-blind applications. The response times at zero bias were 18 and 102 ns for the GaN and SiC detectors, respectively.

[1]  Shuji Nakamura,et al.  The Blue Laser Diode: GaN based Light Emitters and Lasers , 1997 .

[2]  Henryk Temkin,et al.  Low noise p-π-n GaN ultraviolet photodetectors , 1997 .

[3]  Hua-Shuang Kong,et al.  6H-Silicon Carbide Light Emitting Diodes and UV Photodiodes , 1997 .

[4]  Manijeh Razeghi,et al.  Semiconductor ultraviolet detectors , 1996 .

[5]  W. J. Choyke,et al.  Higher Absorption Edges in 6H SiC , 1968 .

[6]  Shuji Nakamura,et al.  InGaN/GaN/AIGaN-Based Laser Diodes With an Estimated Lifetime of Longer Than 10,000 Hours , 1998 .

[7]  U. Mishra,et al.  Anisotropic epitaxial lateral growth in GaN selective area epitaxy , 1997 .

[8]  S. M. Sze,et al.  Physics of semiconductor devices , 1969 .

[9]  Richard Joseph Saia,et al.  Silicon carbide UV photodiodes , 1993 .

[10]  Peter P. Chow,et al.  Ultraviolet-sensitive, visible-blind GaN photodiodes fabricated by molecular beam epitaxy , 1997 .

[11]  Robert F. Davis,et al.  Lateral epitaxy of low defect density GaN layers via organometallic vapor phase epitaxy , 1997 .

[12]  W. Joyce,et al.  Analytic approximations for the Fermi energy of an ideal Fermi gas , 1977 .

[13]  Visible Blind uv GaN Photovoltaic Detector Arrays Grown by rf Atomic Nitrogen Plasma MBE , 1996 .

[14]  James S. Speck,et al.  Electrical characterization of GaN p-n junctions with and without threading dislocations , 1998 .

[15]  Hadis Morkoç,et al.  High speed, low noise ultraviolet photodetectors based on GaN p-i-n and AlGaN(p)-GaN(i)-GaN(n)structures , 1997 .