Efficiency improvement of multicrystalline silicon solar cells after surface and grain boundaries passivation using vanadium oxide

Abstract The aim of this work is to investigate the effect of vanadium oxide deposition onto the front surface of multicrystalline silicon (mc-Si) substrat, without any additional cost in the fabrication process and leading to an efficient surface and grain boundaries (GBs) passivation that have not been reported before. The lowest reflectance of mc-Si coated with vanadium oxide film of 9% was achieved by annealing the deposited film at 600 °C. Vanadium pentoxide (V 2 O 5 ) were thermally evaporated onto the surface of mc-Si substrates, followed by a short annealing duration at a temperature ranging between 600 °C and 800 °C, under O 2 atmosphere. The chemical composition of the films was analyzed by means of Fourier transform infrared spectroscopy (FTIR). Surface and cross-section morphology were determined by atomic force microscope (AFM) and a scanning electron microscope (SEM), respectively. The deposited vanadium oxide thin films make the possibility of combining in one processing step an antireflection coating deposition along with efficient surface state passivation, as compared to a reference wafer. Silicon solar cells based on untreated and treated mc-Si wafers were achieved. We showed that mc-silicon solar cells, subjected to the above treatment, have better short circuit currents and open-circuit voltages than those made from untreated wafers. Thus, the efficiency of obtained solar cells has been improved.

[1]  Laura M. Ilharco,et al.  The defect structure of sol–gel-derived silica/polytetrahydrofuran hybrid films by FTIR , 2001 .

[2]  Residual stress and structural characteristics in Ti and Cu sputtered films on glass substrates at different substrate temperatures and film thickness , 2004 .

[3]  M. Naeem,et al.  EFFECT OF TI DEPOSITION TEMPERATURE ON TISIX RESISTIVITY , 1995 .

[4]  Chemical vapour etching for double-sided buried metallic contacts in polycrystalline silicon solar cells processing , 2008 .

[5]  F. Netzer,et al.  Vanadium oxide surface studies , 2003 .

[6]  C. Julien,et al.  Growth and surface characterization of V2O5 thin films made by pulsed-laser deposition , 2004 .

[7]  G. Demets,et al.  Characterization and properties of mixed bentonite-vanadium(V) oxide xerogels , 2001 .

[8]  M. Bouaïcha,et al.  Effect of porous silicon on the performances of silicon solar cells during the porous silicon-based gettering procedure , 2009 .

[9]  W. K. Schubert,et al.  Effects of light and modulation frequency on spin-dependent trapping at silicon grain boundaries , 1984 .

[10]  H. Möller.  Semiconductors for Solar Cells , 1993 .

[11]  J. Livage,et al.  Infrared and Raman study of amorphous V2O5 , 1982 .

[12]  G. Harbeke,et al.  Assessment of the Surface Quality of SIMOX Wafers by UV Reflectance , 1990 .

[13]  C. Grovenor.  Grain boundaries in semiconductors , 1985 .

[14]  Wayne A. Anderson,et al.  A novel approach for evaluating the series resistance of solar cells , 1988 .

[15]  G. Franz,et al.  Long-wave optical vibrations of V2O5☆ , 1973 .

[16]  G. Poullain,et al.  Conductance of silicon grain boundaries in as‐grown and annealed bicrystals , 1987 .

[17]  A. Slaoui,et al.  Surface passivation at low temperature of p- and n-type silicon wafers using a double layer a-Si:H/SiNx:H , 2009 .

[18]  A. Maldonado,et al.  Physical properties of ZnO:F obtained from a fresh and aged solution of zinc acetate and zinc acetylacetonate , 2006 .

[19]  M. Green.  Silicon solar cells : advanced principles and practice , 1995 .

[20]  E. Baran,et al.  IR spectra of VO2 and V2O3 , 1997 .

[21]  M. Schubert,et al.  Low-temperature a-Si:H/ZnO/Al back contacts for high-efficiency silicon solar cells , 2006 .

[22]  Hatem Ezzaouia,et al.  Improvement of the minority carrier mobility in low-quality multicrystalline silicon using a porous silicon-based gettering under an O2 atmosphere , 2011 .

[23]  Tamas Mallat,et al.  Oxidation of butane and butadiene to furan over vanadia–silica mixed oxides , 1998 .