Laser surface texturing of stainless steel 316L cylindrical pins for interference fit applications

Abstract This study is focused on the development of a novel method for designing high-end interference fit fasteners. In this work, a new surface laser treatment process was utilized to enable enhanced usability and bond strength control of press-fit connections. Cylindrical 10 mm diameter pins of 316L were textured over a 10 mm length using a pulsed CO2 laser beam focused one millimeter below the surface, with the thermal energy adjusted to bring the surface to just above the melting point of the metal. The pin surface morphology and dimensions were precisely controlled by controlling the laser processing parameters specifically the laser beam power, the pulse repetition frequency, and the overlap between scan tracks. The pin was inserted into a hub hole diameter of 10.05 ± 0.003 mm and pull out joint bond strengths were examined. The results of this study showed that surface thus altered provided improved control of the bond strength which is a particular novelty of this new interference fit joining method. Surface roughness, Ra, from 40 to 160 μm, melt pool depths from 0.4 to 1.7 mm, increases in the pin outer diameter from 0.5 to 1.1 mm, and pull out forces of up to 7.51 kN were achieved. The bond joint was found to re-grip before final failure providing a more secure joint and increased safety. This joining method allows for the possibility of joining different materials. The pulse repetition frequency was measured to be the most significant processing parameter for control of the resulting mechanical properties and the bond strength with a clear inverse relationship.

[1]  Celalettin Karadogan,et al.  Analysis of Elastic-plastic Interference-fit Joints , 2014 .

[2]  Carsten Gachot,et al.  Alignment and wear debris effects between laser-patterned steel surfaces under dry sliding conditions , 2014 .

[3]  Simon Barter,et al.  Investigation using quantitative fractography of an unexpected failure in an F/A-18 centre fuselage bulkhead in the FINAL teardown program , 2009 .

[4]  P. Schaaf.  Laser nitriding of metals , 2002 .

[6]  E. Kannatey-Asibu.  Principles of Laser Materials Processing , 2009 .

[7]  Dermot Brabazon,et al.  Comparison of ANN and DoE for the prediction of laser-machined micro-channel dimensions , 2009 .

[8]  The Absorptance of Steels to Nd : YLF and Nd : YAG Laser Light at Room Temperature , 2012 .

[10]  Yucan Fu,et al.  Cold expansion technology of connection holes in aircraft structures: A review and prospect , 2015 .

[11]  D Brabazon,et al.  3D printed metal columns for capillary liquid chromatography. , 2014, The Analyst.

[12]  Robert O. Parmley.  Standard handbook of fastening and joining , 1977 .

[13]  T. DebRoy,et al.  Absorption of CO2 laser beam by AISI 4340 steel , 1985 .

[14]  D. M. Mattox,et al.  Handbook of physical vapor deposition (PVD) processing , 2010 .

[15]  Eric Mazur,et al.  Laser-induced breakdown and damage in bulk transparent materials induced by tightly focused femtosecond laser pulses , 2001 .

[16]  Jonathan Lawrence,et al.  Laser surface engineering: Processes and applications , 2014 .

[17]  Jean-François Fontaine,et al.  Contact pressure between two rough surfaces of a cylindrical fit , 2002 .

[18]  A. Abdollah-zadeh,et al.  Microstructure and mechanical behavior of pulsed laser surface melted AISI D2 cold work tool steel , 2013 .

[19]  K. Ikeuchi,et al.  Nanoindentation Hardness Test for Estimation of Vickers Hardness , 2006 .

[20]  Dermot Brabazon,et al.  Methodology of laser processing for precise control of surface micro-topology , 2016 .

[21]  Jean-François Fontaine,et al.  Influence of roughness on characteristics of tight interference fit of a shaft and a hub , 2001 .

[22]  Lin Li,et al.  An investigation of the effect of pulse frequency in laser multiple-layer cladding of stainless steel , 2003 .