Bioremediation of CCA-treated wood by brown-rot fungi Fomitopsis palustris, Coniophora puteana, and Laetiporus sulphureus

This study evaluated oxalic acid accumulation and bioremediation of chromated copper arsenate (CCA)-treated wood by three brown-rot fungi Fomitopsis palustris, Coniophora puteana, and Laetiporus sulphureus. The fungi were first cultivated in a fermentation broth to accumulate oxalic acid. Bioremediation of CCA-treated wood was then carried out by leaching of heavy metals with oxalic acid over a 10-day fermentation period. Higher amounts of oxalic acid were produced by F. palustris and L. sulphureus compared with C. puteana. After 10-day fermentation, oxalic acid accumulation reached 4.2 g/l and 3.2 g/l for these fungi, respectively. Fomitopsis palustris and L. sulphureus exposed to CCA-treated sawdust for 10 days showed a decrease in arsenic of 100% and 85%, respectively; however, C. puteana remediation removed only 18% arsenic from CCA-treated sawdust. Likewise, chromium removal in F. palustris and L. sulphureus remediation processes was higher than those for C. puteana. This was attributed to low oxalic acid accumulation. These results suggest that F. palustris and L. sulphureus remediation processes can remove inorganic metal compounds via oxalic acid production by increasing the acidity of the substrate and increasing the solubility of the metals.

[1]  C. Clausen,et al.  Removal of CCA from treated wood by oxalic acid extraction, steam explosion, and bacterial fermentation , 1998, Journal of Industrial Microbiology and Biotechnology.

[2]  G. Daniel,et al.  Low molecular weight chelators and phenolic compounds isolated from wood decay fungi and their role in the fungal biodegradation of wood , 1997 .

[3]  C. Clausen.  CCA removal from treated wood using a dual remediation process , 2000 .

[4]  S. Kartal,et al.  Particleboard made from remediated CCA-treated wood : evaluation of panel properties , 2001 .

[5]  Carol A. Clausen,et al.  Leachability and decay resistance of particleboard made from acid extracted and bioremediated CCA-treated wood , 2001 .

[6]  M. Petrič,et al.  Changes of EPR Spectra of Wood Impregnated with Copper-Based Preservatives during Exposure to Several Wood-Rotting Fungi , 2002 .

[7]  F. Green,et al.  Mechanism of Brown-Rot decay : Paradigm or paradox , 1997 .

[8]  V. Arantes,et al.  Production of metal chelating compounds by white and brown-rot fungi and their comparative abilities for pulp bleaching , 2002 .

[9]  S. Kartal,et al.  Removal of copper, chromium, and arsenic from CCA-C treated wood by EDTA extraction. , 2003, Waste management.

[10]  H. Yamaguchi,et al.  Influence of Tannin-Copper Complexes as Preservatives for Wood on Mechanism of Decomposition by Brown-Rot Fungus Fomitopsis palustris , 2001 .

[11]  T. Lundell,et al.  Production of organic acids and oxalate decarboxylase in lignin-degrading white rot fungi , 2002 .

[12]  F. Green,et al.  Production of Polygalacturonase and Increase of Longitudinal Gas Permeability in Southern Pine by Brown-Rot and White-Rot Fungi , 1999 .

[13]  S. N. Kartal,et al.  Bioremediation of CCA-C treated wood by Aspergillus niger fermentation , 2004, Holz als Roh- und Werkstoff.

[14]  H. Leithoff,et al.  Microbial conversion of wood treated with salt preservatives , 1996 .

[15]  S. Kartal,et al.  Remediation of CCA-C treated wood using chelating agents , 2003, Holz als Roh- und Werkstoff.