Lamp‐pumped laser performance of Nd3+:Sr5(PO4)3F operating both separately and simultaneously at 1.059 and 1.328 μm

Lamp‐pumped laser performance of Nd3+‐doped strontium fluorapatite, Sr5(PO4)3F or S‐FAP, has been characterized and compared with that of Nd3+‐doped yttrium aluminum garnet (YAG) at both 1.06 and 1.3 μm. Nd3+:S‐FAP was found to exhibit lower thresholds and lower slope efficiencies than Nd3+:YAG. The former is attributed to the higher emission cross section, and the latter to lower Nd3+ concentration in S‐FAP. The 1.3 μm lasing of Nd3+:S‐FAP is of particular interest because of its high emission cross section (2.4×10−19 cm2). Q‐switched and dual‐wavelength lasing operation were also demonstrated in Nd3+:S‐FAP.

[1]  Lloyd L. Chase,et al.  Evaluation of absorption and emission properties of Yb/sup 3+/ doped crystals for laser applications , 1993 .

[2]  R. Warren,et al.  Selective Site Laser Excitation and ESR Studies of Nd3+ Ions in Ca5 ( PO 4 ) 3 F , 1978 .

[3]  N. Melamed,et al.  Laser properties of nd(+3) and ho(+3) doped crystals with the apatite structure. , 1972, Applied optics.

[4]  Bruce H. T. Chai,et al.  Growth of high-quality single crystals of FAP (Ca5(PO4)3F) and its isomorphs , 1993, Photonics West - Lasers and Applications in Science and Engineering.

[5]  J. Bergquist,et al.  An efficient CW Nd:FAP laser , 1991 .

[6]  Walter Koechner,et al.  Solid-State Laser Engineering , 1976 .

[7]  R. Mazelsky,et al.  Spectroscopic and Laser Characteristics of Neodymium-doped Calcium Fluorophosphate. , 1968, Applied optics.

[8]  William F. Krupke,et al.  Laser, optical, and thermomechanical properties of Yb-doped fluorapatite , 1994 .

[9]  H. Shen,et al.  Simultaneous multiple wavelength laser action in various neodymium host crystals , 1991 .

[10]  D. Findlay,et al.  The measurement of internal losses in 4-level lasers , 1966 .

[11]  Bruce H. T. Chai,et al.  Growth of laser‐quality single crystals of Nd3+‐doped calcium fluorapatite and their efficient lasing performance , 1994 .

[12]  Bruce H. T. Chai,et al.  Efficient laser performance of Nd3+:Sr5(PO 4)3F at 1.059 and 1.328 μm , 1994 .

[13]  William F. Krupke,et al.  Laser and spectroscopic properties of Sr 5 (PO 4 ) 3 F:Yb , 1994 .

[14]  R. Hopkins,et al.  Czochralski-growth of calcium fluorophosphate , 1968 .

[15]  M. Walker,et al.  Thermal Properties of Synthetic Fluorapatite Crystals , 1971 .