Microstructural failure criteria for S235JR steel subjected to spatial stress states

Abstract The study deals with failure criteria for S235JR steel subjected to spatial stress states. The predictions were made using the modified Gurson–Tvergaard–Needleman (GTN) material model, which takes into account the effect of microstructural damage. The relationship between the material strength parameters and the microstructural changes caused by plastic deformation was established by analyzing the void volume fraction. The microstructural failure criteria determined for S235JR steel refer to the moment of decrease in strength and rupture.

[1]  P. G. Kossakowski,et al.  Effect of Initial Porosity on Material Response Under Multi-Axial Stress State for S235JR Steel , 2012 .

[2]  Xiaosheng Gao,et al.  Cell model for nonlinear fracture analysis – I. Micromechanics calibration , 1998 .

[3]  Paweł Grzegorz Kossakowski,et al.  SIMULATION OF DUCTILE FRACTURE OF S235JR STEEL USING COMPUTATIONAL CELLS WITH MICROSTRUCTURALLY-BASED LENGTH SCALES , 2012 .

[5]  P. Kossakowski.  Influence of Initial Porosity on Strength Properties of S235JR Steel at Low Stress Triaxiality , 2012 .

[6]  J. Hutchinson,et al.  Modification of the Gurson Model for shear failure , 2008 .

[7]  C. Shih,et al.  Ductile crack growth-I. A numerical study using computational cells with microstructurally-based length scales , 1995 .

[8]  A. Gurson.  Continuum Theory of Ductile Rupture by Void Nucleation and Growth: Part I—Yield Criteria and Flow Rules for Porous Ductile Media , 1977 .

[9]  A. Needleman,et al.  Analysis of the cup-cone fracture in a round tensile bar , 1984 .

[10]  Percy Williams Bridgman,et al.  Studies in large plastic flow and fracture , 1964 .

[11]  C. Shih,et al.  Ductile crack growth—II. Void nucleation and geometry effects on macroscopic fracture behavior , 1995 .

[12]  W. Trąmpczyński,et al.  Microvoids Evolution in S235JR Steel Subjected to Multi-Axial Stress State , 2012 .

[13]  Xiaosheng Gao,et al.  Cell model for nonlinear fracture analysis – II. Fracture- process calibration and verification , 1998 .

[14]  Paweł Grzegorz Kossakowski,et al.  An analysis of the load-carrying capacity of elements subjected to complex stress states with a focus on the microstructural failure , 2010 .

[15]  V. Tvergaard.  Influence of voids on shear band instabilities under plane strain conditions , 1981 .

[16]  P. Kossakowski.  Prediction of Ductile Fracture for S235JR Steel Using the Stress Modified Critical Strain and Gurson-Tvergaard-Needleman Models , 2012 .