Facile and fast fabrication of iron-phosphate supported on nickel foam as a highly efficient and stable oxygen evolution catalyst

Electrocatalytic water splitting is one of the most promising routes for large-scale hydrogen production. However, it is hindered by the complex oxygen evolution reaction (OER) with sluggish kinetics. NiFe-based catalysts, which are known for their high activity, durability, and low-cost, have been a “hot topic” in research on OER catalysts. Increasing numbers of reports have indicated that Fe sites provide active centers. Meanwhile, Fe is considered as the cheapest and one of the most abundant transition-metal elements. Herein, we report a facile and fast method to prepare iron–phosphate films supported on a nickel foam scaffold (Fe–Pi/NF), with exposed Fe sites at the surface. Fe–Pi/NF exhibited outstanding activity for the OER, requiring low overpotentials of 215 and 257 mV to drive current densities of 10 and 100 mA cm−2, respectively, in 1 M KOH solution. The TOF was as high as 0.381 s−1 at an overpotential of 270 mV. The Tafel slope was as low as 28 mV dec−1 between current densities of around 30 to 125 mA cm−2. It also exhibited excellent durability during a 90 h stability test, and the calculated faradaic efficiency was close to 96%. For comparison, Fe(OH)3/NF electrodes were also prepared. The results showed the OER activity of Fe–Pi/NF to be superior to those of Fe(OH)3/NF. The incorporation of electronegative phosphate groups results in the great hydrophilicity of Fe–Pi/NF and effectively adjusts the electronic structure of Fe3+ and facilitates the oxidation of Fe3+ to Fe4+.

[1]  John A. Turner,et al.  Sustainable Hydrogen Production , 2004, Science.

[2]  J. Kitchin,et al.  Spectroscopic Characterization of Mixed Fe–Ni Oxide Electrocatalysts for the Oxygen Evolution Reaction in Alkaline Electrolytes , 2012 .

[3]  Marc T. M. Koper,et al.  Guidelines for the Rational Design of Ni-Based Double Hydroxide Electrocatalysts for the Oxygen Evolution Reaction , 2015 .

[4]  Jianyin Wang,et al.  Hierarchically Structured 3D Integrated Electrodes by Galvanic Replacement Reaction for Highly Efficient Water Splitting , 2017 .

[5]  G. K. Pradhan,et al.  Hydrated manganese(II) phosphate (Mn₃(PO₄)₂·3H₂O) as a water oxidation catalyst. , 2014, Journal of the American Chemical Society.

[6]  S. Gul,et al.  High-Performance Overall Water Splitting Electrocatalysts Derived from Cobalt-Based Metal–Organic Frameworks , 2015 .

[7]  S. Boettcher,et al.  Revised Oxygen Evolution Reaction Activity Trends for First-Row Transition-Metal (Oxy)hydroxides in Alkaline Media. , 2015, The journal of physical chemistry letters.

[8]  Wei Xing,et al.  NiSe Nanowire Film Supported on Nickel Foam: An Efficient and Stable 3D Bifunctional Electrode for Full Water Splitting. , 2015, Angewandte Chemie.

[9]  C. Berlinguette,et al.  Water oxidation catalysis: electrocatalytic response to metal stoichiometry in amorphous metal oxide films containing iron, cobalt, and nickel. , 2013, Journal of the American Chemical Society.

[10]  D. Corrigan.  The Catalysis of the Oxygen Evolution Reaction by Iron Impurities in Thin Film Nickel Oxide Electrodes , 1987 .

[11]  L. Zhen,et al.  Ternary Metal Phosphide with Triple‐Layered Structure as a Low‐Cost and Efficient Electrocatalyst for Bifunctional Water Splitting , 2016 .

[12]  Hua Zhang,et al.  Synthesis of two-dimensional transition-metal phosphates with highly ordered mesoporous structures for lithium-ion battery applications. , 2014, Angewandte Chemie.

[13]  W. Saenger,et al.  Where Water Is Oxidized to Dioxygen: Structure of the Photosynthetic Mn4Ca Cluster , 2006, Science.

[14]  Abdullah M. Asiri,et al.  An amorphous CoSe film behaves as an active and stable full water-splitting electrocatalyst under strongly alkaline conditions. , 2015, Chemical communications.

[15]  Qiang Zhao,et al.  Facile fabrication of robust 3D Fe–NiSe nanowires supported on nickel foam as a highly efficient, durable oxygen evolution catalyst , 2017 .

[16]  Daniel G Nocera,et al.  The artificial leaf. , 2012, Accounts of chemical research.

[17]  D. Schmeißer,et al.  Unification of catalytic water oxidation and oxygen reduction reactions: amorphous beat crystalline cobalt iron oxides. , 2014, Journal of the American Chemical Society.

[18]  Charles C. L. McCrory,et al.  Benchmarking heterogeneous electrocatalysts for the oxygen evolution reaction. , 2013, Journal of the American Chemical Society.

[19]  Yi Luo,et al.  Nickel–vanadium monolayer double hydroxide for efficient electrochemical water oxidation , 2016, Nature Communications.

[20]  Chaohe Xu,et al.  Activity of Transition‐Metal (Manganese, Iron, Cobalt, and Nickel) Phosphates for Oxygen Electrocatalysis in Alkaline Solution , 2016 .

[21]  S. Kundu,et al.  Recent Trends and Perspectives in Electrochemical Water Splitting with an Emphasis on Sulfide, Selenide, and Phosphide Catalysts of Fe, Co, and Ni: A Review , 2016 .

[22]  Bryan T. Yonemoto,et al.  In situ formation of cobalt oxide nanocubanes as efficient oxygen evolution catalysts. , 2015, Journal of the American Chemical Society.

[23]  Alexis T. Bell,et al.  An investigation of thin-film Ni-Fe oxide catalysts for the electrochemical evolution of oxygen. , 2013, Journal of the American Chemical Society.

[24]  Fang Song,et al.  Ni2P as a Janus catalyst for water splitting: the oxygen evolution activity of Ni2P nanoparticles , 2015 .

[25]  G. Galli,et al.  Characterization of NiFe oxyhydroxide electrocatalysts by integrated electronic structure calculations and spectroelectrochemistry , 2017, Proceedings of the National Academy of Sciences.

[26]  M. Grätzel.  Photoelectrochemical cells : Materials for clean energy , 2001 .

[27]  Zhaolin Liu,et al.  A Flexible Electrode Based on Iron Phosphide Nanotubes for Overall Water Splitting. , 2015, Chemistry.

[28]  F. Walsh,et al.  Nickel based electrocatalysts for oxygen evolution in high current density, alkaline water electrolysers. , 2011, Physical chemistry chemical physics : PCCP.

[29]  M. Antonietti,et al.  The Synthesis of Nanostructured Ni5P4 Films and their Use as a Non‐Noble Bifunctional Electrocatalyst for Full Water Splitting , 2015 .

[30]  Xunyu Lu,et al.  Electrodeposition of hierarchically structured three-dimensional nickel–iron electrodes for efficient oxygen evolution at high current densities , 2015, Nature Communications.

[31]  Tom Regier,et al.  An advanced Ni-Fe layered double hydroxide electrocatalyst for water oxidation. , 2013, Journal of the American Chemical Society.

[32]  Lei Wang,et al.  Fast and simple preparation of iron-based thin films as highly efficient water-oxidation catalysts in neutral aqueous solution. , 2015, Angewandte Chemie.

[33]  H. D. de Groot,et al.  Ni‐Based Electrocatalyst for Water Oxidation Developed In‐Situ in a HCO3−/CO2 System at Near‐Neutral pH , 2014 .

[34]  Jan Kern,et al.  Towards complete cofactor arrangement in the 3.0 Å resolution structure of photosystem II , 2005, Nature.

[35]  Yi Feng,et al.  Carbon coated porous nickel phosphides nanoplates for highly efficient oxygen evolution reaction , 2016 .

[36]  Ki Tae Nam,et al.  Coordination tuning of cobalt phosphates towards efficient water oxidation catalyst , 2015, Nature Communications.

[37]  Abdullah M. Asiri,et al.  NiCo2S4 nanowires array as an efficient bifunctional electrocatalyst for full water splitting with superior activity. , 2015, Nanoscale.

[38]  James Barber,et al.  Architecture of the Photosynthetic Oxygen-Evolving Center , 2004, Science.

[39]  Jens K Nørskov,et al.  Identification of highly active Fe sites in (Ni,Fe)OOH for electrocatalytic water splitting. , 2015, Journal of the American Chemical Society.

[40]  Shannon W. Boettcher,et al.  Oxygen Evolution Reaction Electrocatalysis on Transition Metal Oxides and (Oxy)hydroxides: Activity Trends and Design Principles , 2015 .

[41]  A. Vojvodić,et al.  Homogeneously dispersed multimetal oxygen-evolving catalysts , 2016, Science.

[42]  J. Barber.  Photosynthetic energy conversion: natural and artificial. , 2009, Chemical Society reviews.

[43]  Wang Li,et al.  Ultrafast Formation of Amorphous Bimetallic Hydroxide Films on 3D Conductive Sulfide Nanoarrays for Large‐Current‐Density Oxygen Evolution Electrocatalysis , 2017, Advanced materials.

[44]  Vicky Fidelsky,et al.  The secret behind the success of doping nickel oxyhydroxide with iron. , 2017, Physical chemistry chemical physics : PCCP.

[45]  Bin Zhao,et al.  Assembling pore-rich FeP nanorods on the CNT backbone as an advanced electrocatalyst for oxygen evolution , 2016 .

[46]  Zhipan Zhang,et al.  Photochemical Route for Accessing Amorphous Metal Oxide Materials for Water Oxidation Catalysis , 2013, Science.

[47]  S. Boettcher,et al.  Solution-cast metal oxide thin film electrocatalysts for oxygen evolution. , 2012, Journal of the American Chemical Society.

[48]  Keisuke Kawakami,et al.  Crystal structure of oxygen-evolving photosystem II at a resolution of 1.9 Å , 2011, Nature.

[49]  Daniel G. Nocera,et al.  In Situ Formation of an Oxygen-Evolving Catalyst in Neutral Water Containing Phosphate and Co2+ , 2008, Science.

[50]  Qiu Jiang,et al.  Selenide‐Based Electrocatalysts and Scaffolds for Water Oxidation Applications , 2016, Advances in Materials.

[51]  Yao Zheng,et al.  Design of electrocatalysts for oxygen- and hydrogen-involving energy conversion reactions. , 2015, Chemical Society reviews.

[52]  Yibing Li,et al.  Iron-Doped Nickel Phosphate as Synergistic Electrocatalyst for Water Oxidation , 2016 .

[53]  Z. Wen,et al.  Oxygen-Containing Amorphous Cobalt Sulfide Porous Nanocubes as High-Activity Electrocatalysts for the Oxygen Evolution Reaction in an Alkaline/Neutral Medium. , 2017, Angewandte Chemie.