Corrosion resistance and mechanical properties of low-alloy steels under atmospheric conditions

Abstract The corrosion resistance and mechanical strength of four newly developed low-alloy steels (LAS) were compared with a carbon steel (SS400) and a weathering steel (Acr-Ten A) using a laboratory-accelerated test that involved cyclic wet/dry conditions in a chloride environment (5 wt.% NaCl). The new LAS were designated 1605A, 1605B, 1604A, and 1604B. After 72 cycles of cyclic corrosion tests, the susceptibility of the steels to corrosion could be listed in the following order based on their weight loss (from high to low): SS400 > Acr-Ten A > 1604B ⩾ 1604A > 1605B ⩾ 1605A. The change in mechanical properties by corrosion was the least for SS400, Acr-Ten A was second, and effects of corrosion on the mechanical properties of the other four low-alloy steels were similar. Finally, the characteristics of the rust layers on each LAS sample were observed by SEM, and analyzed by FTIR and EPMA. The results indicated that most of the rust layers on the test steels were composed of a loose outer rust layer and a dense inner rust layer. The outer rust layer of each steel was composed of α-FeOOH, γ-FeOOH, magnetite (Fe3O4), H2O, and amorphous ferric oxyhydroxide (FeOx(OH)3−2x, x=0–1), while the inner rust layer was composed mainly of Fe3O4 with a little α-FeOOH. In addition, it was apparent that the copper and chromium alloying additions were enriched, respectively, at the rust-layer/substrate interface and in the rust layers. Finally, combining the results of the accelerated tests and the rust layer analysis showed that low-alloy steels, such as 1605A and 1605B, have better weathering steel properties than Acr-Ten A for use in the humid and salty weather.

[1]  G. C. Wood.  Conference introductory paper why Manchester , 1993 .

[2]  M. Komp,et al.  Effect of Copper Content of Carbon Steel On Corrosion in Sulfuric Acid , 1965 .

[3]  R. A. Legault,et al.  Kinetics of the Atmospheric Corrosion of Low-Alloy Steels in an Industrial Environment , 1975 .

[4]  H. Schwitter,et al.  Influence of Accelerated Weathering on the Corrosion of Low‐Alloy Steels , 1980 .

[5]  Masato Yamashita,et al.  The long term growth of the protective rust layer formed on weathering steel by atmospheric corrosion during a quarter of a century , 1994 .

[6]  K. Asami,et al.  In-depth distribution of rusts on a plain carbon steel and weathering steels exposed to coastal-industrial atmosphere for 17 years , 2003 .

[7]  S. Tuleja,et al.  Effect of atmospheric corrosion on the mechanical properties of the weathering steel ATMOFIX 52A , 1993 .

[8]  Chris W. Brown,et al.  Characterization of the passive film formed on weathering steels , 1983 .

[9]  H. Uhlig,et al.  Corrosion and corrosion control , 1971 .

[10]  M. Pourbaix,et al.  Recent Progress in Atmospheric Corrosion Testing , 1989 .

[11]  H. Shih,et al.  Modeling of Atmospheric Corrosion Behavior of Weathering Steel in Sulfur Dioxide-Polluted Atmospheres , 1996 .

[12]  Yuzo Hosoi,et al.  Electrochemical Reduction of Thick Rust Layers Formed on Steel Surfaces , 1970 .

[13]  J. Marco,et al.  Corrosion of weathering steel and iron under wet-dry cycling conditions: Influence of the rise of temperature during the dry period , 1992 .

[14]  Joh.‐E. Hiller,et al.  Phasenumwandlungen im Rost , 1966 .

[15]  T. Misawa,et al.  The mechanism of formation of iron oxide and oxyhydroxides in aqueous solutions at room temperature , 1974 .

[16]  J. J. Wang,et al.  Corrosion behavior of weathering steel in marine atmosphere , 2003 .

[17]  Martin Stratmann,et al.  The Influence of Copper upon the Atmospheric Corrosion of Iron , 1987 .

[18]  T. Misawa,et al.  The mechanism of atmospheric rusting and the effect of Cu and P on the rust formation of low alloy steels , 1971 .

[19]  Koji Hashimoto,et al.  The Mechanism of Atmospheric Rusting and the Protective Amorphous Rust on Low Alloy Steel(Chemistry) , 1974 .

[20]  Sebastián Feliu,et al.  The prediction of atmospheric corrosion from meteorological and pollution parameters—I. Annual corrosion , 1993 .

[21]  U. R. Evans.  Mechanism of rusting , 1969 .

[22]  P. Keller.  Quantitative, röntgenographische Phasenanalyse verschiedener Rosttypen , 1967 .

[23]  Blanca R. de Meybaum,et al.  Characterization of Atmospheric Corrosion Products on Weathering Steels , 1980 .

[24]  J. Oung,et al.  Applications of electrochemical hysteresis for constructing the experimental potential-pH diagram for steels in seawater , 1994 .