Effect of the Number of Welding Repairs with GTAW on the Mechanical Behavior of AA7020 Aluminum Alloy Welded Joints

In this work, two different tests were done to establish the effect of heating cycles by welding in an AA7020-T6 aluminum alloy welded with ER5087 and ER5356 electrodes. During 10 months, welds were done to simulate in the laboratory several welding repairs (up to six repairs). Tensile and hardness measurements were done to evaluate the evolution of the properties against time. It was found that a single pass is enough to generate a heat-affected zone (HAZ) of 30 mm, and after four repairs the width of the HAZ exceeds 210 mm. In the HAZ, two regions were observed: the dissolution zone, which recovers a percentage of hardness by natural aging, and the over-aging zone, showing no increase in hardness. The results indicate that there is a maximum number of welding repairs that can be performed in a heat-treatable aluminum superstructure before it fails on the HAZ of the base material, since the tensile strength is reduced around 40 pct compared to the base metal.

[1]  T. Burleigh.  THE POSTULATED MECHANISMS FOR STRESS CORROSION CRACKING OF ALUMINUM ALLOYS: A REVIEW OF THE LITERATURE 1980-1989 , 1991 .

[2]  X. Z. Li,et al.  GP-zones in Al–Zn–Mg alloys and their role in artificial aging , 2001 .

[3]  Wojciech Szymański,et al.  Structural parameters of 7020 alloy after heat treatment simulating the welding process , 2001 .

[4]  A. Deschamps,et al.  Relationship Between Microstructure, Strength, and Fracture in an Al-Zn-Mg Electron Beam Weld: Part I: Microstructure Characterization , 2014, Metallurgical and Materials Transactions A.

[5]  K. Sreekumar,et al.  Cracking of Al–Zn–Mg Aluminum Alloy Nozzle Weld of Propellant Storage Tank: A Metallurgical Investigation , 2009 .

[6]  Hongwei Liu,et al.  In situ studies of microstructure evolution and properties of an Al–7.5Zn–1.7Mg–1.4Cu–0.12Zr alloy during retrogression and reaging , 2014 .

[7]  Y. E. Wu,et al.  Effect of Filler Metal and Postwelding Heat Treatment on Mechanical Properties of Al-Zn-Mg Alloy Weldments , 2010 .

[8]  V. Amigó,et al.  Microstructural change of the HAZ in an MIG welded bond on an AA7020 aluminium alloy: stress corrosion crack growth rate in dissimilar metal welds , 2004 .

[9]  G. Mathers.  The welding of aluminium and its alloys , 2002 .

[10]  Constantinos Soutis,et al.  Recent developments in advanced aircraft aluminium alloys , 2014 .

[11]  C. Schick,et al.  Development of continuous cooling precipitation diagrams for aluminium alloys AA7150 and AA7020 , 2014 .

[12]  Robert Baboian,et al.  Corrosion tests and standards : application and interpretation , 1995 .

[13]  Terence P. Ma,et al.  Softening behaviour of Al–Zn–Mg alloys due to welding , 1999 .

[14]  Ian J. Polmear,et al.  Light Alloys: Metallurgy of the Light Metals , 1982 .

[15]  D. Lloyd,et al.  Characterization of the evolution of the volume fraction of precipitates in aged AlMgSiCu alloys using DSC technique , 2005 .

[16]  S. Kou.  Solidification and liquation cracking issues in welding , 2003 .

[17]  G. G. Stokes.  "J." , 1890, The New Yale Book of Quotations.

[18]  Natural aging in friction stir welded 7136-T76 aluminum alloy , 2014 .

[19]  M. D. Rooij.  Corrosion of Aluminum and Aluminum Alloys , 2011 .